Anti-yellowing antibacterial polypropylene plastic for automobile decorations

An antibacterial polypropylene and anti-yellowing technology, applied in the field of plastics, can solve the problems of insufficient mechanical properties, yellowing, mildew, etc., and achieve the effect of low hydrophilic and lipophilic balance, slowing down the aging speed, and good weather resistance.

Inactive Publication Date: 2019-01-11
何亚龙
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current automotive interior parts usually use plastic materials, which have insufficient mechanical properties, are not wear-resistant, are easy to age, are easy to mold, and are prone to yellowing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-yellowing antibacterial polypropylene plastic for automobile decorations

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] An anti-yellowing and antibacterial polypropylene plastic for automobile accessories, comprising the following raw materials in parts by weight: 100 parts of polypropylene, 30 parts of polystyrene, 15 parts of nitrile rubber, 20 parts of nano-calcium carbonate, 2 parts of titanium dioxide, and shell powder 8 parts, 1.5 parts of octaphenyl clathrate silsesquioxane, 2 parts of polyoxyethylene stearate, 1 part of compound antibacterial agent, 1.5 parts of coupling agent, 1 part of methyl tributylketoxime silane crosslinking agent , 1.5 parts of 1010 anti-aging agent, 1.5 parts of plasticizer, 1 part of stabilizer and 2 parts of processing aid.

[0028] The composite antibacterial agent is composed of lanthanum oxide and nanometer silver oxide with a mass ratio of 1:2.

[0029] The coupling agent is composed of sodium lignosulfonate and glycidyltriethoxysilane with a mass ratio of 1.5:1.

[0030] The plasticizer is composed of rapeseed fatty acid alkanolamide borate and ca...

Embodiment 2

[0038] An anti-yellowing and antibacterial polypropylene plastic for automobile accessories, comprising the following raw materials in parts by weight: 100 parts of polypropylene, 25 parts of polystyrene, 20 parts of nitrile rubber, 15 parts of nano-calcium carbonate, 4 parts of titanium dioxide, and shell powder 10 parts, 2.5 parts of octaphenyl clathrate silsesquioxane, 1 part of polyoxyethylene stearate, 1.5 parts of compound antibacterial agent, 2 parts of coupling agent, 1.5 parts of vinyl tributylketoxime silane crosslinking agent , 0.5 parts of 1076 anti-aging agent, 2 parts of plasticizer, 1.5 parts of stabilizer and 3 parts of processing aid.

[0039] The composite antibacterial agent is composed of lanthanum oxide and nanometer silver oxide with a mass ratio of 1:3.

[0040] The coupling agent is composed of sodium lignosulfonate and glycidyltriethoxysilane with a mass ratio of 1:1.

[0041] The plasticizer is composed of rapeseed fatty acid alkanolamide borate and ...

Embodiment 3

[0049]An anti-yellowing and antibacterial polypropylene plastic for automotive accessories, comprising the following raw materials in parts by weight: 100 parts of polypropylene, 20 parts of polystyrene, 15 parts of nitrile rubber, 20 parts of nano-calcium carbonate, 3 parts of titanium dioxide, and shell powder 7 parts, 3 parts of octaphenyl clathrate silsesquioxane, 1.5 parts of polyoxyethylene stearate, 0.5 parts of compound antibacterial agent, 1 part of coupling agent, 2 parts of dimethyldibutylketoxime silane crosslinking agent 1 part, 1 part of 1010 anti-aging agent, 1 part of plasticizer, 2 parts of stabilizer and 2 parts of processing aid.

[0050] The composite antibacterial agent is composed of lanthanum oxide and nanometer silver oxide with a mass ratio of 1:2.

[0051] The coupling agent is composed of sodium lignosulfonate and glycidyltriethoxysilane with a mass ratio of 1:1.

[0052] The plasticizer is composed of rapeseed fatty acid alkanolamide borate and cas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-yellowing antibacterial polypropylene plastic for automobile decorations. The plastic contains the following raw materials in parts by weight: 100 parts of polypropylene, 20-40 parts of polystyrene, 10-20 parts of nitrile rubber, 15-25 parts of nanometer calcium carbonate, 1-5 parts of titanium dioxide, 5-10 parts of shell powder, 1-3 parts of octaphenyl cage-like silsesquioxane, 1-3 parts of polyoxyethylene stearate, 0.5-1.5 parts of composite antibacterial agent, 1-3 parts of coupling agent, 0.5-2 parts of crosslinking agent, 0.5-2 parts of anti-aging agent, 0.5-2 parts of plasticizer, 1-2 parts of stabilizer and 1-3 parts of processing aid. The polypropylene plastic disclosed by the invention has the advantages of high strength, high impact resistance, good antibacterial effect, good heat resistance, good weather resistance, aging resistance, yellowing resistance and the like and can be processed into various automobile interior parts.

Description

technical field [0001] The invention belongs to the technical field of plastics, in particular to a yellowing-resistant and antibacterial polypropylene plastic for automobile accessories. Background technique [0002] PP, also known as polypropylene, is a semi-crystalline material. It is harder and has a higher melting point than polyethylene (PE) plastic. PP resins have excellent moisture absorption resistance, acid and alkali corrosion resistance, and solubility resistance. Because plastic has the advantages of light weight, no rust, and good insulation, it is one of the fastest-growing varieties of general-purpose thermoplastics. PP resin has certain special requirements in the fields of chemical industry, building materials, home appliances, automobiles, etc., but because PP has large spherulites, grain boundary defects and cracks are prone to appear at the spherulite interface, causing embrittlement. PP has the disadvantages of low modulus, low impact strength, and p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L25/06C08L9/02C08L83/04C08L71/02C08L97/00C08L51/06C08K13/02C08K3/26C08K3/22C08K5/5435
CPCC08K2003/0806C08K2003/221C08K2003/265C08K2201/011C08K2201/014C08L23/12C08L2201/08C08L2205/025C08L2205/035C08L25/06C08L9/02C08L83/04C08L71/02C08L97/00C08L51/06C08K13/02C08K3/26C08K3/22C08K5/5435
Inventor 何亚龙
Owner 何亚龙
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com