Multiple-ammoniation polyacrylonitrile-based carbon fiber spinning solution and preparation method thereof

Abstract

The invention discloses a multiple-ammoniation polyacrylonitrile-based carbon fiber spinning solution and a preparation method of the multiple-ammoniation polyacrylonitrile-based carbon fiber spinning solution. The preparation method comprises the steps of combining acrylonitrile, methyl acrylate, 2-acrylamide-2-methylpro panesulfonic acid and itaconic acid to be a polymer monomer, respectively and sufficiently dissolving the weighed solid monomer (itaconic acid) and an initiator (azodiisobutyronitrile) into a dimethyl sulfoxide solution; conducting ammoniation on the dimethyl sulfoxide solution of the itaconic acid by ammonia water; and sequentially adding all the materials into a polymerizing pot, adding the initiator (azodiisobutyronitrile) to conduct batch polymerization reaction, gathering, defoaming and filtering to obtain the multiple-ammoniation polyacrylonitrile-based carbon fiber spinning solution. According to the multiple-ammoniation polyacrylonitrile-based carbon fiber spinning solution and the preparation method, the comonomer structure of a multiple-copolymerization system is changed by the ammonia water, and dimethyl sulfoxide is taken as a solvent for homogeneous solution polymerization to prepare the polyacrylonitrile-based carbon fiber spinning solution, so that the hydrophily of the spinning solution is improved, and further, the high-performance fiber with high structure compacting degree, good mechanical property and high bonding strength is obtained.

Description

technical field [0001] The invention relates to a preparation method of a polyacrylonitrile-based carbon fiber spinning solution, in particular to a polyacrylonitrile-based carbon fiber spinning solution and a preparation method thereof. Background technique [0002] Carbon fiber is a high-strength special fiber with a carbon content greater than 90%. Due to its high strength, high modulus, high temperature resistance, fatigue resistance, electrical conductivity, and thermal conductivity, it is widely used in cutting-edge fields such as aerospace, national defense, and national economy. Many fields of construction. The main raw material of high-performance carbon fiber is polyacrylonitrile-based precursors. Polymerization is the first step in the preparation of precursors. High-quality polymer solution is the prerequisite for the preparation of high-performance precursors. Adjust the characteristics of polymerized comonomers to improve the spinning solution. The hydrophilic...

AI Technical Summary

Problems solved by technology

Methyl acrylate can reduce the cohesive energy between polyacrylonitrile macromolecules, improve the spinnability of spinning solution, and at the same time, due to the volume effect of ester group, it can enhance the oxygen permeability during the pre-oxidation process, slow down or eliminate the skin-core structure formation; itaconic acid can reduce the activation energy of the reaction, promote cyclization and crosslinking, ease the pre-oxidation exothermic reaction, and prepare homogeneous pre-oxidized silk, but the hydrophilicity of itaconic acid is not very good. Therefore, in order to To improve the hydrophilicity of spinning solution, itaconic acid needs to be modified

[0004] In the patents No. 200510016572.X and CN200710056082.1, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences proposed two high-hydrophilic spinning solutions and preparation methods for high-performance polyacrylonitrile-based carbon fibers. In the polymerization process, itaconic acid and β-itaconic acid amide were used as comonomers or vinylimidazolium salts, itaconic acid, acrylic acid and methacrylic acid were used as comonom

Images