High-voltage-resistant insulating tape and preparation method thereof

An insulating tape, high-voltage-resistant technology, applied in the direction of adhesives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problem that the pressure resistance characteristics cannot meet the needs, achieve good weather resistance, and the preparation process is simple , The effect of material economy

Inactive Publication Date: 2018-07-20
JIANGSU YONGJIA ELECTRONICS MATERIALS
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing insulating tapes for electrical use can no longer meet the demand for their withstand voltage characteristics at higher voltages

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A preparation method for high-voltage insulating adhesive tape, comprising the following steps:

[0019] 1) Using polypropylene as raw material to prepare the base layer according to the conventional process;

[0020] 2) Prepare the adhesive layer: 15 parts of polyimide, 10 parts of polytetrafluoroethylene, 20 parts of polyvinyl chloride, 2 parts of acetate, 30 parts of styrene-butadiene rubber, 40 parts of vinyl polyurethane rubber, ethylene Add 20 parts of acrylic acid copolymer to the double-roller mixer for mixing, then add 8 parts of pigment carbon black, 5 parts of zinc sulfate, 10 parts of quartz powder, 1 part of anthracene oil, 3 parts of plasticizer, and 2 parts of antioxidant Glue in the glue machine to get the glue layer;

[0021] 3) Clean the bonding surface of the base layer with 37% isopropanol solution first, and then use a rubber brush to evenly coat the polyurethane adhesive on the bonding surface. After drying, apply the glue layer is attached to th...

Embodiment 2

[0024] A preparation method for high-voltage insulating adhesive tape, comprising the following steps:

[0025] 1) Using polypropylene as raw material to prepare the base layer according to the conventional process;

[0026] 2) Prepare the adhesive layer: 20 parts of polyimide, 12 parts of polytetrafluoroethylene, 25 parts of polyvinyl chloride, 5 parts of acetate, 35 parts of styrene-butadiene rubber, 45 parts of vinyl polyurethane rubber, ethylene Add 25 parts of acrylic acid copolymer into a double-roller mixer for mixing, then add 12 parts of pigment carbon black, 8 parts of zinc sulfate, 12 parts of quartz powder, 4 parts of anthracene oil, 7 parts of plasticizer, and 5 parts of antioxidant Glue in the glue machine to get the glue layer;

[0027] 3) Clean the bonding surface of the base layer with 37% isopropanol solution first, and then use a rubber brush to evenly coat the polyurethane adhesive on the bonding surface. After drying, apply the glue layer is attached to ...

Embodiment 3

[0030] A preparation method for high-voltage insulating adhesive tape, comprising the following steps:

[0031] 1) Using polypropylene as raw material to prepare the base layer according to the conventional process;

[0032] 2) Prepare the adhesive layer: 17 parts of polyimide, 11 parts of polytetrafluoroethylene, 23 parts of polyvinyl chloride, 3 parts of acetate, 32 parts of styrene-butadiene rubber, 42 parts of vinyl polyurethane rubber, ethylene Add 23 parts of acrylic acid copolymer to a double-roller mixer for mixing, then add 10 parts of pigment carbon black, 6 parts of zinc sulfate, 11 parts of quartz powder, 2 parts of anthracene oil, 5 parts of plasticizer, and 3 parts of antioxidant Glue in the glue machine to get the glue layer;

[0033] 3) Clean the bonding surface of the base layer with 37% isopropanol solution first, and then use a rubber brush to evenly coat the polyurethane adhesive on the bonding surface. After drying, apply the glue layer is attached to th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-voltage-resistant insulating tape. The tape is composed of a base layer and an adhesive layer. The adhesive layer is prepared from the following components by weight: 15-20 parts of polyimide, 10-12 parts of polytetrafluoroethylene, 20-25 parts of polyvinyl chloride, 2-5 parts of acetate, 30-35 parts of styrene-butadiene rubber, 40-45 parts of vinyl polyurethane rubber, 20-25 parts of an ethylene acrylic acid copolymer, 8-12 parts of pigment carbon black, 5-8 parts of zinc sulfate, 10-12 parts of quartz powder, 1-4 parts of anthracene oil, 3-7 parts of a plasticizer and 2-5 parts of an antioxidant. The invention has the advantages that the prepared insulating tape has high voltage resistance, good weather resistance and good flame retardancy, and is particularly applicable to high voltage conditions; the used raw materials are economical; the preparation method is simple in process and suitable for large-scale industrial production; and an isopropyl alcohol solution with a specific concentration is employed for cleaning the bonding surface of the base layer, so subsequent bonding process is more easily realized, a prepared composite layer is more compact, and the service life of the insulating tape is prolonged.

Description

technical field [0001] The invention belongs to the technical field of electrical protection materials, and in particular relates to a high-voltage-resistant insulating tape and a preparation method thereof. Background technique [0002] Insulating tape for electrical use refers to the tape used by electricians to prevent leakage and to insulate, also known as insulating tape and tape, consisting of a base layer and an adhesive layer. The base layer is generally made of cotton cloth, synthetic fiber fabric and plastic film, etc., and the adhesive layer is made of rubber plus tackifying resin and other compounding agents, with good viscosity and excellent insulation performance. Insulating tape has good insulation voltage resistance, weather resistance, flame retardant and other characteristics. It is suitable for wire connection and electrical insulation protection. [0003] However, with the sharp increase in electricity consumption, modern society has generally adopted ul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/30C09J7/24C09J175/14C09J109/06C09J123/08C09J127/06C09J11/04C09J11/06C09J11/08
CPCC08L2201/02C08L2205/035C09J11/04C09J11/06C09J11/08C09J175/14C09J2301/122C09J2423/106C08L9/06C08L23/0869C08L27/06C08L27/18C08K13/02C08K5/12C08K3/36C08K2003/3045C08K3/04
Inventor 陈学强
Owner JIANGSU YONGJIA ELECTRONICS MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com