A kind of polymer cement waterproof coating and preparation method thereof

A waterproof coating and polymer technology, applied in the field of waterproof materials, can solve the problems of low tensile strength and elongation at break, achieve the effects of improving tensile performance and bonding performance, low surface tension, and improving tensile performance

Active Publication Date: 2021-09-21
北京宇阳泽丽防水材料有限责任公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention proposes a polymer cement waterproof coating and a preparation method thereof, which solves the problem of low tensile strength and elongation at break of the polymer cement waterproof coating in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polymer cement waterproof coating and preparation method thereof
  • A kind of polymer cement waterproof coating and preparation method thereof
  • A kind of polymer cement waterproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of polymer cement waterproof paint, is made up of the following components by weight:

[0032] 16 parts of cement, 13 parts of heavy calcium powder, 7 parts of quartz powder, 33 parts of styrene-acrylic emulsion, 4 parts of water, 3 parts of cationic starch, 4.5 parts of compatibilizer, 0.5 parts of poly-N-isopropylacrylamide, polydimethyl 0.05 parts of base siloxane, 1.5 parts of retarder, 0.3 parts of plasticizer, 0.01 part of preservative,

[0033] Among them, the cement is 425# white cement, the particle size of heavy calcium powder is 800 mesh, the particle size of quartz powder is 120-400 mesh, and the compatibilizer is bis(lauramide glutamine) sodium lysine, poloxamer and polyethylene glycol. The mass ratio of diol is a mixture of 1:5:3, the average molecular weight of polyethylene glycol is 760-840, and the retarder is a mixture of carboxymethyl chitosan and sucrose stearate with a mass ratio of 2:1. The plasticizer is dioctyl phthalate, the preservative...

Embodiment 2

[0041] A kind of polymer cement waterproof paint, is made up of the following components by weight:

[0042]25 parts of cement, 20 parts of heavy calcium powder, 15 parts of quartz powder, 45 parts of styrene-acrylic emulsion, 10 parts of water, 7 parts of cationic starch, 6.3 parts of compatibilizer, 1 part of poly-N-isopropylacrylamide, polydimethyl 0.5 parts of base siloxane, 3 parts of retarder, 1.2 parts of plasticizer, 0.1 part of preservative,

[0043] Among them, the cement is 425# white cement, the particle size of heavy calcium powder is 800 mesh, the particle size of quartz powder is 120-400 mesh, and the compatibilizer is bis(lauramide glutamine) sodium lysine, poloxamer and polyethylene glycol. The mass ratio of diol is a mixture of 1:5:3, the average molecular weight of polyethylene glycol is 760-840, and the retarder is a mixture of carboxymethyl chitosan and sucrose stearate with a mass ratio of 2:1. The plasticizer is dioctyl phthalate, the preservative is be...

Embodiment 3

[0046] A kind of polymer cement waterproof paint, is made up of the following components by weight:

[0047] 18 parts of cement, 15 parts of heavy calcium powder, 10 parts of quartz powder, 38 parts of styrene-acrylic emulsion, 6 parts of water, 4 parts of cationic starch, 5.1 parts of compatibilizer, 0.6 parts of poly N-isopropylacrylamide, polydimethyl 0.2 parts of base siloxane, 1.8 parts of retarder, 0.5 parts of plasticizer, 0.03 parts of preservative,

[0048] Among them, the cement is 425# white cement, the particle size of heavy calcium powder is 800 mesh, the particle size of quartz powder is 120-400 mesh, and the compatibilizer is bis(lauramide glutamine) sodium lysine, poloxamer and polyethylene glycol. The mass ratio of diol is a mixture of 1:5:3, the average molecular weight of polyethylene glycol is 760-840, and the retarder is a mixture of carboxymethyl chitosan and sucrose stearate with a mass ratio of 2:1. The plasticizer is dioctyl phthalate, the preservativ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field, and proposes a polymer cement waterproof coating and a preparation method thereof, which consists of the following components in parts by weight: 16-25 parts of cement, 13-20 parts of heavy calcium powder, 7-15 parts of quartz powder, 33-45 parts of styrene-acrylic emulsion, 4-10 parts of water, 3-7 parts of cationic starch, 4.5-6.3 parts of compatibilizer, 0.5-1 part of poly-N-isopropylacrylamide, 0.05 parts of polydimethylsiloxane ~0.5 parts, retarder 1.5~3 parts, plasticizer 0.3~1.2 parts, preservative 0.01~0.1 parts, compatibilizer is bis(lauramide glutamine) sodium lysine, poloxamer and poly The mass ratio of ethylene glycol is a mixture of 1:5:3, and the retarder is a mixture of carboxymethyl chitosan and sucrose stearate with a mass ratio of 2:1. Add half the volume of the mixed solution to ultrasonic dispersion and mix evenly, then add the remaining volume of the mixed solution and mix evenly. Through the above technical solution, the problem of low tensile strength and elongation at break of the polymer cement waterproof coating in the prior art is solved.

Description

technical field [0001] The invention belongs to the technical field of waterproof materials, and relates to a polymer cement waterproof coating and a preparation method thereof. Background technique [0002] Polymer Cement Waterproof Coating (JS Waterproof Coating) is a liquid material and matching powder formed by the optimized combination of synthetic polymer emulsion (such as polyacrylate, polyvinyl acetate, styrene-butadiene rubber emulsion, etc.) and various additives. It is a two-component waterproof coating composed of special cement, quartz powder and various additives. The two components are mixed on site to form a uniform and fine slurry, which is painted or sprayed on the surface of the substrate. After curing, it can form a flexible , High-strength waterproof coating film, using water as the carrier, overcomes the disadvantages of asphalt, tar, and organic solvent-based waterproof materials polluting the environment. It is a new green and environmentally friendly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B111/27
CPCC04B28/04C04B2111/00508C04B2111/27C04B2201/10C04B2201/50C04B14/28C04B24/26C04B24/38C04B24/287C04B24/42C04B14/06C04B24/124C04B24/28C04B24/06C04B24/045C04B24/128C04B24/32
Inventor 李建芳
Owner 北京宇阳泽丽防水材料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap