Amino polycarboxylic acid porous material and its preparation method and application

A technology of amino polycarboxylic acid and porous material, applied in the field of amino polycarboxylic acid porous material and its preparation, to achieve the effects of stable chemical structure, high mechanical strength and low residual rate

Active Publication Date: 2021-06-08
TONGJI UNIV
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the surface of the porous material formed by the oil-in-water concentrated emulsion method is generally lipophilic, and it is difficult to use it in water-based systems such as water treatment, water-based systems, etc. Low cost and ease of operation are important prerequisites for the practical application of adsorbents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Amino polycarboxylic acid porous material and its preparation method and application
  • Amino polycarboxylic acid porous material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0037]

[0038] A kind of preparation method of amino polycarboxylic acid porous material, it comprises the steps:

[0039] (1) Disperse the rigid particles in an aqueous solution of polyethyleneimine, adjust the pH value to 10.5-12.5, add the oil phase under stirring, and obtain an oil-in-water emulsion;

[0040] (2) After adding a cross-linking agent into the oil-in-water emulsion, continue to stir for 1-3 minutes, and stand at 0-90°C for 6-48 hours to solidify; use ethanol to perform Soxhlet extraction and then vacuum-dry, or carry out cross-linking Add cyclohexane to the final system for azeotropic dehydration, then carry out distillation and deoiling, and then carry out vacuum drying to obtain a porous material;

[0041] (3), put the porous material into the aqueous solution of haloacetic acid (the amount is 1-3 molar equivalents of residual amino hydrogen), add a buffer solution with a pH value of 7-9, or continuously add sodium carbonate solution, dilute hydrogen Sod...

Embodiment 1

[0065] The preparation method of the amino polycarboxylic acid porous material of the present embodiment comprises the steps:

[0066] (1), adding silicon dioxide (particle size is 100 μm, 0.18g) to branched polyethyleneimine (M n =60000, 0.1g / mL, 3mL) in the aqueous solution, stir and disperse, adjust the pH value to 11, under vigorous stirring, add cyclohexane (6mL) dropwise to the aqueous dispersion, and drop it within 10min to obtain water Oil-in-emulsion;

[0067] (2), then add polyethylene glycol diglyceryl ether (M n =500, 0.87g, 0.25 equivalent of NH), continue to stir for 1min, and stand to solidify at 25°C for 6h; add 20mL cyclohexane to the system, then heat to reflux and separate most of the water with an oil-water separator, and then The cyclohexane was evaporated, and the remaining solid was vacuum-dried to obtain a porous material;

[0068] (3), get chloroacetic acid (1.485g, 15.7mmol) and dissolve in the phosphate buffer (0.2mol / L, 40mL), drop into the porou...

Embodiment 2

[0070] Same as Example 1, but with the same weight of microcrystalline cellulose instead of silicon dioxide particles, the amino polycarboxylic acid porous material is similarly obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides an amino polycarboxylic acid porous material and its preparation method and application. The preparation method is to disperse rigid particles in an aqueous solution of polyethyleneimine, adjust the pH value, add the oil phase under stirring, and obtain the water Oil-in-water emulsion; adding a cross-linking agent to the oil-in-water emulsion for cross-linking, deoiling and dehydrating, and drying to obtain a porous material; adding the porous material to an aqueous solution containing halogenated acetic acid to react under alkaline conditions to obtain amino Polycarboxylic acid porous material; when the porous material is used as an adsorbent, it can be regenerated by adjusting the pH value. Generally, organic anions are adsorbed at low pH values ​​and desorbed at high pH values; organic cations are adsorbed at high pH values ​​while low desorption under the pH value; the adsorption of metal ions is carried out near neutrality, and can be regenerated under the condition of pH=1-3; compared with the prior art, the amino polycarboxylic acid porous material of the present invention has large size and relatively high mechanical strength. High, easy to regenerate and easy to separate and so on.

Description

technical field [0001] The invention belongs to the technical field of material environmental protection and separation, and in particular relates to an amino polycarboxylic acid porous material and its preparation method and application. Background technique [0002] At present, there are many deficiencies in the use of adsorbents for environmental treatment and separation and purification. For example, some adsorbents are too small to be easily separated from the adsorption system; some adsorbents are difficult to regenerate. function, it is difficult to detach. In addition, regeneration and reuse, and ease of operation all place high demands on the adsorbent. [0003] The preparation of macroporous materials generally faces two challenges: low mechanical strength and difficult surface functionalization. Through-hole materials can be conveniently prepared by water-in-oil thick emulsion, but the obtained materials are usually like chalk, which is easy to be brittle and b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J9/28C08J9/40C08J3/24C08L79/02C08L1/04C08K3/36B01J20/26
CPCB01J20/267C08J3/24C08J3/246C08J9/28C08J9/40C08J2379/02C08J2401/04
Inventor 万德成金明潘海燕
Owner TONGJI UNIV