Method for preparing lubricating oil through graphene and nano zinc borate whisker modified vegetable oil
A technology of nano-zinc borate and modified vegetable oil, which is applied in the field of lubricating oil, can solve the problems of restricting popularization and application, lack of a large number of basic tests on the anti-friction and anti-wear effects of internal combustion engines, etc., and achieve good dispersion stability, excellent anti-wear and anti-friction effects, Good anti-friction and anti-wear properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0028] Example 1
[0029] A method for preparing lubricating oil using graphene-nano zinc borate whisker modified vegetable oil, which is characterized in that it comprises the following steps:
[0030] (1) Graphene modified by oleic acid and stearic acid:
[0031] Disperse 0.2 part of nano graphene ultrasonically for 20min, stir quickly in a water bath at 80-85℃, add dropwise oleic acid-stearic acid modifier, reflux for 4h, aging, rinse with mineral spirits, ultrasound, centrifugation, and filter several times After separation, dry in a 60-65°C drying oven, and grind to obtain oleic acid-stearic acid combined modified nano-graphene;
[0032] (2) Modified nano zinc borate whiskers:
[0033] Add 0.5 part of surfactant trioctyl phosphate to 25 parts of sodium tetraborate decahydrate solution, ultrasonic for 30min, add 5 parts of zinc nitrate hexahydrate solution under stirring, react at 70-75℃ for 20min, add sodium hydroxide solution for adjustment pH is 8, continue constant temperature...
Example Embodiment
[0043] Example 2
[0044] A method for preparing lubricating oil using graphene-nano zinc borate whisker modified vegetable oil, which is characterized in that it comprises the following steps:
[0045] (1) Graphene modified by oleic acid and stearic acid:
[0046] Disperse 0.3 part of nano graphene ultrasonically for 30min, stir quickly in a water bath at 80-85℃, add dropwise oleic acid-stearic acid modifier, reflux for 5h, aging, rinse with mineral spirits, ultrasound, centrifugation, and filter several times After separation, dry in a 60-65°C drying oven, and grind to obtain oleic acid-stearic acid combined modified nano-graphene;
[0047] (2) Modified nano zinc borate whiskers:
[0048] Add 1 part of surfactant trioctyl phosphate to 50 parts of sodium tetraborate decahydrate solution, ultrasonic for 40min, add 10 parts of zinc nitrate hexahydrate solution under stirring, react at 70-75℃ for 30min, add sodium hydroxide solution for adjustment pH is 8, continue constant temperature ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap