Preparation method of high-temperature-resistant flame-retardant cabinet panel

A flame-retardant, high-temperature-resistant technology, which is applied in the field of high-temperature-resistant flame-retardant cabinet panel preparation, can solve the problems of cabinet panel damage, high temperature resistance, and limited flame-retardant effect

Pending Publication Date: 2022-06-24
南通佳饰集成家居有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a method for preparing high temperature resistant and flame retardant cabinet panels to solve the problem that the existing cabinet panels have very limited high temperature resistance and flame retardant effects due to the lack of flame retardant components in the existing cabinet panels prone to damage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A method for preparing a high temperature resistant and flame retardant cabinet panel, comprising a board core layer, a board surface layer and an adhesive, and the components are as follows:

[0049] The board core layer includes the following raw materials in parts by weight:

[0050] 60 pieces of wood base

[0051] 20 parts of flame retardant

[0052] Stabilizer 10 parts

[0053] 1 part of cationic crosslinking agent

[0054] 1 part lubricant

[0055] 3 parts of stearic acid;

[0056] The board surface layer is PVC layer;

[0057] The adhesive includes the following raw materials in parts by weight:

[0058] 70 parts of resin

[0059] 10 parts hardener

[0060] 4 parts of coupling agent

[0061] 5 parts accelerator

[0062] 2 parts of plasticizer;

[0063] The wood base material is pine wood powder; the cationic cross-linking agent is Ti4+; the resin is epoxy resin; and the plasticizer is phthalate.

[0064] The temperature of the extrusion barrel of the ...

Embodiment 2

[0066] A method for preparing a high temperature resistant and flame retardant cabinet panel, comprising a board core layer, a board surface layer and an adhesive, and the components are as follows:

[0067] The board core layer includes the following raw materials in parts by weight:

[0068] 70 pieces of wood base

[0069] 30 parts of flame retardant

[0070] Stabilizer 13 parts

[0071] 3 parts of cationic crosslinking agent

[0072] 2 parts lubricant

[0073] 4 parts of stearic acid;

[0074] The panel laminate is PVDF layer;

[0075] The adhesive includes the following raw materials in parts by weight:

[0076] 90 parts of resin

[0077] 15 parts of curing agent

[0078] 6 parts of coupling agent

[0079] Accelerator 7 servings

[0080] 5 parts of plasticizer;

[0081] The wood base material is fir powder; the cationic cross-linking agent is RN3+; the resin is bisphenol A epoxy resin; and the plasticizer is phosphoric acid ester.

[0082] The temperature of th...

Embodiment 3

[0084] A method for preparing a high temperature resistant and flame retardant cabinet panel, comprising a board core layer, a board surface layer and an adhesive, and the components are as follows:

[0085]The board core layer includes the following raw materials in parts by weight:

[0086] 80 pieces of wood base

[0087] 40 parts of flame retardant

[0088] Stabilizer 15 parts

[0089] 5 parts of cationic crosslinking agent

[0090] 3 parts lubricant

[0091] 5 parts of stearic acid;

[0092] The board surface layer is PTFE layer;

[0093] The adhesive includes the following raw materials in parts by weight:

[0094] 110 parts of resin

[0095] 20 parts of curing agent

[0096] 7 parts of coupling agent

[0097] 10 boosters

[0098] 8 parts of plasticizer;

[0099] The wood base material is red beech powder; the cationic crosslinking agent is Al3+; the resin is a terpene resin; and the plasticizer is an alkyl sulfonate.

[0100] The temperature of the extrusion ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a high-temperature-resistant flame-retardant cupboard panel, and belongs to the technical field of cupboard panel preparation, and the preparation method comprises the following steps: (1) performing hot mixing, drying and cooling on raw materials of a plate core layer, and performing high-temperature extrusion forming through an extrusion device to prepare the plate core layer; and (2) uniformly mixing the raw materials of an adhesive, coating the mixture on the two surfaces of the plate core layer in the step (1), then laminating the plate surface layer on the surface of the plate core layer, and carrying out lamination treatment to obtain the composite panel. The preparation process is simple, the operation is simple and convenient, the stability is good, the processing is easy, the material can be used for large-scale production, the adopted raw materials contain the flame retardant, the high-temperature-resistant and flame-retardant effects are very good, and the long-time use of the material in kitchens is ensured.

Description

technical field [0001] The invention relates to the technical field of cabinet panel preparation, in particular to a preparation method of a high temperature resistant flame retardant cabinet panel. Background technique [0002] The cabinet door refers to the door above the cabinet. As the saying goes, "poor is better than the hall, richer than the kitchen", and people pay more attention to the cabinet as the "finishing touch" of kitchen decoration. [0003] As a kitchen utensil, the cabinet panel needs to have good high temperature resistance and flame retardant function, and the existing cabinet panel has no flame retardant components, so that its high temperature resistance and flame retardant effect are very limited. It is easy to be damaged, which affects its use effect. SUMMARY OF THE INVENTION [0004] The object of the present invention is to provide a method for preparing a high temperature resistant flame retardant cabinet panel, so as to solve the problem that ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B21/02B32B21/08B32B27/30B32B27/32B32B7/12B27N3/10B27N3/08B27D1/04B27D1/08C09J163/00C09J145/00C09J11/06B29D7/01
CPCB32B21/02B32B21/08B32B27/304B32B27/322B32B7/12B27N3/10B27N3/08B27D1/04B27D1/08C09J163/00C09J11/06C09J145/00B29D7/01B32B2307/3065B32B2307/306B32B2479/00C08K5/12C08K5/521C08K5/42
Inventor 顾雪标张陈成武敬芝
Owner 南通佳饰集成家居有限公司