Normal temperature fast filming fluid for aluminium alloy surface and its usage

A technology of aluminum alloy surface and film-forming liquid, which is applied in the field of metal surface chemical conversion liquid that does not contain hexavalent chromium, can solve problems such as difficulty in obtaining a uniform color protective film, inability to realize industrial continuous production, and low concentration of dissolved titanium ions , to achieve the effect of saving industrial production time and energy, reducing costs and reducing production costs

Inactive Publication Date: 2007-08-22
XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
View PDF1 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] For the "chromium-free conversion coating" announced by U.S. Patent 6,638,369, its treatment solution has the advantage of not containing hexavalent chromium, and the fluoride in the same range as the existing hexavalent chromium conversion process has been added to the treatment solution, but due to The sodium titanate or potassium titanate used in this process has extremely low solubility in water, so the effective concentration of dissolved titanium ions is low, which cannot guarantee the quality of the film in the continuous production process, cannot meet the requiremen...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0063] Specific Example 1: Clean the surface of aluminum alloy 3A21 with gasoline, then immerse it in a 3% sodium hydroxide solution at a temperature of 30 to 60°C for 3 minutes for degreasing treatment, and then immerse the alloy in a 5% nitric acid solution at room temperature after washing with water 5 minutes, after rinsing with deionized water, then immerse the surface of the aluminum alloy at room temperature to quickly form a film of hexavalent chromium chemical conversion replacement solution. The composition of the chemical conversion liquid is 0.10 g / L of sodium silicate, 0.5 g / L of titanyl sulfate, 0.5 g / L of hydrogen peroxide, 1 g / L of aluminum sulfate, and 5 g / L of sodium fluoride. Sulfuric acid is used to adjust the pH of the conversion liquid to 2-8, and the temperature is 15-20°C. After reacting for 10 minutes, the aluminum alloy is taken out and washed with water to dry. The formed film has passed the 336-hour neutral salt spray test (ASTM B117) test, and the ...

specific Embodiment 2

[0064] Specific embodiment 2: After the aluminum alloy LD2CS is subjected to the same pretreatment as in Example 1, the alloy is immersed in 0.05g / L sodium silicate, 2g / L titanyl sulfate, hydrogen peroxide 0.5g / L, chlorinated In the conversion solution of cerium 2g / L and sodium fluoride 4g / L, sulfuric acid adjusts the pH value of the solution. The reaction conditions are the same as in Example 1. The aluminum alloy LD2CS treated above has formed a layer of white film layer after 336 hours of neutral salt spray (ASTM B117) test and still does not rust. Glue hard.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses one kind of normal temperature fast filming fluid for aluminum alloy surface and its usage. The filming fluid contains silicate, titanate, peroxide, fluoride and trivalent metal salt. When it is used, the filming fluid is controlled to be in the temperature of 1-40 deg.c and pH value of 2-8, and to be contacted with aluminum alloy for 1-10 min. The filming fluid can form film with high anticorrosive performance and excellent adhering performance, and has less environmental pollution, fast filming speed, low production cost and capacity of being used in industrial production.

Description

technical field [0001] The invention relates to a method for surface treatment of aluminum alloys, in particular to a metal surface chemical conversion solution that does not contain hexavalent chromium, which can quickly endow the aluminum alloy surface with superior corrosion resistance and adhesion performance under normal temperature conditions, and the use of the chemical conversion solution A method for treating the surface of an aluminum alloy. Background technique [0002] Chromate chemical transformation (passivation) of metal surface is a traditional processing technology, which has been widely used in functional coating and decorative coating fields for nearly a century due to its excellent anti-corrosion and adhesion properties, such as aerospace , electronics, automobiles, pharmaceuticals, printing, machinery, chemicals, food processing and other manufacturing industries. [0003] In the past, the surface treatment method of aluminum and its alloys was treated ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C22/05C23C22/34C23C22/66C23C22/68C23C22/78
CPCC23C22/34C23C2222/10C23C22/68
Inventor 郭瑞光耿志良杨杰
Owner XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap