Light-driven oxygen production type corneal contact lens, preparation method and application thereof

A contact lens and light-driven technology, which is applied in optics, optical components, glasses/goggles, etc., can solve the problem of limited use of ophthalmic lenses, achieve excellent control performance, improve wearing comfort, and improve biocompatibility Effect

Active Publication Date: 2020-04-10
JINLING INST OF TECH
View PDF13 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The patent (CN106104365B) discloses "an ophthalmic lens with an oxygen-generating element in it", and the patent also proposes "actively generating oxygen", which is similar to the "oxygen production" of the present invention, but the principle of generating oxygen is the well-known electrolysis of aquatic products. Oxygen, as stated in the patent, the ophthalmic lens essentially needs to be "connected to power supply and control elements" to drive the ophthalmic lens, and the use of the ophthalmic lens is extremely limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Light-driven oxygen production type corneal contact lens, preparation method and application thereof
  • Light-driven oxygen production type corneal contact lens, preparation method and application thereof
  • Light-driven oxygen production type corneal contact lens, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] (1) p-type semiconductor (copper bismuthate, CuBi 2 o 4 ), n-type semiconductor (bismuth vanadate, BiVO 4 ), passivation layer (magnesium oxide, MgO) target preparation:

[0051] The p-type semiconductor, n-type semiconductor, and passivation layer powder are used as raw materials, and ethanol is used as the medium. After the raw materials are wet ball milled for 12 hours, they are dried at 80°C and sintered by hot pressing to form a dense circular target.

[0052] (2) Preparation of central interlayer slurry:

[0053] The raw material of graphene slurry is ultrasonically dispersed in ethanol solvent according to the concentration of 1.0wt%.

[0054] (3) Preparation of flexible heterojunction electrodes:

[0055] The graphene center interlayer slurry was spin-coated on the surface of the polished silicon wafer, and dried at 100°C; the copper bismuthate, bismuth vanadate and magnesium oxide targets were respectively installed on the target position of the magnetron s...

Embodiment 2

[0064] (1) p-type semiconductor (copper bismuthate, CuBi 2 o 4 ; Cuprous oxide, Cu 2 O), n-type semiconductor (bismuth vanadate, BiVO 4 ;Titanium dioxide, TiO 2), passivation layer (aluminum oxide, Al 2 o 3 ) target preparation:

[0065] The p-type semiconductor, n-type semiconductor, and passivation layer powder are used as raw materials, and ethanol is used as the medium. After the raw materials are wet ball milled for 12 hours, they are dried at 80°C and sintered by hot pressing to form a dense circular target.

[0066] (2) Preparation of central interlayer slurry:

[0067] The graphene puree is ultrasonically dispersed in ethanol solvent according to the concentration of 2.0wt%.

[0068] (3) Preparation of flexible heterojunction electrodes:

[0069] The graphene center interlayer slurry is spin-coated on the surface of the polished silicon wafer, and dried at 100°C; the targets of copper bismuthate, cuprous oxide, bismuth vanadate, titanium dioxide and alumina are...

Embodiment 3

[0078] (1) p-type semiconductor (zinc oxide, ZnO), n-type semiconductor (bismuth vanadate), passivation layer (aluminum oxide, Al 2 o 3 ) target preparation:

[0079] The p-type semiconductor, n-type semiconductor, and passivation layer powder are used as raw materials, and ethanol is used as the medium. After the raw materials are wet ball milled for 12 hours, they are dried at 80°C and sintered by hot pressing to form a dense circular target.

[0080] (2) Preparation of central interlayer slurry:

[0081] The carbon nanotube slurry was ultrasonically dispersed in an ethanol solvent at a concentration of 2.0 wt%.

[0082] (3) Preparation of flexible heterojunction electrodes:

[0083] The carbon nanocenter interlayer slurry was spin-coated on the surface of the polished silicon wafer, and dried at 100°C; the zinc oxide, bismuth vanadate and aluminum oxide targets were respectively installed on the target position of the magnetron sputtering instrument; the spin-coated carb...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
transmittivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a light-driven oxygen production type corneal contact lens, a preparation method and application thereof, and belongs to the technical field of corneal contact lenses. The light-driven oxygen production type corneal contact lens is composed of a flexible heterojunction photocatalytic electrode and a silicon-based hydrogel matrix. The preparation method includes: firstly, sputtering a p-type semiconductor and an n-type semiconductor to two faces of a flexible center interlayer through a magnetron sputtering method to prepare the flexible heterojunction photocatalytic electrode, then coating the flexible heterojunction photocatalytic electrode with a passivation layer and performing packaging into the silicon-based hydrogel matrix, and conducting machining and formingto obtain the light-driven oxygen generation type corneal contact lens. According to the invention, the oxygen supply mode that the traditional corneal contact lens carries oxygen with water or allows oxygen to permeate through a channel is changed into a self-oxygen-production oxygen supply mode, so that the wearing comfort and durability of the corneal contact lens are improved. The light-driven oxygen generation type corneal contact lens can absorb harmful light (ultraviolet light) or strong light (blue light and laser) to protect eyes; and the generated high active oxygen, hydrogen and the like have prevention and treatment effects on ophthalmic diseases (keratitis, conjunctivitis and glaucoma) caused by bacteria and viruses.

Description

technical field [0001] The invention relates to a light-driven oxygen-generating corneal contact lens, and a preparation method and application of the light-driven oxygen-generating corneal contact lens. More specifically, it relates to a corneal contact lens and a preparation method thereof, as well as its application in optical protection, vision correction, vision rehabilitation and treatment of ophthalmic diseases. The invention belongs to the technical field of corneal contact lenses. Background technique [0002] Eyes are the window to the soul, and vision needs careful care. In 2018, the Basic Education Quality Monitoring Center of the Ministry of Education released the "China Compulsory Education Quality Monitoring Report". The report pointed out that the number of myopia in China has reached 600 million, and the myopia rate of young people has ranked first in the world. The myopia rate of Chinese junior high school students and college students has exceeded 70%, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G02C7/04
CPCG02C7/04G02C7/049
Inventor 林青胡颖飞王威汪圆圆杜洪秀赵媛梁栋张小娟郝凌云
Owner JINLING INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap