Calcium carbide with diversified raw materials and preparation method of calcium carbide

A calcium carbide and raw material technology, applied in the direction of carbide, calcium carbide, etc., can solve the problems of calcium carbide raw materials, such as diversification and cost reduction, poor chemical reactivity, difficult melting reaction, etc., to achieve good bonding effect, lower melting point, and lower reaction temperature Effect

Inactive Publication Date: 2021-06-25
赵黎明 +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN101172605B discloses a method for synthesizing calcium carbide with coal powder, but coal powder is easy to graphitize at high temperature, has low porosity, poor chemical reactivity, and cannot be used as a reducing agent for producing calcium carbide
Therefore, in the current actual production, only a small amount of anthracite is added to the coke, and the anthracite will float on the upper layer of the reaction system during production, which is difficult to melt and react, and has not really solved the problem of diversification of calcium carbide raw materials or cost reduction.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Weigh 20kg lignite, make coke after washing, crush it to below 2cm through a jaw crusher, grind it through a ball mill, and sieve it with a 20-mesh sieve for later use; weigh 20kg quicklime, pass it through a 20-mesh sieve after grinding Sieve for standby; Weigh 0.2kg fluorite, crush it to below 2cm through a jaw crusher, grind it through a ball mill, and sieve it with a 20-mesh sieve for standby after grinding; Weigh 15g dodecyl carboxymethyl cellulose as viscous Mixture spare.

[0037] Add sieved lignite, quicklime, fluorite and binder into the kneader, fully knead and stir, and then granulate through a 45MPa ball press machine. The diameter of the abrasive tool is 30mm, and the granulation is spherical or hemispherical. , has a certain strength. Place it in a drying shed to dry for a week, dry it in an oven at 150°C for 2 hours, and then smelt it in an electric arc furnace at 1900°C for 30 minutes, take it out, and cool it to obtain a calcium carbide product with a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Ash contentaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of calcium carbide chemical industry, and discloses a raw material diversified calcium carbide, which takes coke prepared from bituminous coal, quick lime and fluorite as main raw materials, and the mass ratio of the coke prepared from bituminous coal to the quick lime to the fluorite is 100:(80-145):(0.01-5). According to the invention, the coke prepared from bituminous coal is uniformly mixed with the quick lime and the fluorite, and thus mass transfer and reaction acceleration are facilitated. The invention also discloses a preparation method of the raw material diversified calcium carbide, which comprises the following steps: washing bituminous coal, preparing coke, crushing the coke, respectively crushing and sieving the quick lime and the fluorite, conducting mixing, uniformly mixing an adhesive with the raw materials, pressing the materials into a spherical or semispherical raw material by using a ball press, conducting drying until the water content is less than or equal to 6%, taking the raw material as a calcium carbide raw material, and feeding the raw material into an electric arc furnace to smelt the calcium carbide. According to the production method for preparing the calcium carbide, the reaction temperature is reduced, the problem of scaling of the calcium carbide furnace wall can be solved, the electric energy consumption of the calcium carbide can be reduced, and the method has a relatively great application prospect.

Description

technical field [0001] The invention relates to the technical field of calcium carbide chemical industry, in particular to a method for preparing calcium carbide in which semi-coke is replaced by coal powder. Background technique [0002] In 1862, Hare and Wohler used Zn, Ca and C to prepare CaC for the first time in the laboratory. 2 , three decades later Moisson and Willson made CaC in an electric furnace from CaO and coal 2 , that is calcium carbide. Calcium carbide is one of the important basic chemical raw materials. The acetylene produced by the reaction of calcium carbide and water can be further synthesized into related series of products, such as acetaldehyde, acetic acid, vinyl acetate, polyvinyl alcohol, synthetic fiber, synthetic rubber, synthetic resin and organic solvents. [0003] In the calcium carbide furnace, the high-temperature heat energy generated by the short-circuit arc between the three-phase electrodes is used to melt quicklime, coke and other raw...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B32/942
CPCC01B32/942
Inventor 赵黎明王中杰赵知远
Owner 赵黎明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products