Preparation method of emulsion type acrylic pressure-sensitive adhesive for high-gloss reflective cloth
A technology of acrylic pressure-sensitive adhesive and reflective cloth, which is applied in the field of pressure-sensitive adhesives. It can solve the problems of affecting the performance of acrylic pressure-sensitive adhesives, poor emulsification effect, and weak gloss, and achieves no explosion and gel phenomenon. , good emulsification effect, excellent process conditions
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0025] A preparation method of emulsion-type acrylic pressure-sensitive adhesive for high-gloss reflective cloth, the steps are as follows:
[0026] (1) Weigh 55 parts by weight of acrylic acid, 75 parts of styrene, 30 parts of modified self-made rosin ester emulsions, 80 parts of isooctyl acrylate, 55 parts of methyl methacrylate, and 50 parts of hydroxyethyl acrylate part, 15 parts of initiator, cross-linking agent diacetone acrylamide and cross-linking agent adipate dihydrazide total 2.5 parts; the ratio of described diacetone acrylamide and adipate dihydrazide is 1:1, ammonia 25 parts, 8 parts of emulsifier, 120 parts of deionized water, 1.5 parts of tackifier. Preferably, the initiator is ammonium persulfate. The modified self-made rosin ester emulsion is prepared by weighing 40 parts of rosin glyceride in parts by weight and melting at 140°C under nitrogen protection, adding 5 parts of ethylene oxide, 3 parts of maleic anhydride, 1 part of p-toluene under stirring sulf...
Embodiment 2
[0030] A preparation method of emulsion-type acrylic pressure-sensitive adhesive for high-gloss reflective cloth, the steps are as follows:
[0031] (1) Weigh 50 parts by weight of acrylic acid, 80 parts of styrene, 40 parts of modified homemade rosin ester emulsions, 75 parts of isooctyl acrylate, 65 parts of methyl methacrylate, 40 parts of hydroxyethyl acrylate part, 20 parts of initiator ammonium persulfate, 20 parts of ammonia water, 10 parts of emulsifier sodium lauryl sulfate, 100 parts of deionized water, 2 parts of water-based tackifier, 2 parts of crosslinking agent (crosslinking agent is diacetone acrylamide and adipic acid dihydrazide, the diacetone acrylamide and the adipic acid dihydrazide ratio are 1:1.); The modified self-made rosin ester emulsion is prepared by weighing 50 parts by weight Parts of rosin glyceride melted under nitrogen protection at 160°C, added 8 parts of ethylene oxide, 5 parts of maleic anhydride, and 2 parts of p-toluenesulfonic acid under ...
Embodiment 3
[0035] A preparation method of emulsion-type acrylic pressure-sensitive adhesive for high-gloss reflective cloth, the steps are as follows:
[0036](1) Weigh 65 parts by weight of acrylic acid, 70 parts of styrene, 50 parts of modified homemade rosin ester emulsions, 95 parts of isooctyl acrylate, 50 parts of methyl methacrylate, 60 parts of hydroxyethyl acrylate part, 10 parts of initiator ammonium persulfate, 30 parts of ammonia water, 5 parts of emulsifier sodium lauryl sulfate, 150 parts of deionized water, 1 part of water-based tackifier, 3 parts of crosslinking agent (the crosslinking agent is diacetone Acrylamide and adipic acid dihydrazide, the diacetone acrylamide and the described adipic acid dihydrazide ratio are 1:1.); The self-made rosin ester emulsion of the modification is prepared by weighing 45 parts by weight Parts of rosin glyceride melted under nitrogen protection at 150°C, added 6 parts of ethylene oxide, 4 parts of maleic anhydride, and 1.5 parts of p-tol...
PUM
Property | Measurement | Unit |
---|---|---|
peel strength | aaaaa | aaaaa |
gloss | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com