Method for preparing soluble kelp cellulose

A cellulose and soluble technology, which is applied in the field of preparation of soluble kelp cellulose, can solve the problems of uneven molecular weight of kelp cellulose, affecting the quality of kelp cellulose, and low kelp cellulose content, so as to reduce production energy consumption and be operable properties, uniform molecular weight, and high cellulose content

Active Publication Date: 2012-11-21
QINGDAO HENGSHENG BIOLOGICAL PHARMA TECH DEV
View PDF4 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, although there are known extraction techniques for extracting kelp cellulose from kelp and kelp residue, cellulase or protease is generally used for high-temperature enzymolysis at a temperature above 50°C. Molecules will also b

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing soluble kelp cellulose
  • Method for preparing soluble kelp cellulose

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0032] Example 1

[0033] Extraction of kelp dietary fiber: add calcium chloride solution to the turbid glue solution of kelp residue until all the kelp residue is flocculated, collect the flocs by standing, add distilled water to the flocs, add hydrochloric acid solution to decalcify, and then collect by centrifugation, Repeat the above decalcification step once, add an appropriate amount of sodium carbonate solution to the filtrate to neutrality, collect the filtrate, add sodium hypochlorite with a mass concentration of 10% in the solution to bleach for 24 hours, suction filtration, wash with water, and then rinse with 75wt% ethanol. Suction filtration, vacuum freeze-drying at 50°C, and pulverization to obtain kelp dietary fiber.

[0034] Preparation of soluble kelp cellulose: add 2wt% NaOH solution to the kelp dietary fiber obtained in step (1) at a mass ratio of 1:20, soak at room temperature for 48h, wash with water until neutral, and add water at a ratio of 1:20 , steam...

Example Embodiment

[0035] Example 2

[0036]Extraction of kelp dietary fiber: add 8wt% calcium chloride solution to the turbid glue solution of kelp slag until all the kelp slag is flocculated, let stand for 1 hour, collect the flocs, and add distilled water to the flocs at a weight ratio of 1:8 , and add 0.1mol / L HCl, heat and stir at 40°C for 0.6h, then centrifuge for collection, add an appropriate amount of sodium carbonate solution to the filtrate to neutralize, collect the filtrate, add 8% sodium hypochlorite in the solution to bleach 24 hour, suction filtration, washing with water, then rinse with 70wt% ethanol, suction filtration, vacuum drying at 45°C, and pulverization to obtain kelp dietary fiber.

[0037] Preparation of soluble kelp cellulose: add the kelp dietary fiber obtained in step (1) into a 1wt% NaOH solution at a mass ratio of 1:15, soak it at room temperature for more than 48 hours, wash it to neutrality, and add water at a ratio of 1:20 , steam explosion at 121°C and 0.14MP...

Example Embodiment

[0038] Example 3

[0039] Extraction of kelp dietary fiber: add 12wt% calcium chloride solution to the turbid glue solution of kelp slag until all the kelp slag is flocculated, let stand for 0.5h, collect the floc, and add to the floc at a weight ratio of 1:10 Distilled water, add 0.2mol / L HCl, heat and stir at 50°C for 0.5h, then filter and collect, repeat the above decalcification step once, add an appropriate amount of sodium carbonate solution to the filtrate to neutralize, collect the filtrate, add the mass of the solution Bleaching with sodium hypochlorite with a concentration of 12% for 24 hours, suction filtration, washing with water, then washing with 80wt% ethanol, suction filtration, vacuum drying at 55°C, and pulverization to obtain kelp dietary fiber.

[0040] Preparation of soluble kelp cellulose: add 3wt% NaOH solution to the kelp dietary fiber obtained in step (1) at a mass ratio of 1:30, soak at room temperature for 48 hours, wash with water until neutral, and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Expansion forceaaaaaaaaaa
Expansion forceaaaaaaaaaa
Expansion forceaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing soluble kelp cellulose. The method includes the steps: firstly, preparing kelp dietary fibers from kelp residues by means of flocculation, decalcifying, bleaching, washing and the like; secondly, performing steam explosion to obtain insoluble kelp cellulose, then adding low-temperature cellulase into the insoluble kelp cellulose, and performing enzymolysis in water bath at the temperature of 25 DEG C-35 DEG C to obtain the soluble kelp cellulose with the content of 90.14+/-1.09wt% and the yield of 50-60%. When the soluble kelp cellulose is prepared, the low-temperature cellulase is used, enzymolysis is performed at the normal temperature, enzymolysis conditions are moderate, only macromolecules are sensitive to the cellulose, and macromolecules in kelp are easily decomposed while micromolecules are relatively stable and not easily further decomposed, so that the obtained soluble kelp cellulose is uniform in molecular weight and high in yield, cellulose content, water-holding capacity and expansibility. Moreover, the enzymolysis temperature is low, so that production energy consumption and operability are reduced.

Description

technical field [0001] The invention relates to the technical field of reuse of kelp industrial waste, in particular to the preparation of soluble kelp cellulose. Background technique [0002] Kelp is a large-scale brown algae that is widely distributed along the coast of my country, but it is mainly produced in the coasts of Shandong and Liaoning provinces in my country. The output and scale of kelp planting in my country ranks first in the world. In 2009, the output of dry kelp in my country reached 6.0×10P 5P t, accounting for more than 50% of the world's total output. Kelp is rich in alginate, cellulose, hemicellulose, vitamins and minerals, etc. In addition to being used for direct consumption, kelp is one of the main raw materials for the brown algae industry. In my country, kelp processing has formed an industrial system with alginate, mannitol, and iodine as the main products. In recent years, due to fierce market competition, low added value of products, high wat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21C5/00A23L1/308
Inventor 缪锦来李友海李健
Owner QINGDAO HENGSHENG BIOLOGICAL PHARMA TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap