Method for preparing graphene-quantum-dot-doped organic-solvent-resistant ultrafiltration membrane, ultrafiltration membrane prepared by method and application of ultrafiltration membrane

A technology of graphene quantum dots and resistance to organic solvents, applied in the field of membrane separation, can solve the problems of insufficient stability of ultrafiltration membranes, and achieve the effects of outstanding substantive features, high water flux and rejection rate, and high resistance to organic solvents

Active Publication Date: 2016-12-14
OCEAN UNIV OF CHINA
View PDF5 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to solve the problem of insufficient stability of the ultrafiltration membrane existing in the prior art in an organic solvent system, to provide a preparation method of an organic solvent-resistant ultrafiltration membrane doped with graphene quantum dots, prepared Ultrafiltration membrane and the application of the ultrafiltration membrane

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing graphene-quantum-dot-doped organic-solvent-resistant ultrafiltration membrane, ultrafiltration membrane prepared by method and application of ultrafiltration membrane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Preparation of graphene quantum dots:

[0048] Step I: Heat anhydrous citric acid to 150-300°C, drop the obtained molten citric acid into sodium hydroxide solution after 20-40 minutes, and then adjust the pH to 7 with hydrochloric acid solution;

[0049] Step II: The solution obtained in step I is separated by an ultrafiltration membrane with a molecular weight cut-off of 50,000 Daltons, and the resulting filtrate is collected; then the obtained filtrate is separated by a nanofiltration membrane with a molecular weight cut-off of 300 Daltons, and continuously added to the nanofiltration retentate Deionized water, the conductivity of the nanofiltration filtrate is less than 20 μs / cm, and the concentrated nanofiltration retentate is the graphene quantum dot solution. It has been determined that the graphene quantum dot nanoparticles contain functional groups such as carboxyl groups and phenolic hydroxyl groups. The particle diameter of the graphene quantum dot nanoparticl...

Embodiment 2

[0053] The preparation of graphene quantum dots is the same as in Example 1. Mix polyimide and DMF evenly, add graphene quantum dots to the casting solution to prepare a casting solution with a mass fraction of 20%, in which the mass fraction of graphene quantum dots is 1%; Stir for 6 hours, then centrifuge at 2000r / min for 20 minutes to defoam at a high speed; pour the prepared casting solution on the polyester non-woven fabric, control the height of the scraper to scrape at room temperature to form a film, and form a coating with a thickness of 120 μm; Evaporate the scraped coating in the air for 20 seconds, and then immerse it in deionized water at 30°C for 20 minutes. At this time, the high molecular polymer in the casting solution undergoes gel phase inversion and precipitates on the surface of the non-woven fabric to form a film. It is cross-linked 2h in the ethylenediamine / isopropanol cross-linking agent solution agent of 2.4% that above-mentioned phase conversion becom...

Embodiment 3

[0056] The preparation of graphene quantum dots is the same as in Example 1. Polyimide, polyethylene glycol 400, graphene quantum dots and DMF were uniformly mixed to prepare a casting solution with a mass concentration of PI of 20%, wherein the mass fraction of graphene quantum dots was 1%, and the concentration of polyethylene glycol 400 The mass fraction is 4%; mechanically stir the casting solution at 55°C for 6h, then let it stand at a constant temperature of 55°C for 24h, and then degas it by high-speed centrifugation at 1500r / min for 30min; pour the defoamed casting solution on On the polyester non-woven fabric, control the height of the scraper to scrape the film at room temperature to form a coating with a thickness of 120 μm; evaporate the scraped coating in the air for 10 seconds, immerse it in deionized water for 20 minutes, then take it out and rinse it clean After immersion in isopropanol for 24h, take it out for use; put the above-mentioned film soaked in isopro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
molecular weightaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing a graphene-quantum-dot-doped organic-solvent-resistant ultrafiltration membrane, the ultrafiltration membrane prepared by method and application of the ultrafiltration membrane. According to the method, graphene quantum dot nanoparticles are added in the preparation process of a polymer polyimide ultrafiltration membrane, and the graphene-quantum-dot-doped polyimide ultrafiltration membrane is modified by crosslinking with ethylenediamine to prepare the graphene-quantum-dot-doped organic-solvent-resistant polyimide ultrafiltration membrane. The graphene quantum dots are used in the preparation process of the ultrafiltration membrane for forming an organic / inorganic hybrid membrane, the quantum effect of the graphene quantum dots is fully used, flux of the prepared ultrafiltration membrane is increased significantly, the mechanical properties of the membrane are significantly improved, organic solvent resistance of the membrane is greatly enhanced, and the retention rate basically keeps stable; and the preparation method is simple in process, and low in cost, and has good application prospects in industrial organic solvent system separation.

Description

technical field [0001] The invention belongs to the technical field of membrane separation, and in particular relates to a preparation method of an organic solvent-resistant ultrafiltration membrane doped with graphene quantum dots, the prepared ultrafiltration membrane and the application of the ultrafiltration membrane. Background technique [0002] In recent years, organic solvents have been widely used in petrochemical, printing, coking, leather, pesticides, medicine and other fields. They have the characteristics of large output, many types, wide distribution, and many industries involved. These organic solvents have environmental risks and pollution hazards in production, transportation, storage, and use. Traditional organic solvent separation and recovery methods such as extraction and distillation have disadvantages such as high energy consumption and large solvent loss, and serious secondary pollution exists in the process of recovery and regeneration of these organ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01D71/64B01D69/02B01D67/00B01D61/14
CPCB01D61/145B01D67/0006B01D69/02B01D71/64B01D2325/30
Inventor 苏保卫黄良伟吕利宋晓娟高学理
Owner OCEAN UNIV OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap