Edge strip made of bisphenol A type polysulfone material and production method thereof

A technology of edge banding and material, which is applied in the field of edge banding made of bisphenol A polysulfone, can solve the problems of few types of edge banding and small choices, and achieve the effect of simple production method, easy operation and high efficiency

Active Publication Date: 2018-12-11
ZHEJIANG WELLSCOM PLASTIC CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the fact that there are relatively few types of existing furniture edge bands and less room for choice, the purpose of the present invention is to provide an edge band made of bisphenol A polysulfone, which fully utilizes the strength, toughness, and strength of bisphenol A polysulfone resin. Dimensional stability and chemical resistance and other properties to prepare edge banding made of bisphenol A polysulfone to meet market demand for edge banding types

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Edge strip made of bisphenol A type polysulfone material and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] An edge strip made of bisphenol A polysulfone is prepared from the following components: 80 g of bisphenol A polysulfone resin, 40 g of composite reinforcing resin, 20 g of hydroxyl-terminated dimethyl polysiloxane, 6 g of EVA emulsion, 6 g of cross-linking auxiliary Agent 1g, nano-silica 5g, ultraviolet absorber 2g, stearic acid 1g, antioxidant DNP 0.8g, silane coupling agent KH550 0.6g, chopped wood fiber 1g and chopped carbon fiber 0.6g, wherein: composite Reinforcing resin is a mixture of ABS resin, polycarbonate and polytetrafluoroethylene resin in a mass ratio of 2:1:0.6; the cross-linking assistant is component A, component B and component C in a mass ratio of 10 : 1:5 mixture, wherein component A is alkoxysilane, component B is dibutyltin dilaurate, component C is acrylic acid; the ultraviolet absorber is a mixture of nano titanium dioxide powder and methyl acrylate, and the two quality ratio of 5:1.

[0029] The production method of the above-mentioned polysul...

Embodiment 2

[0033] An edge strip made of bisphenol A polysulfone is prepared from the following components: 85 g of bisphenol A polysulfone resin, 45 g of composite reinforcing resin, 22.5 g of hydroxyl-terminated diethyl polysiloxane, 7 g of EVA emulsion, cross-linked Auxiliary agent 1.5g, nano silica 7g, UV absorber 2.25g, stearic acid 1.25g, antioxidant TNP 0.85g, silane coupling agent KH550 0.7g, chopped wood fiber 1.25g and chopped carbon fiber 0.65g g, wherein: the composite reinforcing resin is a mixture of ABS resin, polycarbonate and polytetrafluoroethylene resin in a mass ratio of 2.25:1:0.7; the cross-linking assistant is component A, component B and component C respectively The mixture is composed of 10.5:1:5.25 by mass ratio, wherein component A is acetoxysilane, component B is dibutyltin dilaurate, component C is acrylic acid; the ultraviolet absorber is nano-titanium dioxide powder and nano-di The mixture of zirconia powder and methyl acrylate, the mass ratio of the mixture...

Embodiment 3

[0038] An edge strip made of bisphenol A polysulfone is prepared from the following components: 90 g of bisphenol A polysulfone resin, 50 g of composite reinforcing resin, 25 g of hydroxyl-terminated vinyl dimethyl polysiloxane, 8 g of EVA emulsion, 2g of co-agent, 8g of nanodiatomite, 2.5g of ultraviolet absorber, 1.5g of myristic acid, 0.9g of antioxidant TPP, 0.8g of silane coupling agent KH560, 1.5g of tire powder and 0.7g of sorbitol, of which: The composite reinforced resin is a mixture of ABS resin, polycarbonate and polytetrafluoroethylene resin in a mass ratio of 2.5:1:0.8; the cross-linking aids are respectively component A, component B and component C in a mass ratio of A mixture of 11:1:5.5, wherein component A is ethyl orthosilicate, component B is stannous octoate, and component C is crotonic acid; the ultraviolet absorber is a mixture of nano-zirconia powder and methyl acrylate , the mass ratio of the two is 5.5:1.

[0039] The production method of the above-me...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of furniture edge strips and particularly relates to an edge strip made of bisphenol A type polysulfone material and a production method thereof. The edgestrip is prepared by mixing and extruded molding of the following ingredients at a certain weight ratio: bisphenol A type polysulfone resin, composite reinforced resin, hydroxy-contained organosilicon, EVA latex emulsion, a cross-linking adjuvant, a filling adjuvant, an ultraviolet absorbent, an internal lubricant, an antioxidant, a silane coupling agent, an anti-wear adjuvant and an antistatic agent, wherein the bisphenol A type polysulfone resin is adopted as a main raw material, and is doped with the composite reinforced resin containing polycarbonate, ABS resin and polytetrafluoroethylene,hydroxy-contained organosilicon and EVA latex emulsion so as to form a combined system under the effect of the cross-linking adjuvant, the filling adjuvant, the antistatic agent, the antioxidant, thesilane coupling agent, the ultraviolet absorbent, the anti-wear adjuvant and the like. The edge strip has relatively strong chemical resistance, heat resistance, temperature resistance, dimensional stability, ultra-violet resistance and the like, and the production method is simple and is capable of expanding the demand selection space of the market for edge strip types.

Description

technical field [0001] The invention relates to the technical field of furniture edge strips, in particular to an edge strip made of bisphenol A polysulfone and a production method thereof. Background technique [0002] The edge band is used to seal the section of the furniture board, so as to protect the section of the furniture from the damage to the board by the environment and unfavorable factors during use, such as moisture, and prevent the volatilization of formaldehyde inside the board, and at the same time achieve beautiful decoration. It can make the furniture show the overall effect of clear wood grain and colorful colors. The commonly used edge strips are: log edge strips, PVC edge strips, ABS edge strips and melamine edge strips. Among them, log edge strips are made of wood veneer, which is natural and free of chemical pollution. However, the demand for tree resources is large and the cost is high; PVC edge banding is made of polyvinyl chloride resin, which has ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L81/06C08L55/02C08L69/00C08L27/18C08L83/04C08L23/08
CPCC08L81/06C08L2201/08C08L2205/035C08L55/02C08L69/00C08L27/18C08L83/04C08L23/0853