Production method of nickel-iron-phosphorus amorphous alloy catalytic reactor

A catalytic reactor, amorphous alloy technology, used in chemical instruments and methods, chemical/physical processes, metal material coating processes, etc. The effect of improving utilization efficiency

Inactive Publication Date: 2019-01-04
罗奕兵
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The idea of ​​the liquid phase method is to melt the master alloy uniformly first, and then adopt the method of purification and rapid cooling to rapidly cool the alloy liquid in a short period of time. The main advantages of this type of method are that the preparation is simple and the cycle is short. The size is largely limited by the ability of the alloy to form amorphous

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of nickel-iron-phosphorus amorphous alloy catalytic reactor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Embodiment 1: the production technology of nickel-iron-phosphorus amorphous alloy catalytic reactor

[0032] (1) Surface treatment of fibers: using φ 0.04 mm polypropylene fiber, chemical degreasing and degreasing with sodium hydroxide solution;

[0033] (2) Coarsening of polypropylene fibers, the proportion of the coarsening aqueous solution is 80g / L chromic anhydride, 300ml / L sulfuric acid, the roughening treatment temperature is 60°C, and the roughening treatment time is 20min;

[0034] (3) For fiber sensitization, the composition of the sensitization solution is 8g / L tin chloride, 40ml / L hydrochloric acid, and the sensitization treatment time is 3min;

[0035] (4) Silver nitrate and ammonia solution are used to activate the fiber surface, and the activated fiber is reduced by formaldehyde solution;

[0036] (5) Electroless plating of treated fibers, the solution composition is: nickel chloride 0.45mol / L, tartaric acid 0.3mol / L, sodium hypophosphite 0.2mol / L, pota...

Embodiment 2

[0042] Embodiment 2: the production method of nickel-iron-phosphorus amorphous alloy catalytic reactor

[0043] (1) Surface treatment of fibers: using 0.02×1 mm polypropylene thin strip, chemically degreased and degreased with sodium hydroxide solution;

[0044] (2) The ratio of the roughened aqueous solution of the polypropylene thin strip is 65g / L chromic anhydride, 250ml / L sulfuric acid, the roughening treatment temperature is 60°C, and the roughening treatment time is 30min;

[0045] (3) For fiber sensitization, the composition of the sensitization solution is tin chloride 6.5g / L, hydrochloric acid 30ml / L, and the sensitization treatment time is 2min;

[0046] (4) Silver nitrate and ammonia solution are used to activate the fiber surface, and the activated fiber is reduced by formaldehyde solution;

[0047] (5) Electroless plating of treated fibers, the solution composition is: nickel sulfate 0.4mol / L, ferrous sulfate 0.08mol / L, tartaric acid 0.35mol / L, sodium hypophosph...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
areaaaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a nickel-iron-phosphorus amorphous alloy composite fiber. The length of the composite fiber can be continuous, the cross section of the composite fiber can be circular, special-shaped and the like, the external diameter of the composite fiber is 0.01-0.2 millimeter, and the diameter of core yarn of the composite fiber is 0.005-0.08 millimeter; a coating layer of the composite fiber is nickel-iron-phosphorus amorphous alloy, the nickel-iron-phosphorus amorphous alloy is prepared from 40-85% of nickel, 10-20% of ferrum and 6-20% of phosphorus, and the core yarn of the composite fiber is made from a polymer. A preparation method of the composite fiber comprises the steps that (1) a polymer fiber is degreased; (2) the fiber surface is coarsened; (3) the fiber is sensitized; (4) the fiber surface is activated; (5) chemical nickel-iron-phosphorus plating is carried out on the fiber; (6) the nickel-iron-phosphorus amorphous alloy is plated on a fiber electric brush.

Description

technical field [0001] The invention relates to the field of catalyst production, in particular to a nickel-iron-phosphorus amorphous alloy catalytic reactor and a preparation method. Background technique [0002] Amorphous alloys have the following characteristics: ①Amorphous alloys can be made into samples of various compositions in a wide range, so that their electronic properties can be adjusted in a wide range; ②The catalytic active center can be a single The form is evenly distributed in a chemically uniform environment; ③The surface of the amorphous alloy has a high concentration of unsaturated centers, and the coordination number of the unsaturated centers has a certain range, so its catalytic activity and selectivity are generally better than those of the corresponding 4. The non-porosity of its surface is that it gets rid of the problem that the diffusion of reactive species in the presence of multiple catalysts affects the surface reaction. [0003] Amorphous all...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J19/00C22C45/04C23C28/02C23C18/50C25D3/56C25D5/06
CPCB01J19/00C22C45/04C23C18/50C23C28/021C25D3/562C25D5/06
Inventor 罗奕兵
Owner 罗奕兵
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products