Quick-forming organic antiseptic protective film for metal surface

A metal surface and protective film technology, applied in the direction of anti-corrosion coatings, anti-fouling/underwater coatings, paints containing biocide, etc., can solve the problems of poor binding force, easy corrosion and aging, and poor durability of anti-rust coatings, and achieve Large amount of silver loading, high loading fastness, good antibacterial effect

Active Publication Date: 2017-01-04
杭州朱炳仁铜艺股份有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But existing metal antirust paint also has some defects, such as antirust paint has poor binding force on the metal surface and is easy to fall off; and it is easy to corrode and age, and has poor durability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A quick-form organic anti-corrosion protective film on a metal surface, which is formed by curing an organic anti-corrosion protective coating. The organic anti-corrosion protective coating includes the following components by mass: 45 parts of acrylic acid emulsion, 10 parts of phytic acid ester, hydrated magnesium silicate 10 parts of aluminum filler, 5 parts of iron oxide red, 5 parts of antibacterial particles, 3 parts of composite tackifier, 5 parts of pigment, 4 parts of dispersant, 4 parts of defoamer, 5 parts of ethanol, and 15 parts of water.

[0019] Wherein, the solid content of the acrylic emulsion is 50%. The particle diameters of the hydrated magnesium aluminum silicate filler, iron oxide red and antibacterial particles are all between 0.1-1 micron.

[0020] Wherein, the preparation method of the antibacterial particles is: dissolving γ-cyclodextrin in water to obtain a γ-cyclodextrin solution with a concentration of 4wt%, and adding a mass of γ-cyclodextr...

Embodiment 2

[0023] A quick-formed organic anti-corrosion protective film on a metal surface, which is formed by curing an organic anti-corrosion protective coating. The organic anti-corrosion protective coating includes the following components by mass: 40 parts of acrylic acid emulsion, 5 parts of phytic acid ester, hydrated magnesium silicate 15 parts of aluminum filler, 3 parts of iron oxide red, 7 parts of antibacterial particles, 2 parts of composite tackifier, 7 parts of pigment, 1.5 parts of dispersant, 1.5 parts of defoamer, 7 parts of ethanol, and 11 parts of water.

[0024] Wherein, the solid content of the acrylic emulsion is 55%. The particle diameters of the hydrated magnesium aluminum silicate filler, iron oxide red and antibacterial particles are all between 0.1-1 micron.

[0025] Wherein, the preparation method of the antibacterial particles is: dissolving gamma-cyclodextrin in water to prepare a gamma-cyclodextrin solution with a concentration of 2wt%, adding a mass of ga...

Embodiment 3

[0028]A quick-form organic anti-corrosion protective film on a metal surface, which is formed by curing an organic anti-corrosion protective coating. The organic anti-corrosion protective coating includes the following components by mass: 50 parts of acrylic acid emulsion, 5 parts of phytic acid ester, hydrated magnesium silicate 5 parts of aluminum filler, 6 parts of red iron oxide, 3 parts of antibacterial particles, 4 parts of composite tackifier, 3 parts of pigment, 0.5 part of dispersant, 0.5 part of defoamer, 3 parts of ethanol, and 20 parts of water.

[0029] Wherein, the solid content of the acrylic emulsion is 45-55%. The particle diameters of the hydrated magnesium aluminum silicate filler, iron oxide red and antibacterial particles are all between 0.1-1 micron.

[0030] Wherein, the preparation method of the antibacterial particles is: dissolving γ-cyclodextrin in water to obtain a γ-cyclodextrin solution with a concentration of 6 wt%, and adding a mass of γ-cyclode...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of organic coatings and discloses a quick-forming organic antiseptic protective film for the metal surface. The organic antiseptic protective film is formed by curing an organic antiseptic protective coating, the organic antiseptic protective coating is prepared from components in parts by mass as follows: 40-50 parts of an acrylic emulsion, 5-15 parts of inositol hexaphosphate, 5-15 parts of hydrated magnesium-aluminum silicate filler, 3-7 parts of iron oxide red, 3-7 parts of antibacterial particles, 2-4 parts of a compound tackifier, 3-7 parts of pigment, 0.5-1.5 parts of a dispersing agent, 0.5-1.5 parts of a defoaming agent, 3-7 parts of ethanol and 10-20 parts of water. The quick-forming organic antiseptic protective film has high binding force with the metal surface, no bubbles are generated after the film is formed, and the organic antiseptic protective film is corrosion resistance and ageing resistance and has an antibacterial property.

Description

technical field [0001] The invention relates to the field of organic coatings, in particular to a quick-formed organic anti-corrosion protective film on metal surfaces. Background technique [0002] Anti-rust coatings applied to metal surfaces, coatings that protect metal surfaces from chemical or electrochemical corrosion of the atmosphere, sea water, etc. Coating anti-rust coatings on the metal surface can effectively prevent the direct invasion of various corrosive substances in the atmosphere, so as to maximize the extension of the service life of the metal. It can be divided into two categories: physical and chemical antirust paint. The former relies on the proper coordination of pigments and paints to form a dense paint film to prevent the intrusion of corrosive substances, such as iron red, aluminum powder, graphite antirust paint, etc.; the latter relies on the chemical antirust effect of antirust pigments, such as red Dan, zinc yellow antirust paint, etc. Used fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D5/08C09D5/14C09D7/12
CPCC08L2205/035C09D5/08C09D5/14C09D133/00C08L5/16C08L1/02C08K13/06C08K9/12C08K2003/0806C08K2003/265C08K5/521C08K3/34C08K2003/2272
Inventor 朱军岷朱炳仁
Owner 杭州朱炳仁铜艺股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More