Refining and extracting method of dextran by membrane separation

A purification method and plasma replacement technology, which is applied in the field of membrane separation, can solve problems such as narrow and high-purity products, inability to obtain molecular weight distribution, and difficulty in filtration, so as to achieve high economic and social benefits, safe and reliable product efficacy, and improve product quality Effect

Active Publication Date: 2014-04-23
JIANGSU JIUWU HITECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the preparation process, there are often characteristics such as difficult filtration, easy bacterial contamination, heavy opalescence, etc., and high-purity products with narrow molecular weight distribution cannot be obtained.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Take 30L of plasma substitute (hydroxyethyl starch) crude product solution with an average molecular weight of 120kDa, a purity of 70.3%, and a molecular weight range of 500-200,000Da, and use an alumina microfiltration membrane with an average pore size of 100nm for pretreatment and filtration. The operating pressure is 0.8 MPa , the membrane surface flow rate is 5 m / s, and the large particles and bacteria in the plasma substitute (hydroxyethyl starch) solution are removed.

[0023] Next, the obtained permeate is sent to a zirconia ultrafiltration membrane with an average pore size of 20 nm for primary filtration to remove high molecular weight components. The operating pressure is 0.5 MPa and the membrane surface velocity is 10 m / s.

[0024] The obtained permeate enters the titanium oxide ultrafiltration membrane with an average pore size of 2nm, the operating pressure is 0.5MPa, the membrane surface flow rate is 5 m / s, and the temperature is 40°C to remove small molec...

Embodiment 2

[0027] Take 30L of plasma substitute (hydroxyethyl starch) crude product solution with an average molecular weight of 200kDa, a purity of 72.4%, and a molecular weight range of 10-300kDa, and use an aluminum oxide microfiltration membrane with an average pore size of 500 nm for pretreatment and filtration. The operating pressure is 0.5 MPa, membrane surface flow velocity 10 m / s, to remove large particles and bacteria in the plasma substitute (hydroxyethyl starch) solution.

[0028] Next, the obtained permeate was sent to a zirconia ultrafiltration membrane with an average pore size of 50 nm for primary filtration to remove high molecular weight components. The operating pressure was 0.8 MPa and the membrane surface velocity was 5 m / s.

[0029] The obtained permeate enters the titanium oxide ultrafiltration membrane with an average pore size of 10nm, the operating pressure is 0.8 MPa, the membrane surface flow rate is 0.07 m / s, and the temperature is 20°C to remove small molecul...

Embodiment 3

[0032] Take 30 L of the crude plasma substitute solution (hydroxyethyl starch) with an average molecular weight of 150 kDa and a molecular weight range of 50-300 kDa, and use a porous titanium microfiltration membrane with an average pore diameter of 800 nm for pretreatment and filtration. The operating pressure is 0.1 MPa. The flow rate is 0.07 m / s to remove large particles and bacteria in the plasma substitute (hydroxyethyl starch) solution.

[0033] Next, the obtained permeate was sent to a zirconia ultrafiltration membrane with an average pore size of 100 nm for primary filtration to remove high molecular weight components. The operating pressure was 0.1 MPa and the membrane surface velocity was 0.07 m / s.

[0034] The obtained permeate enters the zirconia ultrafiltration membrane with an average pore size of 20nm, the operating pressure is 0.8 MPa, the membrane surface flow rate is 0.07 m / s, and the temperature is 80 ℃ to remove small molecular components in the feed liquid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of membrane separation, and relates to a refining and extracting filtering preparation process of dextran. The method comprises the steps of: first, filtering a crude product liquor of dextran by a micro-filtration membrane; second, filtering the filtrate in the first step by a first ultrafiltration membrane; and third, filtering the filtrate in the second step by a second ultrafiltration membrane, wherein trapped fluid is the refined dextran, the mean pore size of the first ultrafiltration membrane is 20-100nm, and the mean pore size of the second ultrafiltration membrane is 2-20mn or the molecular weight cut-off is 3-100kDa. According to the invention, the membrane separation technology and the pharmaceutical process are combined to filter and refine a dextran raw material, so that a dextran product with narrower distribution of molecular weight is high in purity, is safe and reliable in curative effect and has high economic and beneficial benefits, and the product quality is improved.

Description

technical field [0001] The invention belongs to the technical field of membrane separation, and relates to a filtration preparation process for refining and purifying plasma substitutes, in particular to a process for refining plasma substitutes using inorganic membranes. Background technique [0002] Plasma substitute, referred to as plasma substitute, is a colloidal solution with a molecular weight close to that of plasma albumin. After infusion into blood vessels, it relies on its colloid osmotic pressure to replace and expand blood volume. It can be used in the treatment of hemorrhagic shock. Save a portion of whole blood. It is an important blood volume expander that is often used in the clinical treatment of diseases. It can increase blood volume and temporarily maintain blood pressure. The circulatory and microcirculatory disturbances caused by the capacity state reduce the blood flow and oxygen supply of various organs, so as to maintain the normal operation of body...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K45/00A61P7/08B01D61/58
Inventor 范苏彭文博熊福军秦泗光寇琴
Owner JIANGSU JIUWU HITECH