Pipe for discharging sewage and preparation method of pipe

A sewage and pipeline technology, which is applied in the sewage pipeline and its preparation field, can solve problems such as insufficient pressure resistance and strength, shortened pipeline life, waste of manpower and material resources, etc., to achieve improved bending strength and tensile strength, and improved durability The effect of low corrosion and water repellency

Inactive Publication Date: 2017-11-10
HEFEI ANLI ELECTRIC POWER ENG CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the drainage process, the pipeline will be continuously corroded and infected, and the pressure resistance and strength are not enough, which will shorten the life of the pipeline, which is not only not environmentally friendly, but also uneconomical, and will waste more manpower and material resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A sewage pipe, comprising the following raw materials in parts by weight: 60 parts of unsaturated polyester resin, 13 parts of polyphenylene sulfide, 6 parts of liquid polyisoprene rubber, 3 parts of calcium carbonate, 2 parts of asbestos powder, 4 parts of sodium selenate, 2 parts of polychlorotrifluoroethylene, 3 parts of basalt fiber, 2 parts of polyvinyl acetate, 2 parts of epoxy linseed oil, 1.5 parts of polyolefin elastomer POE, 1 part of preservative, dispersant 1 serving.

[0021] Described calcium carbonate is 200 mesh heavy calcium carbonate.

[0022] The unsaturated polyester resin is a p-phenylene type unsaturated polyester resin, and the viscosity of the resin is 700mpa.s.

[0023] The preservative is selected from one of potassium sorbate, sodium benzoate, xylene or methylparaben or a mixture thereof.

[0024] A method for preparing a sewage pipeline, comprising the following steps:

[0025] Step 1: taking raw materials according to parts by weight;

...

Embodiment 2

[0032] A sewage pipe, comprising the following raw materials in parts by weight: 80 parts of unsaturated polyester resin, 16 parts of polyphenylene sulfide, 10 parts of liquid polyisoprene rubber, 6 parts of calcium carbonate, 4 parts of asbestos powder, 7 parts of sodium selenate, 4 parts of polychlorotrifluoroethylene, 6 parts of basalt fiber, 6 parts of polyvinyl acetate, 3 parts of epoxy linseed oil, 5 parts of polyolefin elastomer POE, 3 parts of preservative, 2 parts of dispersant .

[0033] Described calcium carbonate is 300 purpose ground calcium carbonate.

[0034] The unsaturated polyester resin is a p-phenylene type unsaturated polyester resin, and the viscosity of the resin is 800mpa.s.

[0035] The preservative is selected from one of potassium sorbate, sodium benzoate, xylene or methylparaben or a mixture thereof.

[0036] A method for preparing a sewage pipeline, comprising the following steps:

[0037] Step 1: taking raw materials according to parts by weigh...

Embodiment 3

[0044] A sewage pipe, comprising the following raw materials in parts by weight: 90 parts of unsaturated polyester resin, 19 parts of polyphenylene sulfide, 14 parts of liquid polyisoprene rubber, 9 parts of calcium carbonate, 6 parts of asbestos powder, 9 parts of sodium selenate, 6 parts of polychlorotrifluoroethylene, 6 parts of basalt fiber, 9 parts of polyvinyl acetate, 5 parts of epoxy linseed oil, 7 parts of polyolefin elastomer POE, 4 parts of preservative, 3 parts of dispersant .

[0045] Described calcium carbonate is 400 mesh heavy calcium carbonate.

[0046] The unsaturated polyester resin is a p-phenylene type unsaturated polyester resin, and the viscosity of the resin is 900mpa.s.

[0047] The preservative is selected from one of potassium sorbate, sodium benzoate, xylene or methylparaben or a mixture thereof.

[0048] A method for preparing a sewage pipeline, comprising the following steps:

[0049] Step 1: taking raw materials according to parts by weight; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
particle sizeaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a pipe for discharging sewage. The pipe is prepared from the following raw materials in parts by weight: 60-90 parts of unsaturated polyester resin, 13-19 parts of polyphenylene sulfide, 6-14 parts of liquid polyisoprene rubber, 3-9 parts of calcium carbonate, 2-6 parts of asbestos powder, 4-9 parts of sodium selenite, 2-6 parts of polychlorotrifluoroethylene, 3-6 parts of basalt fibers, 2-9 parts of polyvinyl acetate, 2-5 parts of epoxidized linseed oil, 1.5-7 parts of a POE (polyolefin elastomer), 1-4 parts of an anticorrosive agent and 1-3 parts of a dispersant. The pipe has the advantages that a preparation method is simple and easy to implement, the cost is lower, and raw materials are available; the unsaturated polyester resin, polyphenylene sulfide, the liquid polyisoprene rubber, calcium carbonate and the like are mixed to be used as materials of the pipe; the unsaturated polyester resin has excellent chemical stability, heat and cold resistance, weather resistance, hydrophobicity and low surface tension and does not produce substances polluting the environment, and the anticorrosive agent is added, so that corrosion resistance of the inner surface of the pipe can be significantly improved.

Description

technical field [0001] The invention belongs to the field of pipeline materials, and in particular relates to a sewage drainage pipeline and a preparation method thereof. Background technique [0002] In recent years, with the rapid development of the economy, our environment has also been damaged to varying degrees, among which water pollution is particularly serious. The sewage mainly comes from various industries such as chemical energy, metal smelting, automobiles, and medicine. Although it will be discharged to a certain standard after certain treatment, it will still contain a large amount of acid and alkali, heavy metal ions, and bacteria. During the drainage process, the pipeline will be continuously corroded and infected, and the pressure resistance and strength are not enough, which will shorten the life of the pipeline, which is not only not environmentally friendly, but also uneconomical, and will waste more manpower and material resources. Therefore, it is of g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/06C08L81/02C08L9/00C08L27/12C08L31/04C08L23/08C08L91/00C08K13/04C08K7/12C08K3/26C08K3/24C08K7/10C08K5/098
CPCC08L67/06C08K2201/003C08L2201/08C08L2203/18C08L2205/035C08L81/02C08L9/00C08L27/12C08L31/04C08L23/0815C08L91/00C08K13/04C08K7/12C08K3/26C08K3/24C08K7/10C08K5/098
Inventor 殷世尧
Owner HEFEI ANLI ELECTRIC POWER ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products