Robot-specific heat-resistant oil-resistant polyvinyl chloride cable sheathing material
A technology of oil-resistant polyvinyl chloride and cable sheath, which is applied in the field of cables, can solve the problems of limited application, poor heat resistance and oil resistance of polyvinyl chloride materials, and affect the service life of robots, etc., to achieve good compatibility, The effect of excellent elasticity and synergistic promotion of performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0017] A special heat-resistant and oil-resistant polyvinyl chloride cable sheath material for robots proposed by the present invention, its raw materials include by weight: 100 parts of polyvinyl chloride, 9 parts of thermoplastic polyurethane elastomer, 3 parts of nylon, 35 parts of nitrile rubber, chlorine 3 parts of chemicalized polypropylene, 8 parts of nano-calcium carbonate, 1 part of cobalt aluminate, 5 parts of hydrotalcite, 2 parts of magnesium hydroxide, 9 parts of red mud, 5 parts of graphene oxide, 5 parts of epoxy soybean oil, vinyl three parts 2 parts of (β-methoxyethoxy) silane, 2.9 parts of perfluoroalkyl ethyl acrylate, 2 parts of stabilizer, 3.5 parts of stearic acid, 0.3 part of dicumyl peroxide, and 5 parts of zinc oxide.
Embodiment 2
[0019] A special heat-resistant and oil-resistant polyvinyl chloride cable sheath material proposed by the present invention, its raw materials include by weight: 100 parts of polyvinyl chloride, 3 parts of thermoplastic polyurethane elastomer, 10 parts of nylon, 20 parts of nitrile rubber, chlorine 8 parts of polypropylene, 1 part of nano-calcium carbonate, 5 parts of cobalt aluminate, 2 parts of hydrotalcite, 10 parts of magnesium hydroxide, 2 parts of red mud, 12 parts of graphene oxide, 2 parts of epoxy soybean oil, vinyl three (β-methoxyethoxy) silane 3.8 parts, perfluoroalkyl ethyl acrylate 0.5 parts, stabilizer 5 parts, stearic acid 2 parts, dicumyl peroxide 1.5 parts, zinc oxide 2 parts.
Embodiment 3
[0021] A special heat-resistant and oil-resistant polyvinyl chloride cable sheath material proposed by the present invention, its raw materials include: 100 parts of polyvinyl chloride, 8 parts of thermoplastic polyurethane elastomer, 5 parts of nylon, 31 parts of nitrile rubber, chlorine 4 parts of chemicalized polypropylene, 6.5 parts of nano calcium carbonate, 2 parts of cobalt aluminate, 4.3 parts of hydrotalcite, 4 parts of magnesium hydroxide, 8 parts of red mud, 6 parts of graphene oxide, 4.2 parts of epoxy soybean oil, vinyl three (β-methoxyethoxy)silane 2.6 parts, perfluoroalkyl ethyl acrylate 2.7 parts, stabilizer 2.6 parts, stearic acid 3.2 parts, dicumyl peroxide 0.5 parts, zinc oxide 4.3 parts;
[0022] Wherein, the content of acrylonitrile in the described nitrile rubber is 15%;
[0023] The chlorine content of the chlorinated polypropylene is 38%;
[0024] The magnesium hydroxide is obtained by drying magnesium hydroxide slurry after hydrothermal reaction at 17...