Optical fiber outer sheath material and preparation method thereof

A technology of optical fiber sheath and outer sheath, which is applied in the field of optical fiber outer sheath material and its preparation, can solve the problems of unfavorable optical fiber signal transmission, increased cost and single weight, inconvenient procurement and construction, etc., and achieves good chemical stability, Low friction coefficient, high cost effect

Active Publication Date: 2016-12-07
NANJING WASIN FUJIKURA OPTICAL COMM LTD
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This increases the cost and unit weight, and brings inconvenience to procurement and construction
Traditional polybutylene terephthalate bundle tubes are not flame retardant and dangerous
And there will be warping during the processing, which is not conducive to the signal transmission of the optical fiber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Optical fiber outer sheath material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Composition of raw materials: 40 parts of polytrimethylene terephthalate, 5 parts of modified lignin, 25 parts of polybutylene terephthalate, 2 parts of anti-ultraviolet material (phenyl salicylate), compatibilizer (methanol methyl acrylate-glycidyl methacrylate-ethyl acrylate terpolymer) 2 parts, antioxidant 1010 (tetra[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid] Pentaerythritol ester) 1 part, coupling agent (maleic anhydride) 3 parts, nanoscale composite hydroxide-inorganic filler powder 2 parts, dispersant (sodium alginate) 0.1 part.

[0025] Modified lignin preparation method:

[0026] Take the lignin whose particle size is 80-200 mesh for subsequent use;

[0027] Take a coupling agent (γ-methacryloxypropyl-trimethoxysilane) with a mass ratio of 20:8:72, ammonia water and ethanol to prepare a mixed solution, stir and mix for 1 hour after the proportioning is completed, and set aside;

[0028] Soaking: add lignin into the mixed solution with a substance ra...

Embodiment 2

[0041] Composition of raw materials: 55 parts of polypropylene terephthalate, 10 parts of modified lignin, 35 parts of polybutylene terephthalate, 3 parts of anti-ultraviolet material (phenyl salicylate), compatibilizer (methanol methyl acrylate-glycidyl methacrylate-ethyl acrylate terpolymer) 3 parts, antioxidant 1010 (tetra[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid] Pentaerythritol ester) 2 parts, coupling agent (maleic anhydride grafted polypropylene) 5 parts, nanoscale composite hydroxide-inorganic filler powder 2 parts, dispersant (sodium hydroxymethyl cellulose) 0.2 parts.

[0042] The preparation method is the same as in Example 1.

Embodiment 3

[0044] The raw material weight composition of the optical fiber outer sheath material of the present invention: 50 parts of polytrimethylene terephthalate, 12 parts of modified lignin, 27 parts of polybutylene terephthalate, 2 parts of phenyl salicylate, cyclic Oxygen resin 2 parts of styrene-acrylonitrile-maleic anhydride terpolymer, 1 part of tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester, maleic anhydride 0.88 parts of grafted ethylene-propylene ternary rubber, 2 parts of maleic anhydride, 3 parts of nanoscale composite hydroxide-inorganic filler powder, and 0.12 parts of sodium hydroxymethyl cellulose.

[0045] The preparation method is as follows:

[0046] 1. Preparation of nanoscale composite hydroxide-inorganic filler powder:

[0047] After getting 0.25 kilogram of aluminum hydroxide and 0.125 kilogram of wollastonite into the ball mill jar, put 2 steel balls of 200 grams, 10 steel balls of 100 grams, 40 steel balls of 36 grams and 100...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention discloses an optical fiber outer sheath material and a preparation method thereof. The optical fiber outer sheath material is prepared from the following raw materials in parts by weight: 40-55 parts of polytrimethylene terephthalate, 5-10 parts of modified lignin, 25-35 parts of polybutylene terephthalate, 2-3 parts of ultraviolet-resistant material, 2-3 parts of compatilizer, 1-2 parts of antioxidant, 3-5 parts of coupling agent, 2-3 parts of nano composite hydroxide-inorganic filler powder and 0.1-0.2 part of dispersing agent. The optical fiber outer sheath material has the advantages of higher impact resistance, high tensile strength, high elastic modulus and favorable flame retardancy.

Description

technical field [0001] The invention relates to an optical fiber outer sheath material and a preparation method thereof. Background technique [0002] With the rapid development of informatization, the process of networking is accelerating, and the development of informatization has made single-mode optical fibers with good transmission performance widely used. As the number of optical fibers in the optical cable continues to increase with the increase in the amount of information, in order to keep the signal propagating in the optical fiber unaffected and save space, a parallel optical fiber was invented. After the fiber optic cable is twisted, it must have an outer sheath so that it can maintain stable signal transmission under external influences such as impact stretching and twisting. The impact resistance of the commonly used polybutylene terephthalate outer sheath is generally not high and the elastic modulus is low, and if you encounter technical specifications that ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L97/00C08K13/06C08K9/00C08K3/22C08K3/34C08K5/134B29C47/92B29C48/92
CPCB29C48/92B29C2948/92704C08K2201/011C08L67/02C08L2201/02C08L2201/08C08L2203/20C08L2205/025C08L2205/035C08L97/00C08K13/06C08K9/00C08K2003/2227C08K3/34C08K5/1345
Inventor 昂亚峰
Owner NANJING WASIN FUJIKURA OPTICAL COMM LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap