Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Gemini fluorine-containing surfactant as well as preparation method and application thereof

A surfactant and gemini-type technology, applied in the field of gemini-type fluorine-containing surfactants and its preparation, can solve problems such as endocrine disruption and neurotoxicity

Active Publication Date: 2021-04-23
SHENZHEN TAIKE TECH
View PDF15 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the toxic mechanism of PFOS / PFOA is not yet clear, many animal experiments have shown that PFOS / PFOA has hepatotoxicity, endocrine disruption, embryotoxicity, reproductive toxicity, neurotoxicity and potential carcinogenicity, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Gemini fluorine-containing surfactant as well as preparation method and application thereof
  • Gemini fluorine-containing surfactant as well as preparation method and application thereof
  • Gemini fluorine-containing surfactant as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0063] The present invention further discloses the preparation method of the above-mentioned gemini type fluorine-containing surfactant, first forming a block copolymer by coupling method with perfluoropolyether and chlorinated polyethylene glycol monomethyl ether, and further hydrolyzing the block copolymer Condensation obtains gemini type surfactant, specifically comprises the following steps:

[0064] (1) Alkenylation of perfluoropolyether

[0065] a. Prepare acid-binding agent: by weight, dissolve 4-30 parts of inorganic base in 8-300 parts of water to obtain acid-binding agent;

[0066] b. Substitution reaction: by weight, put into the reactor 50~100 parts of perfluoropolyether alcohol, 0.4~1 part of tetrabutylammonium bromide, 50~3000 parts of fluoroalkylbenzene solvent, 4~50 parts of halogen Substituting allyl group, control the temperature at 20-85°C, add the prepared acid-binding agent dropwise, and the dropping time is 30 minutes to 2 hours; after the addition, keep...

Embodiment 1

[0084] (1) Synthesis of chlorosilanized perfluoropolyether

[0085] 5.6g of potassium hydroxide is dissolved in 20g of deionized water to obtain an acid-binding agent for subsequent use;

[0086] A 500mL three-necked flask was equipped with a thermometer, a reflux condenser and a constant pressure dropping funnel, and 170g of 1,3-bistrifluorotoluene, 80g of number-average perfluoropolyether alcohol (molecular weight: 2000, purchased from HEC Group), and 0.5g of four Butylammonium bromide, 5.3g propylene bromide; after stirring to dissolve completely, raise the temperature to 85°C, add the pre-prepared acid-binding agent dropwise, the dropwise addition time is 30 minutes, and keep warm for 4 hours after the addition;

[0087] After the reaction, stand still and separate layers, discard the upper water layer, add 3g of anhydrous magnesium sulfate to the lower oil layer and dry for 12 hours, filter and remove the desiccant to obtain an alkenylated perfluoropolyether solution, whi...

Embodiment 2

[0100] (1) Synthesis of chlorosilanized perfluoropolyether

[0101] 5.6g of potassium hydroxide is dissolved in 20g of deionized water to obtain an acid-binding agent for subsequent use;

[0102] A 500mL three-necked flask was equipped with a thermometer, a reflux condenser and a constant pressure dropping funnel, and 170g of 1,3-bistrifluorotoluene, 120g of number-average perfluoropolyether alcohol (molecular weight of 3000, purchased from HEC Group), and 0.5g of four Butylammonium bromide, 5.3 g propene bromide. After stirring to dissolve completely, raise the temperature to 85°C, add the pre-prepared acid-binding agent dropwise for 30 minutes, and keep it warm for 4 hours after adding;

[0103] After the reaction, stand still and separate layers, discard the upper water layer, add 3g of anhydrous magnesium sulfate to the lower oil layer and dry for 12 hours, filter and remove the desiccant to obtain an alkenylated perfluoropolyether solution, which is transferred to a 500m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Surface tensionaaaaaaaaaa
Surface tensionaaaaaaaaaa
Surface tensionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a gemini fluorine-containing surfactant as well as a preparation method and application thereof. Perfluoropolyether alcohol (PFPE-OH) reacts with halogenated allyl, and unsaturated double bonds are introduced; then a hydrosilylation reaction with methyl hydrogen dichlorosilane is carried out under the catalysis of platinum; the obtained intermediate product reacts with carbon magnesium polyethylene glycol monomethyl ether to generate perfluoropolyether-polyethylene glycol-methyl monochlorosilane (PFPE-SiCl-PEG); and further hydrolytic condensation is conducted to obtain the gemini fluorine-containing surfactant. The hydrophobic group adopted by the surfactant is perfluoropolyether, so that the problems that long-carbon-chain fluoroalkyl adopted by common perfluorooctane sulfonamide (PFOS), perfluorooctane sulfonic acid (PFOA) and other fluorosurfactants is difficult to degrade and accumulates toxicity are avoided, the hydrophobicity of the surfactant is easy to control by controlling the molecular weight of a perfluoropolyether chain segment, and the surfactant has very high hydrophobic efficiency. The gemini fluorine-containing surfactant provided by the invention is simple and convenient in preparation process, mild in reaction condition and suitable for industrial production, and only conventional equipment is needed in production.

Description

technical field [0001] The invention relates to a gemini-type fluorine-containing surfactant, its preparation method and application, and belongs to the field of fine chemicals and auxiliary agent synthesis. Background technique [0002] Perfluoropolyethers (Perfluoropolyethers, PFPE) were first discovered in the 1960s. They are a special kind of perfluoropolymer compounds with an average molecular weight ranging from 500 to 15,000. Composed of carbon, fluorine and oxygen elements, the product has a series of characteristics such as heat resistance, oxidation resistance, radiation resistance, corrosion resistance, and non-combustibility. [0003] The prior art discloses a perfluoropolyether-based fluorocarbon surfactant and its preparation method and application, which belong to the technical field of polymer surfactants and can be used as an oil phase component in the PCR method to realize in-droplet digital PCR application, and droplet stability can be guaranteed, the per...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01F17/54B01F17/42C08G81/00C08F114/26C09K23/54C09K23/42
CPCC08G81/00C08F114/26C09K23/00
Inventor 李战雄
Owner SHENZHEN TAIKE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com