Preparation method of responsive polymeric ionic liquid hydrogel and swelling test thereof
A technology of polymerizing ionic liquids and ionic liquids, which is applied in the field of preparation of responsive polymeric ionic liquid hydrogels, can solve problems such as poor swelling, slow response, and single type, and achieve the effects of easy operation, increased water absorption rate, and increased surface area
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0040] Example 1: Preparation of ionic liquid
[0041] 1. Synthesis of 1-vinyl-3-ethylimidazole bromide (EVImBr): Weigh N-vinylimidazole into the reaction flask, N 2 Under protection, ethyl bromide was added dropwise to the reaction flask, and stirred at 70°C under reflux for 20 hours to obtain a white solid. The obtained white solid product was dissolved in acetonitrile to obtain a colorless transparent solution, which was slowly added dropwise to ethyl acetate for precipitation, filtered off with suction, and dried under vacuum at 60° C. for 12 hours to obtain a white solid. The synthetic route is as follows:
[0042]
[0043] 2. Synthesis of 1-vinyl-3-hydroxyethylimidazole chloride salt (HEVImCl): add N-vinylimidazole, chloroethanol and methanol into the flask and mix, reflux and stir for 96h under nitrogen protection at 60℃ to obtain dark brown viscous liquid. The obtained viscous liquid was diluted with methanol, precipitated in ethyl acetate, kept standing in the refrigerat...
Example Embodiment
[0049] Example 2: Responsive polymeric ionic liquid hydrogel 1
[0050] (1) Preparation
[0051] Accurately weigh 6.3633g (36.4mmol) of HEVImCl prepared in Example 1, and 0.0884g (0.6mmol) of N,N'-methylenebisacrylamide into a 100ml beaker, and add a mixed solvent of methanol and ethanol (where methanol, ethanol 10ml each) stir to mix the materials uniformly, add 0.1992g (1.2mmol) of azobisisobutyronitrile to it to dissolve it, transfer the mixed solution to a 25ml single-neck flask, pass N 2 After evacuating 6 times, the flask was transferred to a 70°C oil bath and heated for 10 hours. The obtained gel is immersed in an ethanol solution, the solution is changed every certain time until the solution is clear, the gel is immersed in ultrapure water, and the water is changed every certain time until the ethanol is completely removed. A part of the obtained gel was vacuum dried at 35°C, and the other part was freeze-dried for SEM test. The synthetic route is as follows:
[0052]
[0...
Example Embodiment
[0070] Example 3: Responsive polymeric ionic liquid hydrogel 2
[0071] (1) Preparation
[0072] Accurately weigh 6.3633g (36.4mmol) of HEVImCl prepared in Example 1, and 0.0884g (0.6mmol) of N,N'-methylenebisacrylamide into a 100ml beaker, and add a mixed solvent of methanol and ethanol (where methanol, ethanol 10ml each) stir to mix the materials uniformly, add 0.11195g (0.72mmol) of azobisisobutyronitrile to it to dissolve, transfer the mixed solution to a 25ml single-neck flask, pass N 2 After evacuating 6 times, the flask was transferred to a 70°C oil bath and heated for 10 hours. The obtained gel is immersed in an ethanol solution, the solution is changed every certain time until the solution is clear, the gel is immersed in ultrapure water, and the water is changed every certain time until the ethanol is completely removed. A part of the obtained gel was vacuum dried at 35°C, and the other part was freeze-dried for SEM test.
[0073] (2) Study on the swelling performance of ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap