Heat-resistant unsaturated polyester resin

A polyester resin, unsaturated technology, applied in the field of heat-resistant unsaturated polyester resin, can solve the problem of poor thermal stability, antibacterial and anti-mildew effect, unsatisfactory performance of unsaturated polyester resin, easy peeling off of stone bonding, etc. problems, to achieve good antibacterial and antifungal effects, improve infiltration and dispersion performance, and remarkable anti-aging performance

Inactive Publication Date: 2017-01-04
安徽鑫力新材科技股份有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The unsaturated polyester resin prepared by this traditional method is relatively unsatisfactory in terms of bonding and wetting. Meet the application requirements of some products and stone processing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of heat-resistant unsaturated polyester resin proposed by the present invention, its raw material comprises by weight: 30 parts of phthalic anhydride, 15 parts of maleic anhydride, 20 parts of isophthalic acid, 10 parts of fumaric acid, 8 parts of lauric acid, benzoic acid 6 parts, 12 parts of tung oil anhydride, 80 parts of diethylene glycol, 10 parts of propylene glycol, 15 parts of styrene, 20 parts of α-methylstyrene, 4 parts of stabilizer, 0.1 part of hydroquinone, 15 parts of epoxy resin, 1 part of nano silicon dioxide, 4 parts of modified sodium acrylate.

Embodiment 2

[0018] A kind of heat-resistant unsaturated polyester resin proposed by the present invention, its raw material comprises by weight: 40 parts of phthalic anhydride, 5 parts of maleic anhydride, 40 parts of isophthalic acid, 2 parts of fumaric acid, 16 parts of lauric acid, benzoic acid 1 part, 25 parts of tung oil anhydride, 50 parts of diethylene glycol, 30 parts of propylene glycol, 5 parts of styrene, 40 parts of α-methylstyrene, 1 part of stabilizer, 0.8 parts of hydroquinone, 5 parts of epoxy resin, 5 parts of nano silicon dioxide, 1 part of modified sodium acrylate.

[0019] The modified sodium acrylate is prepared by the following process: Microcrystalline paraffin, natural beeswax, polyethylene wax, and lauryl hydroxystearic acid are sealed and heated until melted, air is introduced, potassium permanganate is added, mixed and stirred, and the composite wax is obtained at room temperature ; Mix cornstarch and water evenly, add sodium acrylate and acrylamide, mix evenly,...

Embodiment 3

[0021] A kind of heat-resistant unsaturated polyester resin proposed by the present invention, its raw material comprises by weight: 32 parts of phthalic anhydride, 12 parts of maleic anhydride, 25 parts of isophthalic acid, 8 parts of fumaric acid, 10 parts of lauric acid, benzoic acid 5 parts, 16 parts of tung oil anhydride, 70 parts of diethylene glycol, 15 parts of propylene glycol, 12 parts of styrene, 25 parts of α-methylstyrene, 3 parts of stabilizer, 0.3 parts of hydroquinone, 12 parts of epoxy resin, 2 parts of nano silicon dioxide, 3 parts of modified sodium acrylate.

[0022] Modified sodium acrylate is prepared by the following process: by weight, 5 parts of microcrystalline paraffin, 6 parts of natural beeswax, 3 parts of polyethylene wax, and 0.8 parts of lauryl hydroxystearic acid are sealed and heated until they melt, air is introduced, and 0.15 parts of Mix and stir potassium permanganate for 100 minutes, lower to room temperature to obtain composite wax; mix ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses heat-resistant unsaturated polyester resin. The heat-resistant unsaturated polyester resin comprises the following raw materials in parts by weight: 30-40 parts of phthalic anhydride, 5-15 parts of maleic anhydride, 20-40 parts of m-phthalic acid, 2-10 parts of fumaric acid, 8-16 parts of lauric acid, 1-6 parts of benzoic acid, 12-25 parts of tung oil anhydride, 50-80 parts of diglycol, 10-30 parts of propylene glycol, 5-15 parts of styrene, 20-40 parts of alpha-methyl styrene, 1-4 parts of a stabilizer, 0.1-0.8 part of hydroquinone, 5-15 parts of epoxy resin, 1-5 parts of nano-silicon dioxide and 1-4 parts of modified sodium acrylate. The heat-resistant unsaturated polyester resin has good heat resistance and antibacterial and anti-mold effects, high mechanical strength and remarkable aging resistance.

Description

technical field [0001] The invention relates to the technical field of unsaturated polyester resins, in particular to a heat-resistant unsaturated polyester resin. Background technique [0002] Unsaturated polyester resin is a kind of thermosetting material, which is the most commonly used thermosetting resin in the field of anchoring agent. Ordinary unsaturated polyester resin generally only adopts dibasic acid and dibasic alcohol polycondensation reaction, and adds styrene to dilute at the same time to form A linear polymer compound with ester bonds and unsaturated double bonds. The unsaturated polyester resin prepared by this traditional method is relatively unsatisfactory in terms of bonding and wetting. Meet the application requirements of some products and stone processing. Contents of the invention [0003] Based on the technical problems existing in the background technology, the present invention proposes a heat-resistant unsaturated polyester resin, which has g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/08C08L63/00C08L91/06C08L51/02C08K3/36C08F283/01C08F212/12C08F212/08C08F251/00C08F220/06C08F220/56C08G63/676
CPCC08L51/08C08F251/00C08F283/01C08G63/676C08K2201/011C08L2201/08C08L2205/025C08L2205/035C08L63/00C08L91/06C08L51/02C08K3/36C08F212/12C08F220/06C08F220/56
Inventor 李志业
Owner 安徽鑫力新材科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com