Sealing part for automobile LED instrument panel

A technology for instrument panels and seals, applied in the field of seals for automotive LED instrument panels, can solve the problems of the toughness and tear resistance of shock-absorbing rubber, and achieve enhanced hydrophobic and mechanical properties, high waterproof performance, and enhanced toughness. Effect

Inactive Publication Date: 2017-11-24
ANHUI LAND GRP
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still problems in the toughness and tear resistance of the shock-absorbing rubber of automotive LED instruments, which need to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] The present invention proposes a kind of sealant for automotive LED instrument panel, and its raw material comprises by weight: 50 parts of main material, 1.2 parts of disproportionated rosin, 1 part of polyphenylene sulfide, 1 part of polyphenylene ester, 55 parts of filler, over 1 part of di-tert-butyl oxide, 1 part of 2,4-dichlorobenzoyl peroxide, 1 part of maleic anhydride, 0.2 part of γ-(ethylenediamino)propylmethyldimethoxysilane, titanic acid 1 part of butyl ester, 1 part of magnesium stearate, 2 parts of coal tar, 1 part of antioxidant.

Embodiment 2

[0015] A kind of sealing member for automotive LED instrument panel proposed by the present invention, its raw material comprises by weight: 60 parts of main material, 0.5 part of disproportionated rosin, 2 parts of polyphenylene sulfide, 0.4 part of polyphenylene ester, 65 parts of filler, over 0.2 parts of di-tert-butyl oxide, 2 parts of 2,4-dichlorobenzoyl peroxide, 0.4 parts of maleic anhydride, 0.8 parts of γ-(ethylenediamino)propylmethyldimethoxysilane, titanic acid 0.4 parts of butyl ester, 3 parts of magnesium stearate, 1 part of coal tar, and 3 parts of antioxidant.

[0016] The main ingredients include by weight: 30 parts of EPDM rubber and 18 parts of polytetrafluoroethylene. The filler comprises by weight: 30 parts of calcium carbonate compound and 25 parts of nanometer talcum powder.

[0017] Calcium carbonate complex is prepared by the following process: heat up water, add sulfated sodium oleate evenly under stirring, add stearic acid and palmitic acid and stir,...

Embodiment 3

[0019] A kind of sealing member for automotive LED instrument panel proposed by the present invention, its raw material comprises by weight: 52 parts of main material, 1 part of disproportionated rosin, 1.2 parts of polyphenylene sulfide, 0.8 part of polyphenylene ester, 58 parts of filler, over 0.8 parts of di-tert-butyl oxide, 1.2 parts of 2,4-dichlorobenzoyl peroxide, 0.8 parts of maleic anhydride, 0.4 parts of γ-(ethylenediamino)propylmethyldimethoxysilane, titanic acid 0.8 parts of butyl ester, 1.5 parts of magnesium stearate, 1.8 parts of coal tar, and 1.5 parts of anti-aging agent.

[0020] The main ingredients include by weight: 50 parts of EPDM rubber and 5 parts of polytetrafluoroethylene. The filler comprises by weight: 50 parts of calcium carbonate compound and 15 parts of nanometer talcum powder.

[0021] The calcium carbonate compound is prepared by the following process: warm water to 94°C, add sulfated sodium oleate evenly under stirring, add stearic acid and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a sealing part for an automobile LED instrument panel. The sealing part is prepared from raw materials in parts by weight as follows: 50-60 parts of a main material, 0.5-1.2 parts of disproportionated rosin, 1-2 parts of polyphenylene sulfide, 0.4-1 part of polybenzoate, 55-65 parts of filler, 0.2-1 part of di-tert-butyl peroxide, 1-2 parts of 2,4-dichlorobenzoyl peroxide, 0.4-1 part of maleic anhydride, 0.2-0.8 parts of 3-(2-aminoethylamino)propyl-dimethoxymethylsilane, 0.4-1 part of butyl titanate, 1-3 parts of magnesium stearate, 1-2 parts of coal tar and 1-3 parts of an anti-aging agent. The sealing part for the automobile LED instrument panel has high density, good toughness, extremely high waterproof performance and excellent tearing resistance.

Description

technical field [0001] The invention relates to the technical field of seals, in particular to a seal for an automobile LED instrument panel. Background technique [0002] The instruments on the LED dashboard of different cars are not the same, but the conventional instruments of a general car include speedometer, tachometer, oil pressure gauge, water temperature gauge, fuel gauge, charging gauge, etc. In modern cars, automotive LED meters also need to be equipped with voltage regulators, which are specially used to stabilize the voltage of the instrument power supply and suppress fluctuations to ensure the accuracy of automotive LED meters. However, there are still problems in the toughness and tear resistance of the shock-absorbing rubber of automotive LED instruments, which need to be solved urgently. Contents of the invention [0003] Based on the technical problems existing in the background technology, the present invention proposes a sealing member for automotive L...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/16C08L27/18C08L93/04C08L81/02C08K13/06C08K9/04C08K3/26C08K5/14C08K5/098C08K5/544C08K5/1539C08K3/34
CPCC08K2003/265C08K2201/011C08K2201/014C08L23/16C08L2205/035C08L27/18C08L93/04C08L81/02C08K13/06C08K9/04C08K3/26C08K5/14C08K5/098C08K5/544C08K5/1539C08K3/34
Inventor 李正祥杨学青高耀辉陈佳明刘琴
Owner ANHUI LAND GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap