Purple sand clay-containing colored glaze

A technology of purple sand soil and ingredients is applied in the field of colored glass containing purple sand soil, which can solve the problems of insufficient color rendering, high stability, high price of colored glass products, insufficient glaze gloss, etc., and achieves excellent product quality, improved product value, Bright and bright effect

Inactive Publication Date: 2017-10-03
太仓市科教新城琉璃艺术策划中心
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The process of making colored glaze requires dozens of manual operations to complete, and a slight negligence can cause failure or flaws. Therefore, its value is high, which has led people to attach great importance to the quality of colored glaze products, which has also caused the price of colored glaze products. More expensive, the production process is extremely complicated, and the product cost is high, which is unbearable for ordinary consumers
At the same time, the quality of the current glass products is not stable enough, the gloss of the glaze is not enough, the color is not rich and stable enough, and it is easy to fade under sunlight

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The colored glaze containing purple sand soil composition includes the following components in mass parts: 90 parts of purple sand soil, 4 parts of sodium nitrate, 16 parts of cuprous oxide, 17 parts of lead dioxide, 10 parts of sodium chloride, 12 parts of small bluestone, calcium carbonate 6 parts of antimony oxide, 15 parts of talc, 6 parts of lithium carbonate, 2 parts of explosion-proof fiber, 1 part of starch, 1 part of charcoal powder, 4 parts of potassium feldspar, 2 parts of magnesium carbonate, 1 part of phenolic resin, 17 parts of quartz sand, three 9 parts of alumina, 5 parts of ceria, 20 parts of iron oxide yellow, 4 parts of zirconia, 2 parts of TEOS, and 3 parts of polytetrafluoroethylene.

Embodiment 2

[0016] The colored glaze containing purple sand soil composition includes the following components in mass parts: 110 parts of purple sand soil, 12 parts of sodium nitrate, 20 parts of cuprous oxide, 25 parts of lead dioxide, 12 parts of sodium chloride, 16 parts of small bluestone, calcium carbonate 10 parts of antimony oxide, 22 parts of talc, 10 parts of lithium carbonate, 4 parts of explosion-proof fiber, 8 parts of starch, 8 parts of charcoal powder, 8 parts of potassium feldspar, 16 parts of magnesium carbonate, 5 parts of phenolic resin, 22 parts of quartz sand, three 11 parts of alumina, 9 parts of ceria, 30 parts of iron oxide yellow, 8 parts of zirconia, 4 parts of TEOS, and 6 parts of polytetrafluoroethylene.

Embodiment 3

[0018] The colored glaze containing purple sand soil composition includes the following components in mass parts: 100 parts of purple sand soil, 8 parts of sodium nitrate, 18 parts of cuprous oxide, 22 parts of lead dioxide, 11 parts of sodium chloride, 14 parts of small bluestone, calcium carbonate 8 parts of antimony oxide, 20 parts of talc, 8 parts of lithium carbonate, 3 parts of explosion-proof fiber, 5 parts of starch, 5 parts of charcoal powder, 6 parts of potassium feldspar, 9 parts of magnesium carbonate, 3 parts of phenolic resin, 20 parts of quartz sand, three parts 10 parts of alumina, 7 parts of ceria, 25 parts of iron oxide yellow, 6 parts of zirconia, 3 parts of TEOS, and 5 parts of polytetrafluoroethylene.

[0019] To sum up: the colored glaze containing purple sand soil composition of the present invention has the characteristics of excellent product quality, greatly improves product value, adopts purple sand soil as the main component, greatly reduces producti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses purple sand clay-containing colored glaze. The purple sand clay-containing colored glaze is characterized by comprising the following components in parts by mass: 90-110 parts of purple sand clay, 4-12 parts of sodium nitrate, 16-20 parts of cuprous oxide, 17-25 parts of lead dioxide, 10-12 parts of sodium chloride, 12-16 parts of small bluestone, 6-10 parts of calcium carbonate antimony oxide, 15-22 parts of talcum, 6-10 parts of lithium carbonate, 2-4 parts of explosion-proof fiber, 1-8 parts of starch, 1-8 parts of charcoal powder, 4-8 parts of potassium feldspar, 2-16 parts of magnesium carbonate, 1-5 parts of phenol-formaldehyde resin, 17-22 parts of quartz sand, 9-11 parts of aluminum sesquioxide, 5-9 parts of cerium dioxide, 20-30 parts of ferric oxide yellow, 4-8 parts of zirconium oxide, 2-4 parts of TEOS and 3-6 parts of polytetrafluoroethylene. The invention provides the purple sand clay-containing colored glaze which is good in glaze gloss, non-fading and more environmentally friendly; the production process is simplified, the efficiency is improved, the process time is shortened, and the production cost is reduced.

Description

technical field [0001] The invention relates to a kind of colored glaze, in particular to a kind of colored glaze containing purple clay. Background technique [0002] Glass is an ancient and traditional ceramic material in my country. Its material is solid, bright in color and smooth in glaze. It has been used as a traditional Chinese architectural component. After successive developments and quality improvements, it has been widely used in modern architecture due to its many excellent functions. With the development of tourism, people's demand for glazed tiles is also increasing, and their requirements are also getting higher and higher. The process of making colored glaze requires dozens of manual operations to complete, and a slight negligence can cause failure or flaws. Therefore, its value is high, which has led people to attach great importance to the quality of colored glaze products, which has also caused the price of colored glaze products. More expensive, the pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C14/00C03C6/04C03C4/02
CPCC03C14/00C03C1/00C03C4/02C03C14/002
Inventor 孙武
Owner 太仓市科教新城琉璃艺术策划中心
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products