Organic polymeter as electromagnetic shielding material and its prepn process
An electromagnetic shielding material, polymer technology, applied in the direction of magnetic/electric field shielding, electrical components, etc., can solve the problems of insufficient conductivity, poor processability, difficult adjustment of shielding effectiveness, etc., and achieve good vibration resistance and impact resistance , stable electrical and chemical properties, and improved electromagnetic shielding performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0024] Add 20 g of meta-ferrocenyl aniline to a three-necked flask containing 100 mL of hydrochloric acid, slowly drop an equimolar amount of ammonium persulfate hydrochloric acid solution, pass nitrogen protection, and react at room temperature for 12 hours to obtain a blue-black solid. Filter, wash with hydrochloric acid, distilled water and absolute ethanol successively, and vacuum dry for 12 hours to obtain 18.5 g of target product. Using tetrahydrofuran as the solvent, the number average molecular weight n (degree of polymerization) is 180 when tested by gel chromatography.
[0025] Mix 4g of the organic polymer electromagnetic shielding material with dual electrical and magnetic properties prepared in the above-mentioned embodiment with 3g of paraffin wax. After the paraffin is melted, a sample of 20.1mm, 10.2mm wide and 2.91mm thick is pressed with a mold. Use the four-probe method to test its conductivity at 10 -6 ~10S / cm; with HP4291B impedance analyzer, in the test range...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap