A technology of copper-tungsten alloy and cuprous oxide is applied in the field of recycling and preparing cuprous oxide, which can solve problems such as increasing production cost, and achieve the effects of easy operation, mild reaction conditions, high yield and purity

Inactive Publication Date: 2016-12-07
LIYANG LIFANG PRECIOUS METALS MATERIAL CO LTD
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the raw materials used to prepare cuprous oxide are basically analytically pure copper acetate or copper nitrate. Chinese patents CN103395821A, CN103373739A, et

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of recovering and preparing cuprous oxide by taking waste copper-tungsten alloy as raw material
  • Method of recovering and preparing cuprous oxide by taking waste copper-tungsten alloy as raw material

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Example 1

[0021] (1) Take 10g of waste copper-tungsten alloy and use nitric acid with a concentration of 4mol / L to leach copper in the waste copper-tungsten alloy at a time. The nitric acid leaching temperature is 40℃, the leaching time is 6h, and the amount of nitric acid is twice the theoretical amount. Copper nitrate stock solution, the one-time leaching rate is 26.1%;

[0022] (2) Crush the waste copper-tungsten alloy remaining in step (1) into micron-sized powder with a particle size of 50um;

[0023] (3) Take 2g of the waste copper tungsten powder prepared in step (2), the nitric acid concentration is 6mol / L, the nitric acid leaching temperature is 40°C, the nitric acid leaching time is 30min, and the liquid-solid ratio is 1:1 to obtain a copper nitrate solution. The secondary leaching rate reaches 99.8%;

[0024] (4) The process of reducing sodium sulfite to prepare cuprous oxide, the concentration of sodium sulfite is 1mol / L, the concentration of copper nitrate is 0....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method of recovering and preparing cuprous oxide by taking waste copper-tungsten alloy as a raw material. The method comprises the following steps: copper in the waste copper-tungsten alloy is subjected to primary leaching by nitric acid; the waste copper-tungsten alloy after the primary leaching is pulverized, and waste copper-tungsten alloy powder is obtained; copper in the waste copper-tungsten alloy powder is subjected to secondary leaching by nitric acid; and cupric nitrate is reduced by sodium sulfite, and cuprous oxide is prepared. The method takes the waste copper-tungsten alloy as the raw material, and after leaching with nitric acid is carried out, cuprous oxide is prepared by a sodium sulfite reduction method, so that secondary utilization of the waste copper-tungsten alloy is realized, and the method is good for the environment. The method is simple and is low in cost, and prepared cuprous oxide is high in purity and good in crystal form.

Description

technical field [0001] The invention belongs to the technical field of preparation and application of inorganic functional materials, and in particular relates to a method for recycling and preparing cuprous oxide by using waste copper-tungsten alloy as raw material. Background technique [0002] Nano-cuprous oxide, as a new type of P-type oxide semiconductor material that can be excited by visible light, has an active electron-hole pair system and exhibits good catalytic activity. In addition, it also has strong adsorption properties, low-temperature paramagnetism, etc. characteristic. It has application potential in organic synthesis, photoelectric conversion, new energy, water photolysis, dye bleaching, sterilization, superconductivity and other fields. At present, the main synthesis methods include liquid-phase synthesis, low-temperature solid-phase method, vapor-phase deposition method, nano-copper oxidation method, electrolysis method, gamma-ray interference method, m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22B7/00C22B15/00
CPCC22B7/007C22B15/0073C22B15/0089Y02P10/20
Inventor 尚通明王自伟魏成文王豪郑成沈尧胤邹超刘维桥周全法
Owner LIYANG LIFANG PRECIOUS METALS MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap