A kind of graphene oxide-cerium hydroxide composite material, preparation method and application thereof

A high-hydroxide, composite material technology, applied in chemical instruments and methods, other chemical processes, water/sludge/sewage treatment, etc., can solve the problem of low adsorption effect, achieve significant effect and high reproducibility of experimental results , the adsorption effect is remarkable

Active Publication Date: 2021-12-14
MINNAN NORMAL UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] The invention provides a graphene oxide-cerium hydroxide composite material, a preparation method and its application to solve practical technical problems such as low adsorption effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of graphene oxide-cerium hydroxide composite material, preparation method and application thereof
  • A kind of graphene oxide-cerium hydroxide composite material, preparation method and application thereof
  • A kind of graphene oxide-cerium hydroxide composite material, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0044] 1. Experimental part

[0045] 1. Main raw materials and instruments

[0046] The test materials provided by the implementation of the present invention are: graphene oxide (GO) (AA, Suzhou Carbon Abundance Technology Co., Ltd.), cerium nitrate (Ce(NO 3 ) 3 ) (AR, Sinopharm Chemical Reagent Co., Ltd.), sodium hydroxide (NaOH) (AR, Guangdong. Shantou Xilong Chemical Factory), hydrochloric acid (HCl) (AR, Xilong Science Co., Ltd.), ethanol (C 2 h 5 OH) (AR, Xilong Science Co., Ltd.), ammonium molybdate tetrahydrate ((NH 4 Mo 7 o 24 .4H 2 O) (AR, Xilong Science Co., Ltd.), potassium dihydrogen phosphate (KH 2 PO 4 ) (AR, Xilong Science Co., Ltd.), L(+)—ascorbic acid (C 6 h 8 o 6 ) (AR, Xilong Science Co., Ltd.), Congo red (C 32 h 22 N 6 Na 2 o 6 S 2 ) (AR, Xilong Science Co., Ltd.).

[0047] The instrument provided by the implementation of the present invention is: scanning electron microscope (SEM), X-ray diffraction spectrometer (XRD), HH-4 digital display...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
melting pointaaaaaaaaaa
adsorption capacityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a graphene oxide-cerium hydroxide composite material, a preparation method and an application thereof. In this experiment, graphene oxide-ceric hydroxide composites (Ce(OH) 4 / GO) to adsorb and remove Congo red (CR) and phosphate ion (PO) in the solution 4 3‑ ), and the structure of the composite material was characterized by SEM, FT-IR, etc., and the Congo red (CR) and phosphate ion (PO 4 3‑ ) adsorption effect was discussed, and the optimal adsorption conditions were determined as follows: pH 7.0 and 6.0, adsorption time 6 hours, temperature 50°C and 30°C. Congo red and PO were obtained by Langmuir model analysis 4 3‑ The maximum adsorption capacity is 563.67mg / g, 619.63mg / g respectively, and the adsorption effect is remarkable.

Description

【Technical field】 [0001] The invention belongs to the technical field of preparation of water treatment agents, and in particular relates to a graphene oxide-cerium hydroxide composite material, a preparation method and an application thereof. 【Background technique】 [0002] There are many wastewater treatment technologies, such as: flocculation, membrane filtration, solvent extraction, biosorption, chemical precipitation, ion exchange, reverse osmosis, electrocoagulation, sintering, electrolytic precipitation, coagulation and adsorption, etc. Among them, the adsorption method has become a widely used method for removing pollutants due to its advantages of cheap production and simple operation and treatment process. It is very important to design new adsorbents with excellent adsorption capacity. [0003] There are many kinds of adsorbents, which can be mainly divided into three categories: [0004] The first category is more common porous adsorption materials, such as acti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/20B01J20/30C02F1/28C02F101/30C02F101/10
CPCB01J20/06B01J20/20C02F1/288C02F2101/105C02F2101/308
Inventor 闫海刚黄鸿淮蔡舒雅魏诗佳詹峰萍
Owner MINNAN NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap