PC/ABS alloy modified engineering plastic dedicated for laptop casings and production method thereof

A technology for notebook computers and engineering plastics, which is applied in the field of PC/ABS alloy modified engineering plastics and polymer plastic materials for notebook computer casings, and can solve the problems of unfavorable recycling of metal alloy casings, high production costs, and high prices.

Inactive Publication Date: 2014-03-05
东莞市卡帝德塑化科技有限公司
View PDF6 Cites 45 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

2. The metal alloy casing can be divided into aluminum-magnesium alloy materials and titanium alloy materials according to the selected alloys. However, aluminum-magnesium alloys are not very strong and wear-resistant. After a long time of use, the original silvery white will wear off. If you accidentally scratch it, the scratches will be very conspicuous, and the metal alloy shell is not conducive to recycling and is not environmentally friendly
3. The carbon fiber alloy shell is usually expensive and the production cost is high, and the forming process of the carbon fiber alloy shell is complicated and the plasticity is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0074] A special PC / ABS alloy modified engineering plastic for notebook computer shells, containing the following components by weight percentage:

[0075] Polycarbonate 42%; Compatibilizer 4%;

[0076] Acrylonitrile-butadiene-styrene 22.2%; Mineral filler 15%;

[0077] Antioxidant 0.3%; Halogen-free flame retardant 12%;

[0078] Dispersed lubricant 0.5%; Toughener 4%.

[0079] Among them, the polycarbonate is a powder polycarbonate with a melt index of 9g / 10min; the compatibilizer is a mixture of maleic anhydride grafted polyolefin elastomer and ethylene methyl acrylate copolymer in any proportion; the mineral filler is nano-scale carbonic acid A mixture of calcium, ultrafine mica powder, ultrafine precipitated barium sulfate, glass fiber, and carbon fiber in any proportion; the antioxidant is a mixture of phosphite antioxidants and amine antioxidants in any proportion; halogen-free flame retardant It is a mixture of oligomeric aryl phosphate, triphenyl phosphate a...

Embodiment 2

[0088] A special PC / ABS alloy modified engineering plastic for notebook computer shells, containing the following components by weight percentage:

[0089] Polycarbonate 54.4%; Compatibilizer 2%;

[0090] Acrylonitrile-butadiene-styrene 30%; Mineral filler 5%;

[0091] Antioxidant 0.6%; Halogen-free flame retardant 3%;

[0092] Dispersed lubricant 2%; Toughener 3%.

[0093] Wherein, polycarbonate is the powder polycarbonate that melting index is 25g / 10min; Compatibilizer is styrene-maleic anhydride random copolymer and maleic anhydride grafted acrylonitrile-butadiene-styrene copolymer The two substances are mixed in any proportion; the mineral filler is powdered glass fiber and carbon fiber mixed in any proportion; the antioxidant is a phenolic antioxidant; produced by the company); the dispersant lubricant is a mixture of montan wax and polyethylene wax in any proportion; the toughening agent is ethylene butyl acrylate copolymer.

[0094] In this embodiment, the method fo...

Embodiment 3

[0096] A special PC / ABS alloy modified engineering plastic for notebook computer shells, containing the following components by weight percentage:

[0097] Polycarbonate 28%; Compatibilizer 2%;

[0098] Acrylonitrile-butadiene-styrene 26.3%; Mineral filler 20%;

[0099] Antioxidant 0.9%; Halogen-free flame retardant 17%;

[0100] Dispersed lubricant 1.8%; Toughener 4%.

[0101] Wherein, polycarbonate is the powder polycarbonate that melt index is 12.5g / 10min; Compatibilizer is graft polystyrene-polyethylene-polybutylene-polystyrene block copolymer of maleic anhydride; Mineral filler is Nano talcum powder, carbon fiber and powdered glass fiber are mixed in any proportion; the antioxidant is amine antioxidant; the halogen-free flame retardant is bisphenol A bis(diphenyl phosphate); the dispersing lubricant is polyethylene wax and pentaerythritol stearin The acid ester is mixed in any proportion; the toughening agent is a core-shell structure methyl methacrylate-butadiene-styr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melt indexaaaaaaaaaa
Melt indexaaaaaaaaaa
Melt indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a PC / ABS alloy modified engineering plastic dedicated for laptop casings. The plastic comprises the following components in percentage by weight: 22% to 65% of polycarbonate, 1% to 10% of compatilizer, 22% to 65% of acrylonitrile-butadiene-styrene, 5% to 40% of mineral filling material, 0.3% to 1% of antioxidant, 3% to 20% of halogen-free fire retardant, 0.5% to 2% of dispersed lubricant, and 3% to 20% of flexibilizer. The invention also discloses a production method of the PC / ABS alloy modified engineering plastic dedicated for laptop casings. The PC / ABS alloy modified engineering plastic dedicated for laptop casings has the advantages of capability of being recycled and utilized, multi-choice of color and outer layer treatment, stable size, good heat radiation property, and high cost performance. The production method has the advantages of simple operation and suitability for mass production.

Description

[0001] technical field [0002] The invention relates to the technical field of polymer plastic materials, in particular to the field of PC / ABS alloy modified engineering plastics specially used for notebook computer shells. [0003] Background technique [0004] The shell of a notebook computer is not only the most direct way to protect the body, but also an important factor affecting its cooling effect, "weight" and aesthetics. There are three main types of notebook shell materials: hard plastic shells; metal alloy shells; carbon fiber alloy shells. 1. Hard plastic casing. Traditional notebooks mostly use hard plastic casing, which is heavy, not very strong, and has poor heat dissipation. After a long time of use, the casing will be worn or deformed to varying degrees. It's like a drum skin that can sink in and bounce back up. At present, most manufacturers have abandoned this material. 2. The metal alloy casing can be divided into aluminum-magnesium alloy materials an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L69/00C08L55/02C08K13/04C08K3/34C08K7/14C08K7/06B29B9/06
Inventor 李定标葛磊
Owner 东莞市卡帝德塑化科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com