Fluorocarbon coating good in adhesive force

A technology of fluorocarbon coatings and adhesion, applied in anti-corrosion coatings, fire-proof coatings, coatings, etc., can solve the problems of construction personnel poisoning, difficult implementation of tools, cleaning, etc., to achieve low VOC content, good adhesion, and extended use The effect of longevity

Inactive Publication Date: 2017-07-25
HEFEI LYUJIE ENVIRONMENTAL PROTECTION TECH
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The current fluorocarbon paint is mainly solvent-based, and because the solvent-based fluorocarbon paint contains high VOC, the solvent will be directly volatilized in the air during construction and cannot be recycled, resulting in waste of resources, polluting the environment, and causing some harm to construction workers. Toxic, implementing tools are difficult to clean
In addition, the paint film of solvent-based fluorocarbon paint is dense, the adhesion is poor, and local foaming is easy to form, which needs to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A kind of fluorocarbon paint with good adhesion proposed by the present invention, its raw materials include by weight: 40 parts of polyvinylidene fluoride, 25 parts of acrylic modified alkyd resin, 2 parts of crosslinking agent, 30 parts of urea compound, glass 4 parts of microbeads, 8 parts of calcined kaolin, 4 parts of carbon nanotubes, 4 parts of nano-titanium dioxide, 1 part of magnesium oxide, 2 parts of waterproofing agent, 1 part of anti-aging agent, 3 parts of polyethylene wax.

Embodiment 2

[0017] A kind of fluorocarbon coating with good adhesion proposed by the present invention, its raw materials include by weight: 50 parts of polyvinylidene fluoride, 15 parts of acrylic modified alkyd resin, 4 parts of crosslinking agent, 20 parts of urea compound, glass 10 parts of microbeads, 2 parts of calcined kaolin, 8 parts of carbon nanotubes, 1 part of nano-titanium dioxide, 2 parts of magnesium oxide, 1 part of waterproofing agent, 3 parts of anti-aging agent, 1 part of polyethylene wax.

[0018] The urea complex is prepared by the following process: Stir formaldehyde, polyvinyl alcohol, ammonia water, and water, add urea, heat up and stir, use sodium hydroxide to adjust the pH of the system to 7.8-8.4, add alkali lignin, oxidized starch, borax, and heat up Stir, add diphenyldihydroxysilane and trimethoxyphenylsilane and mix evenly, add tetramethyldivinyldisiloxane, heat up and stir, cool to room temperature, and dry to obtain a urea complex.

Embodiment 3

[0020] A kind of fluorocarbon coating with good adhesion proposed by the present invention, its raw materials include by weight: 42 parts of polyvinylidene fluoride, 22 parts of acrylic modified alkyd resin, 2.5 parts of crosslinking agent, 28 parts of urea compound, glass 6 parts of microbeads, 6 parts of calcined kaolin, 5 parts of carbon nanotubes, 3 parts of nano-titanium dioxide, 1.5 parts of magnesium oxide, 1.5 parts of waterproofing agent, 1.5 parts of anti-aging agent, 2.5 parts of polyethylene wax.

[0021] The crosslinking agent comprises by weight: 1 part of caprolactam-blocked isophorone diisocyanate, and 2 parts of N,N-dimethylethanolamine.

[0022] The urea complex was prepared by the following process: Stir formaldehyde, polyvinyl alcohol, ammonia water, and water for 3 hours, add urea, raise the temperature to 138°C and stir for 0.8 hours, adjust the pH of the system to 7.8-8.4 with sodium hydroxide, add alkali lignin, Oxidized starch and borax, heat up to 90°...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a fluorocarbon coating good in adhesive force. The fluorocarbon coating good comprises the following raw materials in parts by weight: 40-50 parts of polyvinylidene fluoride, 15-25 parts of acrylic modified alkyd resin, 2-4 parts of a crosslinking agent, 20-30 parts of a urea composition, 4-10 parts of glass beads, 2-8 parts of calcined kaolin, 4-8 parts of a carbon nanotube, 1-4 parts of nano titanium dioxide, 1-2 parts of magnesium oxide, 1-2 parts of a waterproof agent, 1-3 parts of an antiageing agent and 1-3 parts of polyethylene wax. The fluorocarbon coating good in adhesive force disclosed by the invention is excellent in ageing resistance, excellent in strong chemical corrosion resistance and good in adhesive force, and avoids bubbling and falling phenomena in severe environments, and the service life is prolonged.

Description

technical field [0001] The invention relates to the technical field of fluorocarbon coatings, in particular to a fluorocarbon coating with good adhesion. Background technique [0002] Fluorocarbon paint has attracted the attention and favor of the decoration industry for its unique weather resistance, stain resistance, solvent resistance, acid and alkali resistance, and hydrophobic properties. [0003] The current fluorocarbon paint is mainly solvent-based, and because the solvent-based fluorocarbon paint contains high VOC, the solvent is directly volatilized in the air during construction and cannot be recycled, resulting in waste of resources, polluting the environment, and has certain harm to the construction workers. Poisonous, the implementation tool is difficult to clean. In addition, the paint film of solvent-based fluorocarbon paint is dense, the adhesion is poor, and it is easy to form local blisters, which needs to be solved urgently. Contents of the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/16C09D5/08C09D7/12
CPCC09D127/16C08K2003/222C08K2003/2241C08K2201/011C08L2201/08C08L2205/03C08L2312/00C09D5/08C09D5/18C09D7/61C09D7/63C09D7/65C08L67/08C08L23/06C08K13/06C08K9/08C08K9/02C08K9/04C08K9/06C08K5/21C08K7/20C08K7/24C08K3/22C08K3/346
Inventor 王成刘梅霞潘海洋
Owner HEFEI LYUJIE ENVIRONMENTAL PROTECTION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com