A kind of spray quick-setting waterproof coating for marine anticorrosion and its preparation and construction method

A marine anti-corrosion and waterproof coating technology, applied in the field of materials, can solve problems affecting the performance and appearance of buildings, moldy buildings, and affecting service life

Active Publication Date: 2021-05-07
SHANDONG NORTH CHUANGXIN WATERPROOF SCI & TECH GRP CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] High Cl in marine environment - The concentration has a corrosive effect on the concrete of the building and the steel bars in the concrete, seriously affecting their service life; and the high humidity in the marine environment will make the building moldy, affecting the performance and appearance of the building

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment example 1

[0034] The spray quick-setting waterproof coating for marine anticorrosion is composed of A and B materials; among them, A material is composed of the following components: 70# emulsified asphalt 50Kg, neoprene latex 30kg, zinc oxide dispersion 8Kg, filler slurry 13Kg, sodium silicate aqueous solution 1Kg, 22462Kg anti-aging agent, 0.05Kg zinc pyrithione zinc pyrithione, 0.2Kg silicone defoamer;

[0035] Material B consists of the following components: calcium nitrate 11Kg, ethylene glycol 1Kg, alkyl polyoxyethylene ether 0.2Kg, deionized water 87.8Kg.

[0036] In the first embodiment, the zinc oxide dispersion liquid is composed of the following components: zinc oxide 50Kg, sodium bentonite 0.5Kg, sodium hydroxide 0.03Kg, sodium methylene dinaphthalene sulfonate 0.7Kg, organic silicon defoamer 0.4Kg , Deionized water 48.37Kg.

[0037] In the first embodiment, the filler slurry is composed of the following components: wollastonite 30Kg, kaolin 40Kg, sodium bentonite 1.0Kg, so...

Embodiment example 2

[0050] In the second example, material A is composed of the following components: 40Kg of 90# emulsified asphalt, 30kg of neoprene latex, 20kg of pre-crosslinked styrene-butadiene latex, 12Kg of zinc oxide dispersion, 5Kg of filler slurry, 2Kg of sodium silicate aqueous solution, anti-aging Agent 2246 1.5Kg, anti-mold antibacterial agent zinc pyrithione 0.07Kg, silicone defoamer 0.2Kg;

[0051] Material B consists of the following components: calcium acetate 13Kg, ethylene glycol 3Kg, alkyl polyoxyethylene ether 0.3Kg, deionized water 83.7Kg.

[0052] In the second embodiment, the zinc oxide dispersion liquid is composed of the following components: zinc oxide 60Kg, sodium bentonite 1.2Kg, sodium hydroxide 0.04Kg, sodium methylene dinaphthalene sulfonate 1.2Kg, silicone defoamer 0.4Kg , Deionized water 37.16Kg.

[0053] In the second embodiment, the filler slurry is composed of the following components: calcium carbonate 73g, kaolin 5Kg, sodium bentonite 0.5Kg, sodium hydroxi...

Embodiment example 3

[0055] In this embodiment three, material A consists of the following components: 90# emulsified asphalt 50Kg, pre-crosslinked chloroprene latex 25kg, styrene-butadiene latex 10kg, zinc oxide dispersion 8Kg, filler slurry 12Kg, sodium silicate aqueous solution 1.5Kg, Anti-aging agent 2246 2Kg, anti-mold antibacterial agent pyrithione zinc 0.05Kg, silicone defoamer 0.15Kg;

[0056] Material B consists of the following components: barium nitrate 10Kg, aluminum nitrate 5Kg, ethylene glycol 4.5Kg, alkyl polyoxyethylene ether 0.5Kg, deionized water 80Kg.

[0057] In the third example, the zinc oxide dispersion liquid is composed of the following components: zinc oxide 55Kg, sodium bentonite 1.0Kg, sodium hydroxide 0.03Kg, sodium methylene dinaphthalene sulfonate 1.0Kg, silicone defoamer 0.3Kg , Deionized water 42.67Kg.

[0058] In the third example, the filler slurry is composed of the following components: calcium carbonate 60g, mica powder 10Kg, sodium bentonite 1.0Kg, sodium hy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
solid contentaaaaaaaaaa
Login to view more

Abstract

The invention provides a spray quick-setting waterproof coating for marine anticorrosion and its preparation and construction method. The present invention is composed of material A and material B. According to weight percentage, material A is composed of the following components: 40-65% of emulsified asphalt, 27-50% of rubber emulsion, 8-20% of zinc oxide dispersion, 5-5% of filler slurry 15%, sodium silicate aqueous solution 0.05-3%, anti-aging agent 1.5-2.5%, anti-mold and antibacterial agent 0.03-0.08%, defoamer 0.1-0.3%; B material is composed of the following components: Chloride-free Soluble metal salt 5-20%, ethylene glycol 1-5%, alkyl polyoxyethylene ether 0.1-0.5%, and the rest is deionized water. The waterproof coating film for marine anticorrosion prepared by the invention has good chloride ion permeability resistance, good waterproof and antibacterial effects, and can be used for marine building waterproofing.

Description

technical field [0001] The invention belongs to the technical field of materials, and in particular relates to a spraying quick-setting waterproof coating for marine anticorrosion and its preparation and construction method. Background technique [0002] High Cl in marine environment - The concentration has a corrosive effect on the concrete of the building and the steel bars in the concrete, seriously affecting their service life; and the high humidity in the marine environment will make the building moldy, affecting the performance and appearance of the building. Therefore, the high salinity and high humidity of the marine environment put forward higher requirements for the protective materials of buildings. Therefore, for the waterproofing of buildings in marine areas, our company has developed a corrosion-resistant chloride ion permeability and antibacterial properties. Spray quick-setting waterproof coating for marine anticorrosion. Contents of the invention [0003...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D195/00C09D111/02C09D109/08C09D5/08C09D5/14E04B1/64E04B1/66
CPCC08K2003/2296C08K2003/265C08K2003/287C08K2201/003C08K2201/014C08L2205/025C08L2205/035C09D5/08C09D5/14C09D195/00E04B1/642E04B1/66C08L11/02C08L71/02C08L33/02C08K13/02C08K3/22C08K3/34C08K5/378C08K3/346C08K5/42C08K3/28C08K5/053C08L9/08C08K3/26C08K5/098
Inventor 王荣博刘方浩严从立王志强辛海洋劳振兴
Owner SHANDONG NORTH CHUANGXIN WATERPROOF SCI & TECH GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap