Emulsified Metal Cutting Fluid Composition

A metal cutting fluid, emulsified technology, used in the field of metal cutting lubrication, can solve the problems of lubricity, extreme pressure cooling, corrosion resistance life difference, etc., to achieve excellent lubricity, health and harmless, long corrosion resistance. Effect

Inactive Publication Date: 2011-12-07
河北九熙新材料科技有限公司
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing emulsified metalworking fluids have large differences in lubricity, extreme pressure, cooling, corrosion resistance, and service life due to formula and other reasons.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0028] Example 1, the emulsion consists of the following components by weight:

[0029] Base oil or oily agent 70.5%

[0030] Mixed olamines 5%

[0031] Anionic Surfactant 5%

[0032] Nonionic Surfactant 5.4%

[0033] Rust inhibitor 8.6%

[0034] Copper alloy corrosion inhibitor 0.3%

[0035] Bactericidal preservative 4%

[0036] Defoamer 0.2%

[0037] Water1%

[0038] Among them, the base oil or oily agent is naphthenic mineral oil, its 40 ℃ viscosity is 9.5mm 2 / s; mixed alcohol amines are monoethanolamine, diethanolamine, triethanolamine, monoisopropanolamine, diisopropanolamine, 2-amino-2-methyl-1-propanol; anionic surfactants are octanoic acid, isopropanolamine Nonionic acid, oleic acid or oleic acid soap, ricinoleic acid soap, tall oil acid; nonionic surfactants are fatty alcohol polyoxyethylene ethers, such as AEO-3, AEO-7, TX-10, NP-12, Or fatty acid polyoxyethylene ester, such as SPAN80, polyoxyethylene oleate; rust inhibitor is sodium petroleum sulfonate, b...

example 2

[0039] Example 2, the emulsion consists of the following components by weight:

[0040] Base oil or oily agent 79%

[0041] Mixed olamines 3%

[0042] Anionic Surfactant 3.2%

[0043] Nonionic Surfactant 3.5%

[0044] Rust inhibitor 7.6%

[0045] Copper alloy corrosion inhibitor 0.3%

[0046] Bactericidal preservative 3%

[0047] Defoamer 0.2%

[0048] Among them, the base oil or oily agent is paraffin-based mineral oil, and its viscosity at 40°C is 19.4mm 2 / s, other components are the same as example 1.

example 3

[0049] Example 3, the emulsion consists of the following components by weight:

[0050] Base oil or oily agent 84.6%

[0051] Mixed olamines 2%

[0052] Anionic Surfactant 3%

[0053] Nonionic Surfactant 3%

[0054] Rust inhibitor 5%

[0055] Copper alloy corrosion inhibitor 0.3%

[0056] Bactericidal preservative 2%

[0057] Defoamer 0.1%

[0058] Wherein, base oil and oiliness agent are the mixture of naphthenic mineral oil and ester oil, and naphthenic mineral oil is the same as the base oil of example 1, and ester oil is pentaerythritol ester, trimethylol propane ester, methyl palmitate , methyl oleate, isopropyl oleate; Other components are with example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an emulsified metal cutting fluid composition, which consists of base oil or oily agent, mixed alcohol amine, anionic surfactant, nonionic surfactant, antirust agent, copper alloy corrosion inhibitor, bactericidal antiseptic, etc. composition. The invention has strong versatility, is suitable for processing various metals, especially for processing aluminum alloy metals, has excellent lubricity, anti-corrosion effect, low cost, and does not contain toxic and harmful substances such as nitrites and phenols. Harmless to the environment and the health of operators.

Description

technical field [0001] The invention relates to metal cutting lubrication technology, in particular to composition components of emulsified metal cutting fluid. Background technique [0002] Emulsified cutting fluid is a kind of water-based cutting fluid. It is widely used in the metal processing industry because of its low cost and excellent performance. The use of pure oil lubrication, the emulsion has better cooling, prevents the sintering of the tool and the workpiece, a better working environment, no oil mist, and maintains the health of the staff. However, the existing emulsified metalworking fluids have large differences in terms of lubricity, extreme pressure, cooling, corrosion resistance, and service life due to formula and other reasons. Contents of the invention [0003] The purpose of the present invention is to provide an emulsion with better comprehensive performance and improve the service life of the emulsion. [0004] Technical solution of the present i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M169/04C10M101/00C10M133/08C10M129/26C10M135/10C10M133/44C10M133/42C10M135/36C10M137/04C10N40/22
Inventor 王金波于海英甄轶黄学东黄学智
Owner 河北九熙新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com