Method for molding automobile transmission gearbox gear stand through powder metallurgy

A technology of gear bracket and powder metallurgy, which is applied in the field of auto parts manufacturing, can solve the problems that the parts are difficult to meet the requirements, and achieve the effect of good hardness, uniform overall density, and improved quality and performance

Inactive Publication Date: 2019-05-07
益阳市再超粉末冶金有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the development of industry, the requirements for parts are getting higher and higher. Due to the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0023] Example 1

[0024] A method for forming a gear bracket of an automobile gearbox made by powder metallurgy includes the following steps:

[0025] S1. Mixing of raw materials: weigh 120 parts of iron powder, 2.0 parts of graphene, 2.0 parts of nickel powder, 2.0 parts of manganese powder, 0.8 parts of lubricant, 0.2 parts of silane coupling agent, 4 parts of copper powder, 1.0 part of chromium powder, zinc 1.5 parts of powder, 0.15 parts of silicon dioxide, 2 parts of tungsten carbide, and 1.0 part of titanium powder are added to a high-speed ball mill for grinding and mixing to obtain a uniformly mixed mixture;

[0026] S2. Pressing: Infiltrate the inner wall of the pressing mold with a powder metallurgy release agent, and then add the mixture obtained from S1 to the pressing mold for pressing to form a rough part of the automobile gearbox gear bracket; the pressing pressure is 500-550MPa , The pressed density of the blank is 6.8-7.3g / cm 3 ;

[0027] S3. Drying: Place the blank...

Example Embodiment

[0034] Example 2

[0035] A method for forming a gear bracket of an automobile gearbox made by powder metallurgy includes the following steps:

[0036] S1. Mixing of raw materials: weigh 100 parts of iron powder, 1.0 part of graphene, 1.0 part of nickel powder, 1.0 part of manganese powder, 0.6 part of lubricant, 0.1 part of silane coupling agent, 3 parts of copper powder, 0.5 part of chromium powder, zinc Add 1.0 part of powder, 0.1 part of silicon dioxide, 1 part of tungsten carbide, and 0.5 part of titanium powder to a high-speed ball mill for grinding and mixing to obtain a uniformly mixed mixture;

[0037] S2. Pressing: Infiltrate the inner wall of the pressing mold with a powder metallurgy release agent, and then add the mixture obtained from S1 to the pressing mold for pressing to form a rough part of the automobile gearbox gear bracket; the pressing pressure is 500-550MPa , The pressed density of the blank is 6.8-7.3g / cm 3 ;

[0038] S3. Drying: Place the blanks of the automo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Rockwell hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for molding an automobile transmission gearbox gear stand through powder metallurgy. The method comprises the steps of raw material mixing, pressing, drying, sintering, quenching, tempering, finishing, rust prevention and the like. Raw materials comprise, by weight part, 100-120 parts of iron powder, 1.0-2.0 parts of graphene, 1.0-2.0 parts of nickel powder, 1.0-2.0 parts of manganese powder, 0.5-0.6 part of a lubricating agent, 0.1-0.2 part of a silane coupling agent, 3-4 parts of copper powder, 0.5-1.0 part of chromium powder, 1.0-1.5 parts of zinc powder, 0.1-0.15 part of silicon dioxide, 1-2 parts of tungsten carbide and 0.5-1.0 part of titanium powder. According to the method, the raw material formula is reasonable, the process is simple, and the production efficiency is high. The automobile transmission gearbox gear stand prepared through the method has the beneficial effects of uniform in overall density, good in strength and hardness, good in rust prevention performance and the like.

Description

technical field [0001] The invention relates to the field of auto parts manufacturing, in particular to a powder metallurgy forming method for a gear bracket of an automobile transmission gearbox. Background technique [0002] With the development of industry, the requirements for parts are getting higher and higher. Due to the influence of cost, delivery cycle and noise, it is often difficult for machined parts to meet the requirements. Powder metallurgy is a technology that can manufacture parts with complex shapes. It has the characteristics of saving raw materials, energy and labor, and is suitable for mass production. Because the gear bracket manufactured by powder metallurgy has higher porosity than the cast gear bracket, the strength, hardness, and overall density uniformity of the gear bracket are affected to a certain extent. Contents of the invention [0003] The object of the present invention is to provide a kind of molding method of powder metallurgy manufact...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/02C22C38/04C22C38/42C22C38/44C22C38/50C22C38/58C22C33/02C21D1/18C21D9/00B22F3/02B22F3/10B22F3/24
Inventor 李建峰钟训华钟智超符人慧
Owner 益阳市再超粉末冶金有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap