Attapulgite finishing coating mortar and preparation method thereof

A technology of facing mortar and attapulgite, which is applied in the field of building materials, can solve the problems of changing decorative effects, unstable coloring, decorative mortar air permeability and loss of decorative style, etc., to improve the compressive strength and flexural strength, and solve the problems of Crack and micro-crack defects, maintain breathability and decorative style effect

Active Publication Date: 2018-12-28
安徽万博材料科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to poor measurement accuracy, it is difficult to stir evenly during mass production, and at the same time, due to uneven dispersion of toner and unstable coloring, the color difference of the decorative surface is serious.
In addition, the facing mortar also has defects such as pan-alkali and cracks.
These defects, especially chromatic aberration, have seriously affected its promotion and application
[0004] At present, when the decorative mortar is used to decorate the exterior wall of the building at home and abroad, the exterior wall primer and latex paint are painted on the surface. Because the latex paint can be accurately toned, the defect of color and color difference is solved, but this makes the construction of the decorative mortar Increased process, increased cost, changed decorative effect, and completely lost the original air permeability and decorative style of decorative mortar

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Attapulgite finishing coating mortar and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Preparation of modified epoxy resin:

[0036] (1) 15 parts of chitosan solids are dropped into the reactor, add the acetic acid solution of mass fraction 5%, make the chitosan acetic acid solution stand-by;

[0037] (2) Add 20 parts of epichlorohydrin to absolute ethanol, heat to reflux state, keep stirring for 10 minutes, then add 20 parts of trimethylolethane and 2 parts of benzoyl peroxide, and continue to reflux and stir for 1 hour; Then add the chitosan acetic acid solution and 1 part of sodium pyrophosphate in step 1, continue to reflux and stir for 2 hours, filter while it is hot, wash the precipitate with deionized water and absolute ethanol to remove impurities, and send it to a drying oven at 100-110°C for drying To constant weight, the modified epoxy resin is obtained.

[0038] Preparation of modified attapulgite: Add 0.3 parts of tripolyphosphoric acid and 0.3 parts of sodium silicate into 75 parts of deionized water, stir until completely dissolved, then a...

Embodiment 2

[0043] Preparation of modified epoxy resin:

[0044] (1) 15 parts of chitosan solids are dropped into the reactor, add the acetic acid solution of mass fraction 5%, make the chitosan acetic acid solution stand-by;

[0045] (2) Add 20 parts of epichlorohydrin to absolute ethanol, heat to reflux state, keep stirring for 10 minutes, then add 20 parts of trimethylolethane and 2 parts of benzoyl peroxide, and continue to reflux and stir for 1 hour; Then add the chitosan acetic acid solution and 1 part of sodium pyrophosphate in step 1, continue to reflux and stir for 2 hours, filter while it is hot, wash the precipitate with deionized water and absolute ethanol to remove impurities, and send it to a drying oven at 100-110°C for drying To constant weight, the modified epoxy resin is obtained.

[0046]Preparation of modified attapulgite: Add 0.3 parts of tripolyphosphoric acid and 0.3 parts of sodium silicate into 75 parts of deionized water, stir until completely dissolved, then ad...

Embodiment 3

[0064] Based on Example 1, a comparative example 1 without modifying the epoxy resin and a comparative example 2 without modifying the attapulgite were set.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses attapulgite finishing coating mortar and a preparation method thereof and relates to the technical field of building materials. The finishing coating mortar is prepared from acomponent A and a component B; during use, the component A and the component B are mixed according to the ratio; the component A is prepared from the following raw materials: modified epoxy resin, 42.5 white Portland cement, a quartz sand mixture, heavy calcium carbonate powder and nanometer aluminum oxide; and the component B is prepared from the following raw materials: modified attapulgite, alkali resistant acrylic emulsion, texanol, color paste and natural vegetable oil. According to the preparation method disclosed by the invention, by carrying out modifying treatment on the epoxy resin and the attapulgite, weather fastness and compressive strength of the finishing coating mortar are enhanced; and the preparation method has the advantages of low cost, simple process, no pollution andsuitability for industrial production.

Description

Technical field: [0001] The invention relates to the technical field of building materials, in particular to an attapulgite decorative mortar and a preparation method thereof. Background technique: [0002] Mortar is a commonly used building material, generally used in masonry and plastering works. Mortar is made by mixing cementitious materials (cement, lime, clay, etc.) and fine aggregate (sand) with water. According to the composition materials, it can be divided into: ①lime mortar: made of lime paste, sand and water according to a certain ratio, generally used for masonry and plastering layers that do not require high strength and are not subject to moisture; ②cement mortar: made of Cement, sand and water are made according to a certain ratio, and are generally used for masonry, walls or floors in wet environments or in water; ③Mixed mortar: Add appropriate admixtures such as fly ash, It is made of diatomite to save the amount of cement or lime and improve the workabil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B20/02C08G59/14C08G59/04C04B111/20
CPCC04B20/023C04B28/04C04B2111/00508C04B2111/2023C04B2201/50C08G59/04C08G59/14C04B14/06C04B14/28C04B14/303C04B14/102C04B24/26C04B24/06C04B2103/54C04B24/08C04B40/0028C04B14/08
Inventor 刘允超
Owner 安徽万博材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com