Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Composite material for construction and preparation method thereof

A composite material and preparation technology, applied in the field of materials, can solve the problems of excessive bulk density, insufficient mechanical strength and poor thermal insulation effect of thermal insulation materials, and achieve the effect of remarkable energy saving effect, good strength, enhanced strength and durability of buildings

Active Publication Date: 2018-09-07
山东创伟外墙保温材料集团有限公司 +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the shortcomings of existing thermal insulation materials such as excessive bulk density, poor thermal insulation effect, insufficient mechanical strength and easy cracking, the present invention provides a thermal insulation material with light weight, low thermal conductivity, fire prevention, good mechanical properties, moisture resistance, sound insulation, mildew resistance and good durability. Composite materials for construction and their preparation technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite material for construction and preparation method thereof
  • Composite material for construction and preparation method thereof
  • Composite material for construction and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A composite material for construction, said material is made of the following components in parts by weight: 10 parts of fly ash, 1 part of calcium hydroxide, 5 parts of hemp fiber, 24 parts of fixed phase change material, chopped 5 parts of carbon fiber, 4 parts of modified starch, 13 parts of modified cellulose airgel, 1 part of modified layered dihydroxy compound hydrotalcite, and 21 parts of polyvinyl alcohol.

[0038] Further, the shape-setting phase-change material is a phase-change material fatty acid ternary eutectic, that is, LA (lauric acid)-PA (palmitic acid)-SA (fatty acid) is loaded in a mass ratio of 6:2:2 Expanded perlite and modified diatomaceous earth are on the base material with a mass ratio of 1:1; the mass content of LA (lauric acid)-PA (palmitic acid)-SA (fatty acid) in the shape-setting phase change material is 25 %.

[0039] Further, the length of the chopped carbon fiber is 0.5-1.5mm.

[0040] Further, the modified cellulose airgel is prepared...

Embodiment 2

[0053] A composite material for construction, said material is made of the following components in parts by weight: 12 parts of fly ash, 2 parts of calcium hydroxide, 8 parts of hemp fiber, 28 parts of fixed phase change material, chopped 7 parts of carbon fiber, 5 parts of modified starch, 15 parts of modified cellulose airgel, 2 parts of modified layered dihydroxy compound hydrotalcite, and 24 parts of polyvinyl alcohol.

[0054] Further, the shape-setting phase-change material is a phase-change material fatty acid ternary eutectic, that is, LA (lauric acid)-PA (palmitic acid)-SA (fatty acid) is loaded in a mass ratio of 6:2:2 Expanded perlite and modified diatomaceous earth are on the base material with a mass ratio of 1.2:1; the mass content of LA (lauric acid)-PA (palmitic acid)-SA (fatty acid) in the shape-setting phase change material is 40 %.

[0055] Further, the length of the chopped carbon fiber is 0.5-1.5 mm.

[0056] Further, the modified cellulose airgel is pre...

Embodiment 3

[0069] A composite material for construction, said material is made of the following components in parts by weight: 13 parts of fly ash, 3 parts of calcium hydroxide, 12 parts of hemp fiber, 33 parts of fixed phase change material, chopped 10 parts of carbon fiber, 7 parts of modified starch, 17 parts of modified cellulose airgel, 3 parts of modified layered dihydroxy composite hydrotalcite, and 33 parts of polyvinyl alcohol.

[0070] Further, the shape-setting phase-change material is a phase-change material fatty acid ternary eutectic, that is, LA (lauric acid)-PA (palmitic acid)-SA (fatty acid) is loaded in a mass ratio of 6:2:2 Expanded perlite and modified diatomaceous earth are on the base material with a mass ratio of 1.3:1; the mass content of LA (lauric acid)-PA (palmitic acid)-SA (fatty acid) in the shape-setting phase change material is less than or equal to 55%.

[0071] Further, the length of the chopped carbon fiber is 0.5-1.5mm.

[0072] Further, the modified ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite material for construction and a preparation method thereof. The composite material is prepared from, by weight, 10-15 parts of fly ash, 1-4 parts of calcium hydroxide, 5-16 parts of hemp fiber, 24-37 parts of form-stable phase change material, 5-12 parts of short carbon fiber, 4-8 parts of modified starch, 13-19 parts of modified cellulose aerogel, 1-3 parts ofmodified layered dihydroxy compound hydrotalcite and 21-38 parts of polyving akohol. The composite material has the excellent functions of heat preservation, fire proofing, sound insulation, moistureproofing, mildew proofing and shock absorption, the composite material is green and environmental-friendly, light in weight, good in mechanical performance and good in durability, and the problems ofexcessively heavy volume weight, poor heat preservation effect, toxicity and harm, easily becoming mildewed and incapable of insulating sound are solved.

Description

technical field [0001] The invention relates to the field of material technology, in particular to a composite material for construction and a preparation process thereof. Background technique [0002] With the rapid development of economy and society, people's requirements for living comfort are increasing, and the requirements for environmental protection, heat preservation and moisture resistance of building materials are also getting higher and higher. Existing thermal insulation materials have technical defects such as poor ratio of thermal insulation particles and adhesives, brittleness, high water absorption, excessive product bulk density, and easy cracking. These technical defects are closely related to frequent accidents of thermal insulation materials falling. The direct fall or collision of building insulation materials will cause great harm to pedestrians, vehicles, etc., and seriously threaten the lives and property safety of the people. In addition, summer an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/04
CPCC04B26/04C04B2111/00017C04B2201/20C04B2201/32C04B2201/50C04B18/08C04B22/064C04B18/248C04B24/085C04B14/185C04B14/08C04B14/386C04B24/383C04B14/36
Inventor 兰军亚
Owner 山东创伟外墙保温材料集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com