A kind of preparation method of environmental protection building adhesive

A kind of adhesive and construction technology, applied in the direction of rosin adhesive, shellac adhesive, polymer adhesive additive, etc., can solve the problems of harmfulness to human body, non-environmental protection of materials, high formaldehyde content, etc., and achieve good environmental protection , Improve performance, less free formaldehyde

Active Publication Date: 2019-11-08
NANYANG INST OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a method for preparing an environmentally friendly construction adhesive with extremely low residual formaldehyde, so as to solve the problems in the above-mentioned background technology that the construction adhesive contains more formaldehyde, the material is not environmentally friendly, and is harmful to the human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of environmental protection building adhesive
  • A kind of preparation method of environmental protection building adhesive
  • A kind of preparation method of environmental protection building adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] An environmentally friendly construction adhesive, comprising the following raw materials in parts by weight: 80 parts of rosin glyceride, 25 parts of shellac, 172 parts of terpene resin, 24 parts of turpentine, 4 parts of aluminum silicate powder, 2 parts of white carbon black 5 parts of zirconium hydrogen phosphate, 1 part of tannin, 2 parts of potassium pyrophosphate, 6 parts of ethanol, 10 parts of hydroxyethyl cellulose, 5 parts of gum arabic, 3 parts of potassium lactate, 2 parts of sodium lactate, 1 part of sodium diacetate , 6 parts of silicon carbide whiskers and 5 parts of butyl lactate.

[0050] A kind of preparation method of environment-friendly building adhesive comprises the following steps:

[0051] 1) Pour 5 parts of gum arabic and 25 parts of shellac into a stirring pot, heat and stir under pressure, the heating temperature is 50°C, the stirring speed is 20r / min, the pressure is 50MPa, heat and stir The time is 20min, and viscous liquid is obtained, a...

Embodiment 2

[0055] An environmentally friendly construction adhesive, comprising the following raw materials in parts by weight: 97 parts of glycerin rosin, 32 parts of shellac, 186 parts of terpene resin, 57 parts of turpentine, 6 parts of aluminum silicate powder, 4 parts of white carbon black 7 parts of zirconium hydrogen phosphate, 3 parts of tannin, 4 parts of potassium pyrophosphate, 8 parts of ethanol, 12 parts of hydroxyethyl cellulose, 9 parts of gum arabic, 5 parts of potassium lactate, 4 parts of sodium lactate, 4 parts of sodium diacetate , 9 parts of silicon carbide whiskers and 8 parts of butyl lactate.

[0056] A kind of preparation method of environment-friendly building adhesive, comprises the following steps:

[0057] 1) Pour 9 parts of gum arabic and 32 parts of shellac into a stirring pot, and heat and stir under pressure. The heating temperature V1 is 60°C, the stirring speed R1 is 30r / min, and the pressure P1 is 70MPa , the heating and stirring time T1 is 30min, and...

Embodiment 3

[0064] An environmentally friendly construction adhesive, comprising the following raw materials in parts by weight: 90 parts of rosin glyceride, 28 parts of shellac, 180 parts of terpene resin, 35 parts of turpentine, 5 parts of aluminum silicate powder, 3 parts of white carbon black 6 parts of zirconium hydrogen phosphate, 2 parts of tannin, 3 parts of potassium pyrophosphate, 7 parts of ethanol, 11 parts of hydroxyethyl cellulose, 7 parts of gum arabic, 4 parts of potassium lactate, 3 parts of sodium lactate, 2 parts of sodium diacetate , 8 parts of silicon carbide whiskers and 7 parts of butyl lactate.

[0065] A kind of preparation method of environment-friendly building adhesive, comprises the following steps:

[0066] 1) Pour 7 parts of gum arabic and 28 parts of shellac into a stirring pot, and heat and stir under pressure. The heating temperature W1 is 55°C, the stirring speed R1 is 25r / min, and the pressure P1 is 60MPa , the heating and stirring time T1 is 25min, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of environmentally friendly building adhesive. The method comprises the steps that 1), gum acacia and shell lac are poured into an agitating pan, heating agitation processing is conducted under the condition of compression to obtain viscous liquid; 2), terpene resin, glycerol ester of rosin, turpentine, aluminium silicate powder, white carbon black andthe like are poured into an agitation tank to perform agitation processing to obtain a mixture; 3), emulsion obtained in step 2) is poured into the viscous liquid obtained in step 1), agitation is constantly performed until the material is cooled down to room temperature, ethanol is added, and emulsifying agitation processing is conducted to obtain the adhesive. According to the method, the residual formaldehyde content of the environmentally friendly building adhesive is extremely low, the health of human is not affected, which is beneficial to the protection of the environment.

Description

technical field [0001] The invention belongs to the technical field of environmental protection building adhesives, and in particular relates to a preparation method of environmental protection building adhesives. Background technique [0002] Construction adhesive is an essential material in construction engineering and has a wide range of applications. With the development of economy, synthetic construction adhesives are increasingly used in various fields. In the process of building decoration and decoration, it is mainly used for plate bonding, wall pretreatment, wallpaper pasting, ceramic wall and floor tiles, various floors, carpet laying and bonding, etc., increasing waterproofness, sealing, elasticity, and impact resistance. This can not only improve the quality of architectural decoration, increase the aesthetic comfort, but also improve the construction process, improve the efficiency and quality of building construction, etc. [0003] Among the currently used ad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J145/00C09J193/04C09J193/02C09J11/04C09J11/06C09J11/08
CPCC08K2003/321C08K2201/014C08L2201/08C08L2205/035C09J11/04C09J11/06C09J11/08C09J145/00C08L93/04C08L93/02C08L91/00C08L1/284C08L5/00C08K13/04C08K7/10C08K3/36C08K3/34C08K3/32C08K5/098
Inventor 褚卫瑞井珉刘蕊袁延玲
Owner NANYANG INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap