A kind of preparation method of chlorohydroxyapatite whisker

A chlorohydroxyapatite and whisker technology, applied in the fields of chemistry and materials, can solve problems such as restricting application, and achieve the effects of low production cost, simple equipment and simple process

Inactive Publication Date: 2016-01-06
QILU UNIV OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As a bioactive ceramic raw material, hydroxyapatite has broad application prospects, however, the inherent brittleness of ceramic materials restricts its application in bio-bone replacement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of chlorohydroxyapatite whisker
  • A kind of preparation method of chlorohydroxyapatite whisker

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Weigh 4g calcium carbonate, 10.32g calcium hydrogen phosphate and 28.64g sodium chloride, mix them in a ball mill at 300 rpm for 3 hours, take them out and put them in an alumina crucible, and put the alumina crucible in a high-temperature furnace. Raise the furnace temperature to 1000°C in 4 hours, keep it warm for 1 hour, and turn off the power. When the temperature in the furnace drops to room temperature, take out the product, put it in a mortar and grind slightly to obtain a dispersed powder. Add distilled water to the powder, fully stir and filter, and repeatedly wash 3 times. Put the powder in an oven and dry at 100°C for 24 hours to obtain chlorapatite whiskers. The obtained chlorapatite whiskers The diameter is 3-40μm and the length is 10-300μm.

Embodiment 2

[0022] Weigh 4g calcium carbonate, 10.32g calcium hydrogen phosphate and 14.32g potassium chloride, mix them in a ball mill at 300 rpm for 3 hours, take them out and put them in an alumina crucible, and put the alumina crucible in a high-temperature furnace. Raise the furnace temperature to 1150°C for 4 hours, keep it warm for 1 hour, and turn off the power. When the temperature in the furnace drops to room temperature, take out the product, put it in a mortar and grind slightly to obtain a dispersed powder. Add distilled water to the powder, fully stir and filter, repeat washing 5 times, put the powder in an oven at 120°C for 24 hours to obtain chlorapatite whiskers, and the obtained chlorapatite whiskers The diameter is 1-30μm and the length is 5-200μm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a chlorohydroxyapatite whisker, and belongs to the fields of chemistry and materials. The method comprises the steps: with calcium carbonate and calcium hydrophosphate as calcium and phosphorus source materials and an alkali metal chloride as a fused salt, obtaining the chlorohydroxyapatite whisker material by controlling the composition of the fused salt, the ratio of the fused salt to the calcium and phosphorus mixed material, and the reaction temperature. The diameter of the obtained chlorohydroxyapatite whisker ranges from 0.5 microns to 40 microns, and the length of the chlorohydroxyapatite whisker ranges from 5 microns to 300 microns; the chlorohydroxyapatite whisker is mainly used for reinforcing and toughening ceramics and high molecular biological materials; therefore, the chlorohydroxyapatite whisker has the value of wide application.

Description

Technical field [0001] The invention relates to the fields of chemistry and materials, in particular to a preparation method of chloroapatite whiskers. Background technique [0002] The human body contains more than 60 elements. The four elements of oxygen, carbon, hydrogen, and nitrogen account for 96% of the total body, and the seven elements of calcium, phosphorus, potassium, sulfur, sodium, chlorine, and magnesium account for 3.95%. The above eleven elements account for 99.95% of the total human body and are called essential macro elements in the human body. The salt in human bone tissue is mainly calcium phosphate, followed by carbonate, citrate, and a small amount of chloride and fluoride. Phosphorus, calcium, and chlorine are all essential nutrients for animal and human growth. [0003] The main inorganic component of human and animal bone tissue is hydroxyapatite, and a small amount of apatite containing carbonate and chloride ions. There are a wide range of isomorphic su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/12C01B25/32
Inventor 赵萍任学华杨凯刘金华王峰
Owner QILU UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap