Imitated Hetian jade ceramic tile and preparation method thereof
A ceramic tile and basic technology, which is applied in the field of imitation Hetian jade tiles and its preparation, can solve problems such as poor density, poor whiteness, and pollution of colored spots
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0037] Carrying out the first pretreatment on the preparation raw materials of the basic high-white material to obtain the prefabricated basic high-white material;
[0038] performing a second pretreatment on the preparation raw materials of the permeable material to obtain a prefabricated permeable material;
[0039] adding the prefabricated permeable material to the prefabricated basic high-whitening material, and mixing to obtain a mixture;
[0040] Adding water to the mixture, undergoing the first ball milling treatment, standing still, and then continuing the second ball milling treatment to obtain the slurry;
[0041] After the slurry is subjected to impurity removal treatment, iron removal treatment, homogenization treatment, spray granulation treatment and stale treatment, it is pressed and formed to obtain bricks;
[0042] The brick adobe is dried, then fired, and cooled to obtain imitation Hetian jade tiles.
[0043] In one embodiment, the first pretreatment is: af...
Embodiment 1-3
[0060] The mass percent of base high white material and permeable material is as shown in table 1 in embodiment 1-3;
[0061] A method for preparing imitation Hetian jade tiles, comprising the following steps:
[0062] Mix 8 parts of white ball clay, 15 parts of white corundum, 5 parts of white stone powder, 9 parts of white kaolin, and 7 parts of calcined talc powder, and stir at a speed of 1500 r / min for 15 minutes to obtain a prefabricated basic high white material;
[0063] After mixing 8 parts of white ball clay, 7 parts of bentonite, 6 parts of wollastonite, 7 parts of quartz sand and 15 parts of potassium feldspar under the condition of 1500r / min, continue to add 3 parts of albite and 1 part of diopside, Continue mixing for 15 minutes under the condition of 3000r / min to obtain prefabricated permeable material;
[0064] adding the prefabricated permeable material to the prefabricated basic high-whitening material, and mixing to obtain a mixture;
[0065] Add water to t...
Embodiment 4-5
[0069] The difference from Example 3 is only that the raw materials and added content of the basic high white material and the permeable material are different, as shown in Table 2 for details.
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com