Biodegradable hard water-resistant water-soluble metalworking liquid

A biodegradable, hard water-resistant technology, applied in lubricating compositions, petroleum industry, additives, etc., can solve problems such as poor biodegradability, difficult disposal of waste liquid, endangering human health, etc., and achieve improved biodegradability, reliability and safety Hygienic performance, the effect of super hard water resistance

Inactive Publication Date: 2012-09-12
QIDONG YUSHIRO CHEMICAL INDUSTRY CO LTD +1
View PDF1 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

First, the biodegradability is poor. After testing, its BOD (biological oxygen demand)/COD (chemical oxygen demand) is generally around 0.2, which makes the waste liquid

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Mix and stir the components of a certain weight percentage to obtain a biodegradable hard water-resistant water-soluble cutting fluid product:

[0023] Cinnamic acid 3%

[0024] Sebacic acid 3%

[0025] Oleic Acid 4%

[0026] Ricinoleic Acid 5%

[0027] Triethanolamine 10%

[0028] Monoisopropanolamine 6%

[0029] Diethylaminoethanol 5%

[0030] Trimethylolpropane 30%

[0031] Neopentyl polyol ester 10%

[0032] Fatty alcohol polyoxyethylene (9) ether 8%

[0033] Alcohol ether carboxylate 3%

[0034] Tolylbenzotriazole 0.5%

[0035] Emulsified silicone oil 0.5%

[0036] Water 12%.

Embodiment 2

[0038] A biodegradable hard water-resistant water-soluble cutting fluid, which is mixed with the following components by weight percentage:

[0039] Organic acid 5-25% (eg 5%, 15%, 25%)

[0040] Organic amine 10-25% (eg 10%, 15%, 25%)

[0041] Corrosion inhibitor 1-5% (eg 1%, 3%, 5%)

[0042] Synthetic lubricant 20-40% (eg 20%, 30%, 40%)

[0043] New surfactant 5-15% (eg 5%, 10%, 15%)

[0044] Water 5-15% (eg 5%, 10%, 15%)

[0045] Defoamer 0.1~0.8% (eg 0.1%, 0.5%, 0.8%).

[0046] The sum of the amounts of the above-mentioned components is 100%.

[0047] Organic acid is C 6 -C 14 Straight-chain dibasic acid, C 8 -C 18 Fatty acids, p-tert-butylbenzoic acid, p-nitrobenzoic acid or sulfamic acid compounds.

[0048] Organic amines are monoethanolamine, diethanolamine, triethanolamine, monoisopropanolamine, diisopropanolamine, triisopropanolamine, morpholine, dicyclohexylamine, N-methylmorpholine, 2-amino 2- Methylpropanol or diethylaminoethanol.

[0049] The corrosion ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses biodegradable hard water-resistant water-soluble metalworking liquid. The biodegradable hard water-resistant water-soluble metalworking liquid consists of organic acid, organic amine, corrosion inhibitor, synthetic lubricant, surfactant, water and defoamer. The biodegradable hard water-resistant water-soluble metalworking liquid is high in biodegradability, hard water resistance, lubricity, rust prevention property and corrosion resistance and long in service life and is friendly to people and environment.

Description

technical field [0001] The invention relates to a biodegradable hard water-resistant water-soluble cutting fluid. Background technique [0002] In order to adapt to the rapid development of my country's mechanical processing industry and better meet the requirements of users, in the past ten years, the water-soluble cutting fluid products used in metal processing produced by domestic manufacturers not only have lubricating performance, anti-rust and anti-corrosion performance, cycle life, etc. The performance index has been significantly improved; and the hard water-resistant water-soluble cutting fluid product developed in combination with national conditions, when used under the condition of 7000mg / l hardness water quality, there is no oil separation or soap separation phenomenon, but due to various reasons such as technology, technology, and understanding At present, there are still two major drawbacks in the hard water-resistant water-soluble cutting fluid products produce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M173/02C10M167/00C10N40/22C10N30/12C10N30/18C10N20/00
Inventor 林丽静阿部聪常建忠俞威茅晓华
Owner QIDONG YUSHIRO CHEMICAL INDUSTRY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap