Glass laminating glue

A technology of glass clips and microspheres, applied in the direction of layered products, adhesive types, adhesive additives, etc., can solve the problems of limiting the application of laminated glass, poor flame retardant effect, poor heat insulation performance, etc., to maintain lighting and aesthetic requirements, improved light reflectivity, and excellent high temperature resistance

Inactive Publication Date: 2019-07-05
天津市凯辉玻璃制品有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

PVB glass laminate has poor heat insulation performance and poor flame retardant effect, which limits the application of laminated glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0018] The embodiment of the present invention also provides the preparation method of the above-mentioned glass interlayer, which comprises the following steps:

[0019] S1, disperse the silica microspheres and the zirconia microspheres in the first solvent, add the phytic acid and the first mass part of the polymethyl methacrylate in sequence, after mixing, remove The first solvent to obtain the first mixture;

[0020] S2, dispersing the modified LDHs in a second solvent, adding the polyurethane resin, raising the temperature to 120-150° C. and stirring for 2-3 hours, and then ultrasonically treating for 30-50 minutes to obtain a second mixture;

[0021] S3, melt blending the first mixture, the second mixture, the second mass part of the polymethyl methacrylate and the rare earth oxide to obtain the glass interlayer.

[0022] In the above preparation method, the silica microspheres and zirconia microspheres are first mixed with a part of polymethyl methacrylate through a so...

Embodiment 1

[0037] A glass interlayer provided in this embodiment is prepared according to the following steps:

[0038](1) Preparation of modified LDHs: Weigh 0.18 mol of magnesium chloride, 0.08 mol of aluminum chloride and 0.285 mol of urea and dissolve them in deionized water, then sonicate for 30 min, add 0.1 mol of melamine phosphate solution dropwise, and transfer to and then placed in a muffle furnace at 90°C to react for 18 hours. After the reaction, filter and wash to obtain the modified LDHs powder.

[0039] (2) Disperse 7 parts of silicon dioxide microspheres and 7 parts of zirconium dioxide microspheres in tetrahydrofuran, add 4 parts of phytic acid and 20 parts of polymethyl methacrylate in turn, and mix them at 60°C The tetrahydrofuran was removed by drying under low temperature to obtain the first mixture.

[0040] (3) Disperse 15 parts of modified LDHs in dimethyl sulfoxide, add 20 parts of polyurethane resin, heat up to 130° C. and stir for 2 hours, and then ultrasonica...

Embodiment 2

[0043] A glass interlayer provided in this embodiment is prepared according to the following steps:

[0044] (1) Pretreatment of rare earth oxides: Dissolve 0.25 parts of La2O3 and 0.25 parts of CeO2 in nitric acid, then add 5 parts of molecular sieves, ultrasonically treat for 1.5h, and heat treat at 800°C for 2h.

[0045] (2) Preparation of modified LDHs: Weigh 0.18 mol of magnesium chloride, 0.08 mol of aluminum chloride and 0.285 mol of urea and dissolve them in deionized water, then sonicate for 30 min, add 0.1 mol of melamine phosphate solution dropwise, and transfer to and then placed in a muffle furnace at 90°C to react for 18 hours. After the reaction, filter and wash to obtain the modified LDHs powder.

[0046] (3) Disperse 7 parts of silica microspheres and 7 parts of zirconium dioxide microspheres in tetrahydrofuran, add 4 parts of phytic acid and 20 parts of polymethyl methacrylate in turn, after mixing, at 60 ° C The tetrahydrofuran was removed by drying under l...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a glass laminating glue. The glass laminating glue comprises 100 parts of polymethyl methacrylate, 15-20 parts of polyurethane resin, 3-8 parts of zirconia microspheres, 6-8 parts of silica microspheres, 10-20 parts of modified LDHs, 2-5 parts of phytic acid and 0.1-1 part of rare earth oxide, wherein the modified LDHs are prepared by the following steps: dispersing a water-soluble divalent metal salt, a water-soluble trivalent metal salt and a precipitant in water, dropwise adding a polyphosphate solution, and performing a reaction at 80-100 DEG C for 6-36 h. The modified LDHs are intercalated and modified with the polyphosphate, so the modified LDHs have a good flame retardant effect; the modified LDHs are added to the polymethyl methacrylate matrix, so the glasslaminating glue has good flame retardancy; and the zirconia microspheres, silica microspheres and phytic acid are added, so the glass laminating glue has excellent resistance to the high temperatureand radiation.

Description

technical field [0001] The invention relates to the technical field of glass production and manufacturing, in particular to a glass laminate. Background technique [0002] Laminated glass is laminated glass, which is sandwiched between two or more pieces of glass with one or more layers of organic polymer interlayer film (glass interlayer). After special high temperature and other processes, the glass and interlayer film are permanently A bonded composite glass product. [0003] Laminated glass is a kind of safety glass, which has good impact resistance, penetration resistance, safety, noise reduction, UV protection, etc. With the development of the times, laminated glass is widely used in architectural doors and windows, lighting ceilings, skylights, suspended ceilings, aquariums, etc. due to its unique properties. As people's demand for laminated glass becomes more diversified, not only the original characteristics of the glass are required, but also other special proper...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J133/12C09J175/04C09J11/04C09J11/08C09J11/06C03C27/12B32B17/10
CPCB32B17/10B32B17/1077B32B17/10779C08K2003/164C08K2003/166C08K2003/221C08K2003/2213C08K2201/014C08L2201/02C09J11/04C09J11/06C09J11/08C09J133/12B32B2367/00B32B2375/00C08L75/04C08K13/06C08K9/04C08K3/16C08K9/08C08K7/18C08K5/521C08K3/22
Inventor 刘凯王振赵俊郎
Owner 天津市凯辉玻璃制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com