Preparing method for load magnetic metal sepiolite composite powder or fiber
A sepiolite fiber and magnetic metal technology, applied in metal processing equipment, coating, transportation and packaging, etc., can solve the problems of insignificant absorption effect, high density, narrow absorption frequency band, etc., and achieve easy magnetic loss matching characteristics, Simple preparation method and good adsorption effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0042] Example 1
[0043] After the sepiolite powder is burned in an oven at 120° C. for 12 hours, it is cooled, ground, and passed through a 200-mesh sieve to obtain the pretreated sepiolite powder. Using xylene as the organic solvent, the carbonyl iron content in the solution system is 50% by mass to configure the metal organic solution system, and added to the 20L reactor, the filling volume is 50%, and the liquid-to-solid ratio is 4 to the pretreated Sepiolite powder. The reactor was closed, nitrogen was introduced, and the oxygen in the reactor was removed. Set up 3 heating programs: (1) heating from room temperature 120min to 100℃, (2) heating from 100℃ 540min to 120℃, (3) heating from 120℃ 240min to 135℃. Then the temperature is lowered to room temperature, and the material is discharged. The obtained material is washed with absolute ethanol, filtered, dried, ground, and sieved to obtain the reaction product, which is the sepiolite fiber composite powder loaded with magn...
Example Embodiment
[0046] Example 2
[0047] After the sepiolite powder is burned in an oven at 120° C. for 12 hours, it is cooled, ground, and passed through a 200-mesh sieve to obtain the pretreated sepiolite powder. Xylene is an organic solvent, and iron carbonyl and cobalt carbonyl are mixed in a ratio of 1:1 by mass. The mixture of iron pentacarbonyl and dicobalt octacarbonyl in the solution system is configured with a metal organic solution system with a mass percentage of 50%, and added to 20L reaction In the kettle, the filling volume is 50%, and the pretreated sepiolite powder is added with a liquid-solid ratio of 4. The reactor was closed, nitrogen was introduced, and the oxygen in the reactor was removed. Set up 3 heating programs: (1) heating from room temperature 120min to 100℃, (2) heating from 100℃ 540min to 120℃, (3) heating from 120℃ 240min to 135℃. Then the temperature is lowered to room temperature and the material is discharged. The obtained material is washed with absolute et...
Example Embodiment
[0048] Example 3
[0049] Prepare a silane coupling agent (KH550) 95% ethanol solution with a concentration of 0.5mmol / L, add sepiolite fiber to the silane coupling agent 95% ethanol solution at a liquid-solid ratio of 3, stir at 20°C for 60 minutes, then wash and filter , Dried at 120℃ for 2h, cooled, ground, and sieved to obtain pretreated sepiolite fiber. Quinoline is an organic solvent. Nickel tetracarbonyl and dimanganese decacarbonyl are mixed at a mass percentage of 2.6:1. The mixture of nickel tetracarbonyl and dimanganese decacarbonyl has a mass percentage of 30% in the solution system. The metal organic solution system is configured and added to In the 20L reactor, the filling volume is 50%, and the pretreated sepiolite powder is added with a liquid-solid ratio of 8. The reactor was closed, nitrogen was introduced, and the oxygen in the reactor was removed. Set up 3 heating programs: (1) from room temperature 240min to 150℃, (2) from 150℃ to 480min to 200℃, (3) from 2...
PUM
Property | Measurement | Unit |
---|---|---|
Saturation magnetization | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap