Anti-aging dazzling thermal insulation type real stone imitation brick coating and manufacturing method thereof

A manufacturing method and anti-aging technology, applied in anti-corrosion coatings, rosin coatings, chitin polysaccharide coatings, etc., can solve the problems of affecting the thermal insulation system and the base surface, low hardness, poor bonding force, etc., and achieve good decorative effect and reflective ratio. High, good lubricity effect

Inactive Publication Date: 2019-04-16
QINGDAO TIANDICAI PAINT
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the limitation is that when using conventional imitation brick paint on the surface of high-rise buildings, first of all, this paint is not real stone, but a mortar resin paint, so it has the disadvantages of low hardness and poor weather resistance, and the cost is relatively higher. Real stone paint is just the opposite. It has poor adhesion to the wall and is not acid-resistant (mainly carbonated salts).
[0006] In the prior art, although there are many types of such coatings, since there is no related technology that combines the hardness and weather resistance of "real stone" and the bonding force and corrosion resistance of "imitation brick", not only the color effect is difficult to guarantee, What's more, it may cause surface differentiation, cracking, etc., which will affect the insulation system and base surface, and cause damage to the main body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] An anti-aging glare heat preservation type real stone imitation brick paint. The components of the imitation brick paint are composed of three functional components and deionized water accounting for 35% of the total weight of the paint. The first functional component A is a graft copolymer of acrylic acid, acrylonitrile and styrene prepared from 30Kg of acrylic resin, 20Kg of acrylonitrile and 20Kg of styrene, modified by 10Kg of pentaerythritol rosin ester; the second functional component B is the particle size 35Kg of pyroxene granite powder with a particle size of 0.1mm-0.2mm and 25Kg of marble powder with a particle size of 0.1mm-0.2mm; the third functional component C is 8Kg of chitin and 3Kg of titanium dioxide powder; the composition relationship of the three components is: C and component B are dispersed in the colloidal molecular cluster of component A in the form of solid powder or turbid in deionized water.

[0027] The manufacturing method of the above-ment...

Embodiment 2

[0043] The whole is consistent with Example 1, the difference is:

[0044] An anti-aging glare heat preservation type real stone imitation brick paint. The components of the imitation brick paint are composed of three functional components and deionized water accounting for 30% of the total weight of the paint. The first functional component A is a graft copolymer of acrylic acid, acrylonitrile and styrene prepared from 35Kg of acrylic resin, 15Kg of acrylonitrile and 15Kg of styrene, modified by 8Kg of pentaerythritol rosin ester; the second functional component B is the particle size 30Kg of pyroxene granite powder with a particle size of 0.1mm-0.2mm and 20Kg of marble powder with a particle size of 0.1mm-0.2mm; the third functional component C is 6Kg of chitin and 2Kg of titanium dioxide powder; the composition relationship of the three components is: C and component B are dispersed in the colloidal molecular group of component A in the form of solid powder or turbid in dei...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an anti-aging dazzling thermal insulation type real stone imitation brick coating and a manufacturing method thereof. The imitation brick coating consists of three functional compositions and deionized water accounting for 30-35% of the total weight of the coating, wherein the first functional composition A is a grafted copolymer which is modified by pentaerythritol rosin ester and prepared from acrylic acid, acrylonitrile and styrene; the second functional composition B is composed of granite powder and marble powder; the third functional composition C is composed of chitin and titanium dioxide powder. According to the composition relationship of the three compositions, the composition C and the composition B are dispersed in a micelle molecular group of the composition A in a form of solid powder or are turbid in deionized water. The imitation brick coating has the advantages of being environmentally friendly, free of pollutants, resistant to water and acid corrosion, antibacterial, high in binding force and long in service life.

Description

technical field [0001] The invention relates to the field of environmental protection coatings, in particular to an anti-aging glare heat preservation type real stone imitation brick coating and a manufacturing method thereof. Background technique [0002] Real stone paint is a kind of paint whose decorative effect is similar to marble and pyroxene granite. It is mainly made of natural stone powder of various colors, and it is applied to the imitation stone effect of building exterior walls, so it is also called liquid stone. [0003] Imitation brick paint is similar to imitation pyroxene granite and marble paint (such as real stone paint and water-in-water paint). Imitation brick paint is a kind of paint that imitates the color and texture of bricks. At present, from the perspective of economy, ease of construction and product safety, mainstream manufacturers use textured mortar products to achieve this effect. [0004] Due to the standardization of the Chinese constructi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D151/00C09D105/08C09D193/04C09D5/08C09D5/14C09D7/61C09D7/65C08F265/04C08F220/44C08F212/08
CPCC08F265/04C08K2003/2241C08K2003/265C09D5/08C09D5/14C09D7/61C09D7/65C09D151/003C08F220/44C08F212/08C08L5/08C08L93/04C08K3/22C08K3/36C08K3/26
Inventor 刘英武刘丰毓
Owner QINGDAO TIANDICAI PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products