Polyacrylate adhesive for calcium plastic corrugated paper and preparation method thereof

A polyacrylate and acrylate technology, applied in the direction of ester copolymer adhesives, adhesive types, etc., can solve the problems that the adhesiveness and heat resistance of the adhesive cannot fully meet the requirements of use, and improve the adhesive strength. and tensile strength, high solids content, and lower production costs

Inactive Publication Date: 2013-04-10
NINGBO INST OF TECH ZHEJIANG UNIV ZHEJIANG
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the adhesion and heat resistance of acrylate emu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A polyacrylate adhesive for calcium-plastic corrugated paper, comprising the following components in percentage by weight:

[0030] N-methylolacrylamide 3g

[0031] Soft monomer: butyl acrylate 60g

[0032] Hard monomer: methyl methacrylate 16.5g

[0033] Emulsifier: OP-10 0.9g

[0034] Sodium Lauryl Sulfate 0.4g

[0035] Ammonium persulfate 3.75g

[0036] Recycled PVB: 10g

[0037] 95% ethanol: 20g

[0038] Ethyl acetate: 20g

[0039] Distilled water: 100g

[0040] The preparation method of the above-mentioned polyacrylate adhesive for calcium-plastic corrugated paper comprises the following steps:

[0041] (1) Add all the emulsifier and 1 / 2 of N-methylolacrylamide, soft monomer and hard monomer into a four-necked flask with a stirrer, reflux condenser and thermometer, stir for 30 minutes at a stirring speed of 600 ~800r / min;

[0042] (2) Put the four-neck flask in a water bath and raise the temperature to 70°C, open the reflux condenser, add 1 / 3 ...

Embodiment 2

[0048] A polyacrylate adhesive for calcium-plastic corrugated paper, comprising the following components in percentage by weight:

[0049]N-methylolacrylamide 4g

[0050] Soft monomer: ethyl acrylate 70g

[0051] Hard monomer: methacrylic acid 18g

[0052] Emulsifier: OP-10 0.8g

[0053] Sodium dodecylbenzenesulfonate 0.6g

[0054] Ammonium persulfate 3.5g

[0055] Recycled PVB: 8g

[0056] 95% ethanol: 16g

[0057] Ethyl acetate: 16g

[0058] Distilled water: 100g

[0059] The preparation method of the above-mentioned polyacrylate adhesive for calcium-plastic corrugated paper is the same as in Example 1, and the prepared polyacrylate adhesive for calcium-plastic corrugated paper is milky white, with a pH value of 6~7, a solid content of 50%, and a peel strength of 681N. / m, the tensile strength is 195.6N / 25mm, which fully meets the corrugated board adhesive index.

Embodiment 3

[0061] A polyacrylate adhesive for calcium-plastic corrugated paper, comprising the following components in percentage by weight:

[0062] N-methylolacrylamide 3.5g

[0063] Soft Monomer: Ethyl Acrylate 25g

[0064] Butyl acrylate 35g

[0065] Hard monomer: methyl acrylate 17g

[0066] Emulsifier: sodium vinyl sulfonate 0.8g

[0067] Sodium dodecylbenzenesulfonate 0.5g

[0068] Ammonium persulfate 3.6g

[0069] Recycled PVB: 14g

[0070] 95% ethanol: 28g

[0071] Ethyl acetate: 28g

[0072] Distilled water: 120g

[0073] The preparation method of the above-mentioned polyacrylate adhesive for calcium-plastic corrugated paper is the same as in Example 1, and the prepared polyacrylate adhesive for calcium-plastic corrugated paper is milky white, with a pH value of 6~7, a solid content of 39.6%, and a peel strength of 692N / m, the tensile strength is 240.7N / 25mm, which fully meets the corrugated board adhesive index.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Peel strengthaaaaaaaaaa
Peel strengthaaaaaaaaaa
Peel strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a polyacrylate adhesive for calcium plastic corrugated paper and a preparation method thereof. The adhesive comprises 3-5% of N-hydroxymethyl acrylamide, 20-30% of soft monomer, 5-8% of hard monomer, 0.45-0.7% of emulsifier, 1.5-2% of ammonium persulfate, 1-6% of PVB (polyvinyl butyral), 7-10% of 95% ethanol, 7-10% of ethyl acetate and the balance of water. The preparation method comprises the following steps: adding the emulsifier, 1/2 of N-hydroxymethyl acrylamide, 1/2 of soft monomer and 1/2 of hard monomer into a four-neck flask; adding 1/3 of ammonium persulfate and water; dropwisely adding the rest of N-hydroxymethyl acrylamide, soft monomer, hard monomer and ammonium persulfate, keeping at the temperature of 85 DEG C for 2 hours, and cooling to 50 DEG C; regulating the pH value to 6-7 to obtain an acrylate adhesive; and adding the PVB into the 95% ethanol to obtain a white transparent colloid, adding the ethyl acetate, adding the acrylate adhesive, and heating while stirring, thereby obtaining the finished product. The adhesive has the advantages of high adhesive strength, high tensile strength and low cost.

Description

technical field [0001] The invention relates to the technical field of adhesives and preparation thereof, in particular to a polyacrylate adhesive for calcium-plastic corrugated paper and a preparation method thereof. Background technique [0002] Calcium plastic material is a new material developed by filling and modifying resin with fillers. The resins it uses are mainly thermoplastic polyolefin resins such as high-density polyethylene, low-density polyethylene or polypropylene, and the raw materials used are mainly inorganic calcium salts such as calcium carbonate, calcium sulfate or calcium sulfite, so it is called "calcium plastic". Material". Because calcium-plastic materials have the advantages of being moisture-proof and not afraid of water, good toughness and not easy to break, and are environmentally friendly and pollution-free, they can be recycled and reused. In the packaging industry, calcium-plastic materials have begun to be widely used. Calcium-plastic corr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J133/08C08F220/18C08F220/14C08F220/06C08F2/26C08F2/30
Inventor 高德张萍赵满
Owner NINGBO INST OF TECH ZHEJIANG UNIV ZHEJIANG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap