Crack-resistant warm mortar and preparing method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology for thermal insulation mortar and raw materials, applied in the field of building materials, can solve the problems of affecting use and different performance and quality of mortar, and achieve the effects of improving compression resistance, outstanding thermal insulation and energy saving effect, and good adhesion.
Inactive Publication Date: 2017-03-22
GUANGXI UNIV
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] At present, the performance and quality
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0019] An anti-crack thermal insulation mortar, the raw materials are in the following ratio:
[0020] 5 parts of aluminum sulfate, 2 parts of alum, 15 parts of charcoal, 240 parts of perlite, 21 parts of pitch rock, 35 parts of obsidian, 31 parts of coal slime, 30 parts of fly ash, 4 parts of urea, 3 parts of potassium dihydrogen phosphate , 180 parts of cement, 41 parts of sepiolite wool, 110 parts of sand, 41 parts of silica fume, 2 parts of dodecyltrimethylammonium chloride, 41 parts of bentonite, 42 parts of coral powder, 4 parts of oil waste, flakes 3 parts of alkali, 2 parts of rosin, 3 parts of sodium pyrophosphate, 4 parts of monoethanolamine, 21 parts of PVA fiber, 83 parts of fly ash, 0.9 part of polyisobutylene, 6 parts of stainless steel fiber, 2 parts of acetylene carbon black, 0.3 part of lead isooctanoate , 4 parts of dipentaerythritol hexaacrylate, 2 parts of methyl methacrylate, 0.7 parts of amino resin, 1 part of organic bentonite, 0.6 parts of tartaric acid...
Embodiment 2
[0028] An anti-crack thermal insulation mortar, the raw materials are in the following ratio:
[0029] 8 parts of aluminum sulfate, 5 parts of alum, 19 parts of charcoal, 260 parts of perlite, 26 parts of pitch rock, 39 parts of obsidian, 42 parts of coal slime, 52 parts of fly ash, 6 parts of urea, and 6 parts of potassium dihydrogen phosphate , 210 parts of cement, 53 parts of sepiolite wool, 130 parts of sand, 52 parts of silica fume, 5 parts of dodecyltrimethylammonium chloride, 53 parts of bentonite, 48 parts of coral powder, 7 parts of oil waste, tablets 6 parts of alkali, 5 parts of rosin, 6 parts of sodium pyrophosphate, 8 parts of monoethanolamine, 27 parts of PVA fiber, 105 parts of fly ash, 1.4 parts of polyisobutylene, 9 parts of stainless steel fiber, 5 parts of acetylene carbon black, 0.6 parts of lead isooctanoate 6 parts of dipentaerythritol hexaacrylate, 4 parts of methyl methacrylate, 1.4 parts of amino resin, 1.5 parts of organic bentonite, 1.0 parts of tart...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a crack-resistant warm mortar and a preparing method thereof. The mortar is prepared from 5-8 parts of aluminum sulfate, 2-5 parts of alum, 15-19 parts of charcoal, 240-260 parts of perlite, 21-26 parts of pitchstone, 35-39 parts of obsidian, 31-42 parts of coal slime, 30-52 parts of coal ash, 4-6 parts of urea, 3-6 parts of monopotassium phosphate, 180-210 parts of cement, 41-53 parts of sepiolite fabric, 110-130 parts of grid, 41-52 parts of silica fume, 2-5 parts of dodecyl trimethyl ammonium chloride and 41-53 parts of bentonite. According to the crack-resistant warm mortar and the preparing method thereof, the mortar is good in adhesiveness, water-retaining property and heat preservation and insulation performance and remarkable in heat preservation and energy conservation effect; by the use of the sepiolite fabric, the mortar further has good crack-resistant performance, and is applicable to masonry and plastering construction of wall body material; by using auxiliary, compression and fracture resistant strength of the mortar is improved, and peaceability, anti-sagging property, thixotropy and anti-subsidence performance are improved.
Description
technical field [0001] The invention relates to the technical field of building materials, in particular to a crack-resistant thermal insulation mortar and a preparation method thereof. Background technique [0002] Mortar: The bonding substance used for bricklaying in buildings. It is composed of a certain proportion of sand and cementing materials (cement, lime paste, clay, etc.) and water. It is also called mortar and mortar. Mortar is made by mixing cementitious materials (cement, lime, clay, etc.) and fine aggregate (sand) with water. Commonly used are cement mortar, mixed mortar (or cement-lime mortar), lime mortar and clay mortar. [0003] At present, the performance and quality of mortar are different, which affects the use. Specifically, the factors that affect the performance of mortar include the workability, fluidity, water retention of freshly mixed mortar, and the strength of hardened mortar. New mortars need to be researched to have excellent construction a...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more