Method for preparing ultraviolet light polymerization environment-friendly antibacterial acrylic ester medical pressure sensitive adhesive product

An acrylate, ultraviolet light technology, applied in the direction of adhesives, film/sheet adhesives, non-polymer organic compound adhesives, etc. Effects of infection, good biocompatibility, good adhesion properties

Active Publication Date: 2013-01-30
ZHENDE MEDICAL CO LTD
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this pressure-sensitive adhesive can only be used to manufacture industrial pressure-sensitive adhesive products, and cannot be used to prepare medical pressure-sensitive adhesive products, especially broad-spectrum antibacterial medical pressure-sensitive adhesive products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Carry out according to following formula and preparation technology:

[0025] a. Preparation of acrylate oligomer

[0026] Mix 86 parts of soft monomer 2-ethylhexyl acrylate (parts by weight, the same below), 10 parts of hard monomer methyl methacrylate, 1 part of functional monomer methacrylic acid and 3 parts of hydroxyethyl acrylate to form 100 parts of internal acrylate monomer mixture, take 30 parts of the acrylate monomer mixture and add it to the reaction container, then add 10 parts of humectant ethylene glycol, and stir under nitrogen protection and heat to 70 ° C, add dropwise with 10 parts 1.0 part of benzoyl peroxide solution dissolved in the above-mentioned monomer mixture, react for 0.5 hours and then add dropwise the remaining above-mentioned acrylate monomer mixture, drop in 1 hour; react for 2.5 hours after dropping to obtain acrylate oligomerization body;

[0027] b, 2 parts of protective colloid sodium polyacrylate, 3 parts of photoinitiator benzoin...

Embodiment 2

[0030] Carry out according to following formula and preparation technology:

[0031] a. Preparation of acrylate oligomer

[0032] Mix 76 parts of soft monomer 2-ethylhexyl acrylate and 12 parts of butyl acrylate, 8 parts of hard monomer methyl methacrylate, 1 part of functional monomer acrylic acid and 3 parts of hydroxyethyl acrylate to form 100 parts of acrylic acid ester monomer mixture, take 30 parts of the acrylate monomer mixture and add it to the reaction container, then add 8 parts of humectant propylene glycol, protect it with nitrogen and heat it to 70 ° C, dropwise add 1.0 parts dissolved in 10 parts of the above monomer mixture part of benzoyl peroxide solution, add dropwise the remaining above-mentioned acrylate monomer mixture after reacting for 0.5 hours, finish dropping in 1 hour, and then react for 2.5 hours after dropping to obtain acrylate oligomer;

[0033] b, 1 part of protective colloid Span 60, 3 parts of photoinitiator benzoin methyl ether, 5 parts of ...

Embodiment 3

[0036] Carry out according to following formula and preparation technology:

[0037] a. Preparation of acrylate oligomer

[0038] Mix 86 parts of soft monomer 2-ethylhexyl acrylate (parts by weight, the same below), 10 parts of hard monomer methyl methacrylate, 1 part of functional monomer methacrylic acid and 3 parts of hydroxypropyl acrylate to form 100 parts of acrylate monomer mixture, take 25 parts of the internal acrylate monomer mixture and add it to the reaction container, then add 6 parts of humectant ethylene glycol, protect it with nitrogen and heat it to 70°C, add 10 parts dropwise 1.0 parts of benzoyl peroxide solution dissolved in the above monomer mixture, react for 0.5 hours, then add dropwise the remaining above acrylate monomer mixture, drop in 1 hour, and then react for 2.5 hours to obtain acrylate oligomer ;

[0039] b, 2 parts of protective colloid Tween 60, 4 parts of photoinitiator benzophenone, 6 parts of broad-spectrum antibacterial drug sulfadiazine...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing an ultraviolet light polymerization environment-friendly antibacterial acrylic ester medical pressure sensitive adhesive product. The method comprises the following steps of: (a), preparing an acrylic ester oligomer; (b), uniformly mixing protective colloid, a broad-spectrum antibacterial medicine, a polymer elastomer and the acrylic ester oligomer; and (c), dissolving the mixture mixed in the step (b) in a polymerizable monomer to obtain pressure sensitive adhesive cement capable of coating at normal temperature, coating the pressure sensitive adhesive cement on a base material, and performing ultraviolet light polymerization to obtain the medical pressure sensitive adhesive product. The medical pressure sensitive adhesive product is environment-friendly and antibacterial, has good adhesion property on skins, and can well absorb moisture and release sweat; when the pressure sensitive adhesive product is pasted and removed, a user does not feel pain, and residual adhesives are avoided; and the medical pressure sensitive adhesive product has good biocompatibility, does not irritate the skins, and can effectively prevent infection of wounds or surgical incision sites.

Description

Technical field: [0001] The invention relates to the technical field of production of medical pressure-sensitive adhesives and products thereof, in particular to a method for preparing ultraviolet-cured environmental-friendly antibacterial acrylate medical pressure-sensitive adhesive products. Background technique: [0002] Medical pressure-sensitive adhesives are widely used in the manufacture of pressure-sensitive adhesive products in the medical and health field and some medical composite materials. The application of ultraviolet (UV) light-curing acrylate pressure-sensitive adhesives in the medical and health field is a new trend and has good advantages. UV light-curing medical acrylate pressure-sensitive adhesive does not contain solvents and will not cause environmental pollution. It is an environmentally friendly pressure-sensitive adhesive; medical adhesive products coated with it have better adhesion to the skin. It can better absorb moisture and perspiration. It w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/02C09J7/04C09J4/02C09J4/06C09J11/06C09J11/08
Inventor 刘成刚胡修元杨玉昆
Owner ZHENDE MEDICAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com