A kind of bismuth oxide/manganese oxide composite supercapacitor and preparation method thereof

A supercapacitor and manganese oxide technology, applied in the manufacture of hybrid/electric double layer capacitors, hybrid capacitor electrodes, etc., can solve problems such as reduction or crystal transformation, unstable structure of bismuth oxide, etc., to improve stability and enhance electrochemical The effect of capacitive performance, high application prospects and value in use

Active Publication Date: 2022-05-17
JIANGSU UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, the application of bismuth oxide in the field of supercapacitors has attracted the attention of the industry. However, the structure of a single bismuth oxide is unstable, and it is prone to reduction or crystal transformation. It is necessary to further improve its stability when it is used in capacitors.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of bismuth oxide/manganese oxide composite supercapacitor and preparation method thereof
  • A kind of bismuth oxide/manganese oxide composite supercapacitor and preparation method thereof
  • A kind of bismuth oxide/manganese oxide composite supercapacitor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Weigh 0.4g of bismuth nitrate, 0.2g of manganese nitrate, and 0.3g of mesoporous silica dissolved in 20ml of absolute ethanol and stir for 3 hours, dry at 30°C for 10h, put the sample into a tube furnace for 3 hours at 500°C for annealing, and then use Wash repeatedly with sodium hydroxide and deionized aqueous solution, centrifuge at last, and dry at 30°C for 10 hours to obtain bismuth oxide / manganese oxide.

[0031] figure 1 It is a scanning electron microscope image of a bismuth oxide / manganese oxide composite supercapacitor. In the figure, the bismuth oxide with a dendritic structure as the main body is covered by a film-like manganese oxide. The film-like manganese oxide increases the specific surface area of ​​the overall structure and increases a lot The active sites and oxygen vacancies effectively improve the electrochemical capacitive performance of the material.

[0032] figure 2 It is the transmission electron microscope (a) and the element distribution m...

Embodiment 2

[0034] Weigh 0.1g of bismuth nitrate, 0.3g of manganese nitrate, 0.1g of mesoporous silica dissolved in 10ml of absolute ethanol and stir for 2 hours, dry at 60°C for 5h, put the sample in a tube furnace for 2 hours at 600°C for annealing, and then use Wash repeatedly with sodium hydroxide and deionized aqueous solution, centrifuge at last, and dry at 60°C for 5 hours to obtain bismuth oxide / manganese oxide.

[0035] image 3 It is the X-ray diffraction pattern of the bismuth oxide / manganese oxide composite supercapacitor, and the test result is consistent with the standard comparison card comparison, indicating that the bismuth oxide and manganese oxide are successfully composited.

[0036] Figure 4 It is the XPS diagram of a bismuth oxide / manganese oxide composite supercapacitor. The full spectrum shows that the composite does contain manganese, oxygen, and bismuth elements. Bi 4f shows two characteristic peaks, which are 4f at 164.1ev 5 / 2 and 4f at 158.8ev 7 / 2 , indicat...

Embodiment 3

[0039] Weigh 1g of bismuth nitrate, 0.5g of manganese nitrate, 1g of mesoporous silica dissolved in 50ml of absolute ethanol and stir for 5 hours, dry at 80°C for 1h, put the sample in a tube furnace for 5 hours at 300°C and anneal for 5 hours, then oxidize with hydrogen Repeated washing with sodium and deionized aqueous solution, centrifugation at last, and drying at 80°C for 1 hour to obtain bismuth oxide / manganese oxide.

[0040] Image 6 It is the cyclic voltammogram of the bismuth oxide / manganese oxide composite supercapacitor, using the composite as the working electrode, the platinum sheet electrode as the counter electrode, and silver / silver chloride as the reference electrode to form a three-electrode system. At 1 mVs in the electrolyte -1 ,10 mV s -1 ,50 mV s -1 ,100 mV s -1All CV curves have a similar shape, and the potential range of the Faraday redox peak is -0.2V to 0.5V. The CV curves shown in the figure have a larger closed area, indicating a higher capaci...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a bismuth oxide / manganese oxide composite supercapacitor and a preparation method thereof, which belong to the technical field of material preparation; in the invention, mesoporous silicon dioxide is selected as a template, and bismuth oxide with high ion conductivity and specific capacitance High manganese oxide is combined to form a composite supercapacitor with more excellent electrochemical performance; the prepared supercapacitor has high specific capacitance and energy density under the premise of ensuring the stability of the electrode material, and the raw materials required for the preparation method are cheap , the process is simple, the reaction is mild, and it can be recycled in industry.

Description

technical field [0001] The invention belongs to the technical field of material preparation, and in particular relates to a bismuth oxide / manganese oxide composite supercapacitor and a preparation method thereof. Background technique [0002] As an emerging energy storage material in the 21st century, supercapacitors have become an important goal of sustainable energy research due to their small size, high energy, low cost, and long life. However, the high energy density and strong electrochemical stability of the supercapacitors currently prepared have not been well demonstrated and realized due to the limitation of materials, that is, it is difficult to have a relatively stable electrode material under the premise of ensuring stability. High specific capacitance, which hinders the application and development of supercapacitors. [0003] As an abundant element in the earth's crust, manganese has rich physical and chemical properties, and has excellent performance in cataly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01G11/86H01G11/46H01G11/24
CPCH01G11/86H01G11/46H01G11/24Y02E60/13
Inventor 李海涛储晨刘运亮李亚锡武如强李华明邓沛基
Owner JIANGSU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com