High-weatherability environment-friendly decoration material and preparation method thereof

A decorative material, high weather resistance technology

Inactive Publication Date: 2017-09-01
HEFEI ANLI ELECTRIC POWER ENG CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Decorative materials in the prior art are easily affected by climate, such as rainy weather is easy to get damp, cold weather is easy to crack, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] An environment-friendly decorative material with high weather resistance, comprising the following components in parts by weight: 5 parts of aramid fiber, 10 parts of cellulose powder, 5 parts of coated perlite, 6 parts of organic polymer emulsion, plastic polymethacrylate 5 parts of ester, 3 parts of medium alkali glass fiber, 5 parts of filler, 2 parts of redispersible rubber powder, 3 parts of light magnesium carbonate filler, 1.5 parts of pigment, 1 part of stabilizer, 1 part of defoamer, 2 parts of lubricant share.

[0023] Preferably, the filler is one or a combination of calcium carbonate, wollastonite powder, talcum powder, quartz sand, kaolin; the redispersible rubber powder is one of ethylene vinyl acetate or vinyl chloride ethylene vinyl laurate or any combination.

[0024] Preferably, the pigment is a fluorescent pigment or a luminescent pigment.

[0025] Preferably, the coated expanded perlite is prepared in the following manner: take 100 mesh expanded pe...

Embodiment 2

[0034] An environment-friendly decorative material with high weather resistance, comprising the following components in parts by weight: 7 parts of aramid fiber, 12 parts of cellulose powder, 9 parts of coated perlite, 12 parts of organic polymer emulsion, plastic polymethacrylate 10 parts of ester, 4 parts of medium-alkali glass fiber, 9 parts of filler, 4 parts of redispersible rubber powder, 6 parts of light magnesium carbonate filler, 2 parts of pigment, 2 parts of stabilizer, 3 parts of defoamer, and 4 parts of lubricant share.

[0035] Preferably, the filler is one or a combination of calcium carbonate, wollastonite powder, talcum powder, quartz sand, kaolin; the redispersible rubber powder is one of ethylene vinyl acetate or vinyl chloride ethylene vinyl laurate or any combination.

[0036] Preferably, the pigment is a fluorescent pigment or a luminescent pigment.

[0037] Preferably, the coated expanded perlite is prepared in the following manner: take 100 mesh expan...

Embodiment 3

[0046] An environment-friendly decorative material with high weather resistance, comprising the following components in parts by weight: 10 parts of aramid fiber, 14 parts of cellulose powder, 13 parts of coated perlite, 18 parts of organic polymer emulsion, plastic polymethacrylate 15 parts of ester, 6 parts of medium alkali glass fiber, 13 parts of filler, 6 parts of redispersible rubber powder, 9 parts of light magnesium carbonate filler, 2.5 parts of pigment, 3 parts of stabilizer, 5 parts of defoamer, 6 parts of lubricant share.

[0047] Preferably, the filler is one or a combination of calcium carbonate, wollastonite powder, talcum powder, quartz sand, kaolin; the redispersible rubber powder is one of ethylene vinyl acetate or vinyl chloride ethylene vinyl laurate or any combination.

[0048] Preferably, the pigment is a fluorescent pigment or a luminescent pigment.

[0049] Preferably, the coated expanded perlite is prepared in the following manner: take 100 mesh expa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-weatherability environment-friendly decoration material, which is prepared from the following ingredients in parts by weight: 5 to 10 parts of aramid fiber, 10 to 14 parts of cellulose powder, 5 to 13 parts of film coating perlite, 6 to 18 parts of organic polymer emulsion, 5 to 15 parts of plastic polymethylmethacrylate, 3 to 6 parts of medium-alkali glass fiber, 5 to 13 parts of filling materials, 2 to 6 parts of redispersible glue powder, 3 to 9 parts of filling materials of light-weight magnesium carbonate, 1.5 to 2.54 parts of pigments, 1 to 3 parts of stabilizing agents, 1 to 5 parts of defoaming agents and 2 to 6 parts of lubricating agents. The environment-friendly decoration material prepared by the method has the advantages that the product weatherability is high; the high-weatherability environment-friendly decoration material is particularly suitable for being used in outdoor positions; the wind-proof and rain-proof effects are achieved; the maintenance cost is low.

Description

technical field [0001] The invention belongs to the field of decorative materials, and in particular relates to a highly weather-resistant environment-friendly decorative material and a preparation method thereof. Background technique [0002] It has become a consensus that environmental pollution will induce pathological changes in the human body. The pathogenic bacteria, PM2.5 fine particles and pathogenic and carcinogenic organic substances permeating the living environment have attracted more and more attention. Formaldehyde, volatile organic compounds (Volatile Organic Compounds, VOC) and fine dust particles produced by interior decoration materials , Toxic ingredients have become the first concern of consumers after house decoration. Among them, formaldehyde is a colorless gas with a strong pungent smell. It is very volatile at room temperature, and the volatile amount increases with the increase of temperature. It has a strong stimulating effect on human skin and muc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L1/02C08L77/10C08L101/00C08L33/12C08K13/06C08K9/08C08K9/02C08K7/26C08K7/14C08K3/26C08K3/34
CPCC08L1/02C08K2003/262C08K2201/003C08L2205/025C08L2205/035C08L2205/16C08L77/10C08L101/00C08L33/12C08K13/06C08K9/08C08K9/02C08K7/26C08K7/14C08K3/26C08K3/346
Inventor 殷世尧
Owner HEFEI ANLI ELECTRIC POWER ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com