Preparation method of tipping paper body stock for cigarettes
A technology of tipping paper and base paper for cigarettes, which is applied in the process of adding pulp raw materials, paper, papermaking, etc., can solve the problem of poor air permeability of base paper for cigarette tipping paper, wear resistance, smoothness and physical strength of base paper for tipping paper. Meet the printing process requirements and other issues, to achieve the effect of reducing the harm to the human body, high smoothness, and good tar reduction effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0015] Example 1
[0016] First weigh 20g polystyrene resin, 15g polymethyl methacrylate resin and 3g silane coupling agent KH-550 into a beaker containing 150mL acetone, and heat to 70℃, stir to dissolve for 30min, and then add to the flask Add 100 mL of 5% sodium hydroxide solution with a mass fraction of 5% to 40°C, cool to 40°C, stir and react for 2h. When the reaction is over, stop heating, collect the product for use; then weigh 20 parts by weight of poplar slag, 10 parts Part bamboo shavings, 35 parts alkali-free glass fiber, 8 parts polyvinylpyrrolidone, 40 parts water and 1 part nano-zinc oxide are added to the beater for beating, beating to 65°SR to obtain slurry; then weigh 5g iron Yellow, 8g polyvinyl alcohol, 3g chitosan, 6g polyacrylamide and 200g of the above slurry are added to the blender. After stirring and mixing for 3 minutes, add water to the blender to adjust the solid content of the slurry to 8%. The slurry is formed by a paper press at a speed of 1.3 cm / s...
Example Embodiment
[0018] Example 2
[0019] First, weigh 25g polystyrene resin, 18g polymethyl methacrylate resin and 4g silane coupling agent KH-550 into a beaker containing 175mL acetone, and heat to 75°C, stir and dissolve for 35min, then add to the flask Add 150mL of a 5% sodium hydroxide solution with a mass fraction of 5%, cool to 45°C, stir and react for 2h. When the reaction is over, stop heating, collect the product for use; then weigh 25 parts by weight of poplar slag, 15 parts Part bamboo shavings, 40 parts alkali-free glass fiber, 10 parts polyvinylpyrrolidone, 45 parts water and 2 parts nano-zinc oxide are added to the beater for beating, beating to 68°SR to obtain slurry; then weigh 8g iron Yellow, 10g polyvinyl alcohol, 4g chitosan, 7g polyacrylamide and 250g of the above slurry are added to the blender. After stirring and mixing for 4 minutes, add water to the blender to adjust the solid content of the slurry to 9%. The slurry is formed by a paper press at a speed of 1.4cm / s, and ...
Example Embodiment
[0021] Example 3
[0022] First weigh 30g polystyrene resin, 20g polymethyl methacrylate resin and 5g silane coupling agent KH-550 into a beaker containing 200mL acetone, and heat to 80℃, stir to dissolve for 40min, and then add to the flask Add 200 mL of 5% sodium hydroxide solution with a mass fraction of 5% to the mixture, cool to 50°C, stir and react for 3 hours, after the reaction is over, stop heating, collect the product, and use it for later use; then weigh 30 parts of cypress slag, 20 parts by weight Part bamboo shavings, 45 parts alkali-free glass fiber, 12 parts polyvinylpyrrolidone, 50 parts water and 3 parts nano-zinc oxide are added to the beater for beating, beating to 70°SR to obtain slurry; then weighing 10g iron Yellow, 12g polyvinyl alcohol, 5g chitosan, 8g polyacrylamide and 300g of the above slurry are added to the blender. After stirring and mixing for 5 minutes, add water to the blender to adjust the solid content of the slurry to 10%. The slurry is formed...
PUM
Property | Measurement | Unit |
---|---|---|
Length | aaaaa | aaaaa |
Width | aaaaa | aaaaa |
Longitudinal tensile strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap