PVC board and preparation process thereof

A preparation process and board technology, applied in the field of PVC board and its preparation technology, can solve the problems of processing performance, poor impact resistance and aging resistance, poor thermal stability, easy softening and relaxation, etc., to achieve good thermal stability, improve Appearance, profile smooth effect

Inactive Publication Date: 2017-12-15
SUZHOU FUTONG NEW MATERIALS & HIGH TECH
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Existing PVC plastic special-shaped plates have the following defects: 1. High cost; 2. Poor thermal stability, hardening and brittle at low temperature, easy to soften and relax at high temperature; 3. Poor processing performance, impact resistance and aging resistance ; 3. Release harmful substances during the production process and produce hazardous waste products. The finished product will release dioxin acid gas at high temperature, and its additives will gradually volatilize during use, polluting the air

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A PVC board, comprising by weight components: 40 parts of polyvinyl chloride resin, 0.1 part of white oil, 2.5 parts of stabilizer, 1 part of titanium dioxide, 0.1 part of stearic acid, 0.1 part of polyethylene wax, stearic acid amide 0.01 part, 0.01 part of ultraviolet absorber, 0.01 part of coloring agent, 0.01 part of fluorescent whitening agent OB, 10 parts of activated calcium carbonate, 10 parts of talcum powder, and 0.1 part of foaming agent.

[0027] Specifically, the density of the polyvinyl chloride resin is 1.35~1.45g / cm 3 , the apparent density is 0.4~0.5 g / cm 3 .

[0028] Specifically, the polyvinyl chloride resin is a loose polyvinyl chloride resin with a particle size of 0.1-0.2 mm and is in the shape of cotton balls.

[0029] Specifically, the stabilizer includes 2 parts of tribasic lead sulfate and 0.5 part of dibasic lead stearate. More specifically, it has excellent thermal stability, long-term performance, good electrical insulation and weather re...

Embodiment 2

[0041] A PVC board, comprising by weight components: 60 parts of polyvinyl chloride resin, 0.5 parts of white oil, 3 parts of stabilizer, 3 parts of titanium dioxide, 0.5 parts of stearic acid, 0.3 parts of polyethylene wax, stearic acid amide 0.5 parts, 0.2 parts of UV absorber, 0.03 parts of coloring agent, 0.1 part of fluorescent whitening agent OB, 20 parts of activated calcium carbonate, 20 parts of talcum powder, and 0.3 parts of foaming agent.

[0042] Specifically, the density of the polyvinyl chloride resin is 1.35~1.45g / cm 3 , the apparent density is 0.4~0.5 g / cm 3 .

[0043] Specifically, the polyvinyl chloride resin is a loose polyvinyl chloride resin with a particle size of 0.1-0.2 mm and is in the shape of cotton balls.

[0044] Specifically, the stabilizer includes 7 parts of tribasic lead sulfate and 1.5 parts of dibasic lead stearate. More specifically, it has excellent thermal stability, long-term performance, good electrical insulation and weather resista...

Embodiment 3

[0056]A PVC board, comprising by weight components: 50 parts of polyvinyl chloride resin, 0.3 parts of white oil, 2.8 parts of stabilizer, 2 parts of titanium dioxide, 0.28 parts of stearic acid, 0.2 parts of polyethylene wax, stearic acid amide 0.25 parts, 0.1 parts of UV absorber, 0.02 parts of coloring agent, 0.06 parts of fluorescent whitening agent OB, 15 parts of activated calcium carbonate, 15 parts of talcum powder, and 0.2 parts of foaming agent.

[0057] Specifically, the density of the polyvinyl chloride resin is 1.35~1.45g / cm 3 , the apparent density is 0.4~0.5 g / cm 3 .

[0058] Specifically, the polyvinyl chloride resin is a loose polyvinyl chloride resin with a particle size of 0.1-0.2 mm and is in the shape of cotton balls.

[0059] Specifically, the stabilizer includes 5 parts of tribasic lead sulfate and 1 part of dibasic lead stearate. More specifically, it has excellent thermal stability, long-term performance, good electrical insulation and weather resis...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a PVC board and a preparation process thereof. The PVC board is prepared from, by weight, 40-60 parts of polyvinyl chloride resin, 0.1-0.5 part of white oil, 2.5-3 parts of stabilizer, 1-3 parts of titanium dioxide, 0.1-0.5 part of stearic acid, 0.1-0.3 part of polyethylene wax, 0.01-0.5 part of octadecanamide, 0.01-0.2 part of ultraviolet absorbent, 0.01-0.03 part of colorant, 0.01-0.1 part of fluorescent whitening agent OB, 10-20 parts of activated calcium carbonate, 10-20 parts of talcum powder and 0.1-0.3 part of foaming agent. The PVC board is low in cost and good in heat stability, the rigidity is improved, the plastifying quality is improved, and the appearance is improved, so that section bars are smooth and good in weather resistance, toughness and uniformity.

Description

technical field [0001] The invention relates to the technical field of plate forming, in particular to a PVC plate and a preparation process thereof. Background technique [0002] Polyvinyl chloride, referred to as PVC in English, is a thermoplastic resin polymerized by polyethylene under the action of an initiator. The molecular weight of industrially produced PVC is generally in the range of 50,000 to 120,000. It has large dispersibility. The molecular weight increases with the decrease of polymerization temperature, but its stability to light and heat is poor. , it will be decomposed to produce hydrogen chloride, and further autocatalytic decomposition will cause discoloration, and the physical and mechanical properties will also decline rapidly. In practical applications, additives must be added to improve various performances. [0003] PVC plastic sheet is already a very popular new type of light-weight decorative material in the world today, and it is a popular produc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/06C08K13/02C08K3/22C08K5/09C08K5/20C08K3/26C08K3/34C08K5/098C08K3/30C08J9/10
CPCC08L27/06C08J9/103C08J2203/04C08J2327/06C08J2423/06C08K2003/2241C08K2003/265C08K2003/3045C08L2201/08C08L2205/03C08L23/06C08K13/02C08K3/22C08K5/09C08K5/20C08K3/26C08K3/34C08K5/098C08K3/30
Inventor 陈健杨文乾张建光
Owner SUZHOU FUTONG NEW MATERIALS & HIGH TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com