Preparation and applications of biocarbon supported thermally activated iron containing ore composite material

A composite material and biochar technology, applied in chemical instruments and methods, water pollutants, other chemical processes, etc., can solve problems such as difficult dispersion and general biochar adsorption effect, achieve increased dispersibility, simple and feasible preparation method, The effect of improving the efficiency of heavy metal restoration

Inactive Publication Date: 2020-02-28
CENT SOUTH UNIV
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the limited surface groups on its surface and difficulty in dispersing, the adsorption effect of biochar is not good.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation and applications of biocarbon supported thermally activated iron containing ore composite material
  • Preparation and applications of biocarbon supported thermally activated iron containing ore composite material
  • Preparation and applications of biocarbon supported thermally activated iron containing ore composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A preparation method of biochar-loaded heat-activated iron-containing mineral composite material according to the present invention is as follows:

[0029] Firstly, the biomass raw materials (agricultural waste rice straw and bagasse) were washed and dried at 80 °C for 48 h to obtain biomass with a water content of 10-11%, and the mineral raw materials were preliminarily crushed. 1~3 cm, the selected iron-containing mineral is goethite, the crushing particle size is 0.5~1 cm, then the biomass and mineral raw materials are ground and mixed according to a certain mass ratio (3:1), and passed through 80~100 mesh The mixed material powder is obtained by sieving; the mixed material powder is put into a mold to obtain a biomass-loaded mineral complex with a diameter of 0.5-2 cm and a height of 1-1.5 cm;

[0030] The biomass-loaded mineral complex was placed in an atmosphere with hydrogen as the reducing atmosphere and nitrogen as the protective gas, the gas flow rate was cont...

Embodiment 2

[0033] The biochar-loaded heat-activated iron-containing mineral composite material of the present invention treats heavy metal ions Cr(VI) and Cu(II) in water, comprising the following steps:

[0034] Weigh 0.05 g of bagasse biochar (Z-Z) / straw biochar (J-Z) loaded thermally activated iron-containing mineral composites and place them in a 50 ml centrifuge tube, set the concentration gradient of heavy metals to 30, 50, 150, 250, 350 , 450 mg / L, adjust the pH value to about 6 with 1 mol / L sodium hydroxide and 30% nitric acid solution, put the centrifuge tube in a constant temperature shaker for 24 h, set the temperature at 30 °C, and rotate at 170 r / min. After 24 hours of reaction, 1 mL of the solution was taken for centrifugation, and the supernatant was taken into a centrifuge tube. The chromium ion content in the solution was measured by the diphenylcarbohydrazide (DPCI) method, and the copper ion content in the solution was determined by the BCO method. The results showed...

Embodiment 3

[0036] The biochar-loaded heat-activated iron-containing mineral composite material of the present invention treats Cr(VI) and Cu(II) of heavy metal ions in water, comprising the following steps:

[0037]Weigh 0.05 g of bagasse biochar (Z-Z) / straw biochar (J-Z) loaded heat-activated iron-containing mineral composites and place them in a 50 mL centrifuge tube, add 15 mL of deionized water into the centrifuge tube, and mix the materials and After the water is fully mixed, measure the initial pH value of the solution with a pH meter, and adjust the pH value of the solution with 1 mol / L sodium hydroxide and 30% nitric acid solution, and set the gradient to 4, 5, 6, 7, 8. After the pH value of the system was stabilized, 5 mL of copper solution and chromium solution with corresponding pH values ​​were added respectively, and the centrifuge tube was placed in a constant temperature shaker for 24 h. The temperature was set at 30 °C and the rotation speed was 170 r / min. After the react...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
heightaaaaaaaaaa
adsorption capacityaaaaaaaaaa
Login to view more

Abstract

The invention relates to preparation and applications of a biocarbon supported thermally activated iron containing ore composite material. Thermally activated iron containing ores are loaded on the surface of biocarbon. The preparation method comprises following steps: grinding iron containing ores and a biomass material, then evenly mixing ores and the biomass material according to a certain massratio, evenly pressing and moulding the mixture, burning the mixture in a reductive atmosphere, naturally cooling, and milling the mixture in an anaerobic atmosphere to obtain fine powder, namely thebiocarbon supported thermally activated iron containing ore composite material. The prepared biocarbon supported thermally activated iron containing ore composite material has the characteristics oflarge specific surface area, high stability, and strong oxidizing-reducing activity. Compared with biomass or thermally activated iron containing ores, the composite material has a prominently improved performance on removing or stabilizing heavy metal ions in water and soil, and thus can be used to process heavy metal pollution of water and soil.

Description

technical field [0001] The invention belongs to the field of environmental functional materials, in particular to a preparation method of biochar-loaded heat-activated iron-containing mineral composite materials. Background technique [0002] Iron oxides widely exist in the natural environment. Due to their excellent properties such as low toxicity, fast kinetics, and strong affinity for heavy metals, they have been often used as high-efficiency adsorbents for heavy metals in recent years. By using H 2 Reduction of ferrihydrite, goethite (α-FeOOH) or hematite (α-FeOOH) as reducing gas 2 o 3 ) and other iron-containing minerals can obtain zero-valent iron (ZVI). Due to the large surface-to-volume ratio and the increased proportion of surface and near-surface atoms, the ZVI thus prepared has unique mechanical, electronic, and magnetic properties, and can directly reduce high-priced heavy metal ions from industrial waste, which has a wide range of environmental application p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/20B01J20/02B01J20/30C02F1/28C02F1/70B09C1/00B09C1/08C02F101/20C02F101/22
CPCB01J20/02B01J20/20B01J20/3007B01J20/3021B01J20/3078B01J2220/4825B09C1/00B09C1/08C02F1/283C02F1/705C02F2101/20C02F2101/22
Inventor 朱建裕甘敏曾健陈耀宗陈芳章可何鹏梁金叶黄冬丽蔡渺
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap